In this study, the axial fatigue behaviour of hot forging tool steels at room temperature was investigated. Fatigue tests were performed on two steels within the same H13 specification. The fatigue tests were carried out in the high-cycle fatigue domain under normal conditions. These tests were also performed on specimens in contact with a corrosive medium, applying stress values that led to the high-cycle fatigue domain under normal conditions for the sake of comparison. Both materials showed similar fatigue strengths when they were tested under normal conditions. In contrast, corrosion fatigue lives were much lower than in normal tests and differed significantly between the two steels. Crack initiation was triggered by microstructural and surface defects in the normal tests, whereas the formation of corrosion pits caused crack initiation in the corrosion fatigue tests. Moreover, a fracture surface analysis revealed dissimilar crack propagation areas between both steels, which suggested that both steels had different fracture toughness. These results were in line with the differences observed between the carbide and grain sizes of both of the material microstructures.

Shot peening is generally used to improve the fatigue performance of mechanical components. However, identifying the geometrical and mechanical characteristics of the shots that improve fatigue strength is still a challenging task, as there are many variables involved in the shot peening process. The present work addresses the effect of different shot media on the fatigue behaviour of an aluminium alloy 6082 T6. Four different shot types were used: silica microspheres, alumina shots, aluminium cut wire and zinc cut wire. Axial fatigue tests were carried out to obtain the Wöhler curves corresponding to each shot peening treatment. The surface properties of the shot-peened specimens, such as grain size, hardness, residual stress and roughness were measured to determine their effect on the fatigue results. The fatigue results revealed that silica and zinc shots increased significantly the fatigue life of the alloy, whereas alumina and aluminium shots reduced its fatigue strength. Almen intensities have shown to correlate well with grain refinement and strain hardening. However, better fatigue results were obtained with the shots that generated higher surface compressive residual stresses. It is believed that small and smooth shots are preferable to sharp and irregular ones, regardless of the Almen intensity or surface hardness attained with the latter.

The main objective of this research is to conduct an experimental investigation of the bimetallic material formed by 316LSI stainless steel and S275JR structural steel, produced via hybrid wire arc additive manufacturing technology with cool metal transfer welding and machining, and with the objective of being able to reduce the industrial cost of certain requirements for one of the materials. A methodological investigation has been carried out starting with welding beads of 316LSI on S275JR plates, followed by overlapping five beads and conducting final experiments with several vertical layers, with or without intermediate face milling. The results achieved optimal bead conditions for wire speeds of 4 m/min and 5 m/min at a travel speed of 400 mm/min. Overlap experiments show that the best deposition results are obtained with an overlap equal to or greater than 28%. Cooling time does not significantly influence the final geometry of the coatings. Regarding metallographic analysis, the filler material presents an austenitic columnar structure. In the base material, a bainitic structure with inferred grain refinement was detected in the heat-affected zone. An increase in hardness is observed in the heat-affected zone. In the results obtained from the tensile tests of the bimetallic material, an increase in mechanical strength and yield strength is observed in the tested specimens.