Membrane gas separation is one of the most promising technologies for the separation of carbon dioxide (CO2) from various gas streams. One application of this technology is the treatment of flue gases from combustion processes for the purpose of carbon capture and storage. For this application, poly(ethylene oxide)-containing block copolymers such as Pebax® or PolyActive™ polymer are well suited. The thin-film composite membrane that is considered in this overview employs PolyActive™ polymer as a selective layer material. The membrane shows excellent CO2 permeances of up to 4 m3(STP)·(m2·h·bar)−1 (1 bar = 105 Pa) at a carbon dioxide/nitrogen (CO2/N2) selectivity exceeding 55 at ambient temperature. The membrane can be manufactured reproducibly on a pilot scale and mounted into flat-sheet membrane modules of different designs. The operating performance of these modules can be accurately predicted by specifically developed simulation tools, which employ single-gas permeation data as the only experimental input. The performance of membranes and modules was investigated in different pilot plant studies, in which flue gas and biogas were used as the feed gas streams. The investigated processes showed a stable separation performance, indicating the applicability of PolyActive™ polymer as a membrane material for industrial-scale gas processing

New CO₂ selective blend materials were tested for gas transport properties as thick film and thin film composite membrane.

Porous, porous/gutter layer and porous/gutter layer/selective layer types of membranes were investigated for their gas transport properties in order to derive an improved description of the transport performance of thin film composite membranes (TFCM). A model describing the individual contributions of the different layers’ mass transfer resistances was developed. The proposed method allows for the prediction of permeation behaviour with standard deviations (SD) up to 10%. The porous support structures were described using the Dusty Gas Model (based on the Maxwell–Stefan multicomponent mass transfer approach) whilst the permeation in the dense gutter and separation layers was described by applicable models such as the Free-Volume model, using parameters derived from single gas time lag measurements. The model also accounts for the thermal expansion of the dense layers at pressure differences below 100 kPa. Using the model, the thickness of a silicone-based gutter layer was calculated from permeation measurements. The resulting value differed by a maximum of 30 nm to the thickness determined by scanning electron microscopy.