Electrochemical impedance spectroscopy (EIS) was used to characterize commercial cylindrical Li‐ion cells under different state‐of‐charge (SOC) conditions and up to 300 charge/discharge cycles to monitor state‐of‐health (SOH) status. The study included the effect of temperature to access better resolution of the time constants related to the redox reactions at the electrodes. The EIS in the 10 kHz–1 mHz frequency range allowed the elaboration of a comprehensive electrical equivalent that incorporated the geometry of the cell and the electrochemical processes occurring at the anode and cathode active material. The fitting procedure of the experimental EIS data to the equivalent circuit produced parameter values that can be used to assess the SOC and SOH of the cell. In the study example, early detection of cell degradation can be obtained using the evolution of Li ⁺ diffusion resistance through the solid electrolyte interface (SEI) layer.

In this study, the axial fatigue behaviour of hot forging tool steels at room temperature was investigated. Fatigue tests were performed on two steels within the same H13 specification. The fatigue tests were carried out in the high-cycle fatigue domain under normal conditions. These tests were also performed on specimens in contact with a corrosive medium, applying stress values that led to the high-cycle fatigue domain under normal conditions for the sake of comparison. Both materials showed similar fatigue strengths when they were tested under normal conditions. In contrast, corrosion fatigue lives were much lower than in normal tests and differed significantly between the two steels. Crack initiation was triggered by microstructural and surface defects in the normal tests, whereas the formation of corrosion pits caused crack initiation in the corrosion fatigue tests. Moreover, a fracture surface analysis revealed dissimilar crack propagation areas between both steels, which suggested that both steels had different fracture toughness. These results were in line with the differences observed between the carbide and grain sizes of both of the material microstructures.

Shot peening is generally used to improve the fatigue performance of mechanical components. However, identifying the geometrical and mechanical characteristics of the shots that improve fatigue strength is still a challenging task, as there are many variables involved in the shot peening process. The present work addresses the effect of different shot media on the fatigue behaviour of an aluminium alloy 6082 T6. Four different shot types were used: silica microspheres, alumina shots, aluminium cut wire and zinc cut wire. Axial fatigue tests were carried out to obtain the Wöhler curves corresponding to each shot peening treatment. The surface properties of the shot-peened specimens, such as grain size, hardness, residual stress and roughness were measured to determine their effect on the fatigue results. The fatigue results revealed that silica and zinc shots increased significantly the fatigue life of the alloy, whereas alumina and aluminium shots reduced its fatigue strength. Almen intensities have shown to correlate well with grain refinement and strain hardening. However, better fatigue results were obtained with the shots that generated higher surface compressive residual stresses. It is believed that small and smooth shots are preferable to sharp and irregular ones, regardless of the Almen intensity or surface hardness attained with the latter.