As the industry develops and energy demand increases, wind turbines are increasingly being used to generate electricity, resulting in an increasing number of obsolete turbine blades that need to be properly recycled or used as a secondary raw material in other industries. The authors of this work propose an innovative technology not yet studied in the literature, where the wind turbine blades are mechanically shredded and micrometric fibers are formed from the obtained powder using plasma technologies. As shown by SEM and EDS studies, the powder is composed of irregularly shaped microgranules and the carbon content in the obtained fiber is lower by up to seven times compared with the original powder. Meanwhile, the chromatographic studies show that no hazardous to the environment gases are formed during the fiber production. It is worth mentioning that this fiber formation technology can be one of the additional methods for recycling wind turbine blades, and the obtained fiber can be used as a secondary raw material in the production of catalysts, construction materials, etc.

Dispersion-hardened materials based on TiC–AlnCn are alloys with high heat resistance, strength, and durability that can be used in aircraft and rocket technology as a hard lubricant. The titanium-rich composites of the Ti–Al–C system were synthesized via the spark plasma sintering process. Composite powder with 85% of Ti, 15% of Al, and MAX-phases was processed using high-voltage electrical discharge in kerosene at a specific energy of 25 MJ kg⁻¹ to obtain nanosized particles. This method allows us to analyze the most efficient, energy saving, and less waste-generating technological processes producing materials with improved mechanical and physical properties. An Innova test indentation machine was used to determine the hardness of the synthesized composites. The microhardness of Ti–Al–C system samples was determined as approximately 500–600 HV. Scanning electron microscopy and energy-dispersive X-ray spectroscopy were performed to identify the hard titanium matrix reinforced by intermetallic phases and the clusters of carbides. Three types of reinforcing phases were detected existing in the composites—TiC, Al₄C₃, and Al₃Ti, as well as a matrix consisting of α- and β-titanium. The lattice parameters of all phases detected in the composites were calculated using Rietveld analysis. It was determined that by increasing the temperature of sintering, the amount of aluminum and carbon increases in the carbides and intermetallic phases, while the amount of titanium decreases.