In the last few decades, there has been a trend involving the use of nanoscale fillers in a variety of applications. Significant improvements have been achieved in the areas of their preparation and further applications (e.g., in industry, agriculture, and medicine). One of these promising materials is magnesium oxide (MgO), the unique properties of which make it a suitable candidate for use in a wide range of applications. Generally, MgO is a white, hygroscopic solid mineral, and its lattice consists of Mg${}^{2+}$ ions and O${}^{2-}$ ions. Nanostructured MgO can be prepared through different chemical (bottom-up approach) or physical (top-down approach) routes. The required resultant properties (e.g., bandgap, crystallite size, and shape) can be achieved depending on the reaction conditions, basic starting materials, or their concentrations. In addition to its unique material properties, MgO is also potentially of interest due to its nontoxicity and environmental friendliness, which allow it to be widely used in medicine and biotechnological applications.

Composite insulation materials are an inseparable part of numerous electrical devices because of synergy effect between their individual parts. One of the main aims of the presented study is an introduction of the dielectric properties of nanoscale magnesium oxide powder via Broadband Dielectric Spectroscopy (BDS). These unique results present the behavior of relative permittivity and loss factor in frequency and temperature range. Following the current trends in the application of inorganic nanofillers, this article is complemented by the study of dielectric properties (dielectric strength, volume resistivity, dissipation factor and relative permittivity) of epoxy-based composites depending on the filler amount (0, 0.5, 0.75, 1 and 1.25 weight percent). These parameters are the most important for the design and development of the insulation systems. The X-ray diffraction patterns are presented for pure resin and resin with optimal filler amount (1 wt %), which was estimated according to measurement results. Magnesium oxide nanoparticles were also treated by addition of silane coupling agent ( $\gamma$ -Glycidoxypropyltrimethoxysilane), in the case of optimal filler loading (1 wt %) as well. Besides previously mentioned parameters, the effects of surface functionalization have been observed by two unique measurement and evaluation techniques which have never been used for this evaluation, i.e., reduced resorption curves (RRCs) and voltage response method (VR). These methods (developed in our departments), extend the possibilities of measurement of composite dielectric responses related to DC voltage application, allow the facile comparability of different materials and could be used for dispersion level evaluation. This fact has been confirmed by X-ray diffraction analyses.

The paper is focused on the possibility of replacing petroleum-based oils used as electro-insulating fluids in high voltage machinery. Based on ten years of study the candidate base oil for the central European region is rapeseed (Brassica napus) oil. Numerous studies on the elementary properties of pure natural esters have been published. An advantage of natural ester use is its easy biodegradability, tested according to OECD–301D (Organisation for Economic Co-operation and Development) standard, and compliance with sustainable development visions. A rapeseed oil base has been chosen for its better resistance to degradation in electric fields and its higher oxidation stability. The overall ester properties are not fully competitive with petroleum-based oils and therefore have to be improved. Percolation treatment and oxidation inhibition by a phenolic-type inhibitor is proposed and the resulting final properties are discussed. These resulting fluid properties are further improved using titanium dioxide (TiO₂) nanoparticles with a silica surface treatment. This fluid has properties suitable for use in sealed distribution transformers with the advantage of a lower price in comparison with other currently used biodegradable fluids.

The influence of different concentrations (0.5, 1.0, and 2.0 wt.%) of Zinc Oxide (ZnO) filler on the dielectric properties of the cold-curing polyurethane (PU) resin is presented in this study. For this purpose, the direct DC conductivity and the broadband dielectric spectroscopy measurements were used to describe the changes in dielectric responses of PU/ZnO nanocomposites over the frequency and temperature range, respectively. It can be stated that, the 1.0 wt.% nanoparticles and lower caused a decrease in the real relative permittivity compared to the pure PU resin, while the higher concentration of nanoparticles for frequencies above 1 Hz had the opposite effect. The presence of nanoparticles in the polyurethane resin affected the segmental dynamics of the polymer chain and changed a charge distribution in the given system. These changes caused a shift of local relaxation peaks in the spectra of imaginary permittivity and dissipation factor of nanocomposites. It is suggested that the temperature-dependent transition of the electric properties in the nano-composite is closely associated with the $\alpha$-relaxation and intermediate dipolar effects (IDE).

The influence of various types of nanoparticle fillers with the same diameter of 20 nm were separately incorporated into a single component impregnating resin based on a polyesterimide (PEI) matrix and its subsequent changes in complex relative permittivity were studied. In this paper, nanoparticles of Al${}_2$O${}_3$ and ZnO were dispersed into PEI (with 0.5 and 1 wt.%) to prepare nanocomposite polymer. Dielectric frequency spectroscopy was used to measure the dependence of the real and imaginary parts of complex relative permittivity within the frequency range of 1 mHz to 1 MHz at a temperature range from +20 °C to +120 °C. The presence of weight concentration of nanoparticles in the PEI resin has an impact on the segmental dynamics of the polymer chain and changed the charge distribution in the given system. The changes detected in the ${}^1$H NMR spectra confirm that dispersed nanoparticles in PEI lead to the formation of loose structures, which results in higher polymer chain mobility. A shift of the local relaxation peaks, corresponding to the $\alpha$-relaxation process, and higher mobility of the polymer chains in the spectra of imaginary permittivity of the investigated nanocomposites was observed.

This study presents the influence of various types of nanoparticle (NP) fillers incorporated into a polyurethane (PU) (VUKOL 022) matrix and its subsequent changes in complex permittivity. Two types of surface modification of SiO ₂ fillers were investigated. The frequency dependence of the real and imaginary parts of complex permittivity was measured within the frequency range of 1 mHz to 1 MHz using the capacitance method. The 1 wt.% NPs in PU caused an increase (MgO, TiO ₂ , n-SiO ₂ , and f-SiO ₂ ) or a decrease (d-SiO ₂ ) in the real permittivity. The α-relaxation and intermediate dipolar effect were observed at the temperature dependence of the imaginary permittivity. The change in permittivity by various surface modifications of SiO ₂ and other nanofillers was discussed based on the multi-core model. Moreover, the NPs caused a shift in the local maximum of the permittivity, which was a result of the interfacial polarisation and a charge multiplication of the α-relaxation process.