A top hydrophobic layer can increase the durability of exterior coatings applied on wood. Two hydrophobic topcoats - synthetics and waterborne acrylate resin with wax additives, were tested as top layers on twenty-four different coating systems applied on oak wood in this experiment. Artificial accelerated weathering lasted for six weeks. Changes of color, gloss, surface wetting were evaluated, and microscopic analyses of coated surfaces were done during weathering. The results have shown that a top hydrophobic layer increases the durability of tested coating systems in most cases. However, the effectiveness of the two tested hydrophobic topcoats turned out to be different depending on the specific coating systems used.

The effect of the initial modification of beech and spruce wood using a solution of caffeine and of a commercial product FN-NANO^® FN-1 containing a water dispersion of TiO₂ nanoparticles for increasing the service life of a transparent oil and acrylate coatings during 6 weeks of artificial accelerated weathering was tested. Changes in colour, gloss, and the contact angle of water were monitored. Degradation of the coating film was also evaluated visually and microscopically. The resistance of the coatings to mould growth was also subsequently tested. Based on the results, it is possible to recommend the initial treatment of spruce and beech wood with a 2% caffeine solution or 15% solution of FN-NANO^® dispersion to increase the overall life of a transparent acrylic coating in exterior applications. No positive effect of the applied treatments was observed with the oil coating. In addition, lower concentrations of FN-NANO^® did not have a sufficient effect, and the synergistic effect of using FN-NANO^® in a mixture with a 1% caffeine solution was also not confirmed.

At present, many historical artefacts and furniture are only reconstructed and not restored. They are preserved in terms of material reparation, but their historical value decreases significantly. This work is focused on the comparison of the resistance of high-gloss polyurethane varnish with traditional shellac varnish. The varnishes were applied to oak wood and exposed to interior artificial accelerated ageing in Xenotest. Before and after ageing, cold liquid-resistance tests were performed on the tested specimens and gloss, colour, and adhesion were also evaluated. The structures of the surfaces were also analysed using a confocal laser scanning microscope. As expected, polyurethane varnish was much more durable than shellac varnish. Interestingly, shellac varnish was fairly resistant to water at the beginning, but this resistance was greatly reduced after artificial accelerated ageing. This illustrates the importance of sheltering the shellac treated artefacts in stable temperature-humidity conditions with the least possible effect of solar radiation.

Timber suffers from various biological damages. Recent efforts aim on nature-friendly sustainable technologies of wood protection to replace classical synthetic agents having usually negative impact on many non-target organisms including man. This research investigated the biocidal effectiveness of lavender oil (LO) in protecting the Norway spruce (Picea abies) wood against the termites Reticulitermes flavipes and the brown-rot fungus Rhodonia placenta. Following, selected physical characteristics of spruce wood treated with LO were evaluated: colour changes, roughness, surface wetting with water and surface free energy (SFE). Experiments showed that LO increased the resistance of spruce wood to termites nearly to the level of its treatment with commercial biocide based on trivalent boron and quaternary ammonium salt. The additional hydrophobic treatment of wood ensured its full termite-resistance even after artificial weathering in Xenotest and leaching in water according to EN 84, respectively. It shows a high potential of LO to protect wood against termites. Adversely, the effectiveness of 5% LO against rot was not sufficient. The colour of the oil-treated wood was preserved, its roughness increased slightly, and wetting and SFE led to a positive change, improving the adhesion of potentially applied coatings or adhesives for exterior exposures.

In the future, we can expect increased requirements to the health and ecological integrity of biocides used for the protection of wood against bio-attacks, and it is therefore necessary to search for and thoroughly test new active substances. Caffeine has been shown to have biocidal efficacy against wood-destroying fungi, moulds and insects. The aim of the research was to determine whether the effectiveness of caffeine, as a fungicide of natural origin, is affected by a different type of treated wood. Norway spruce mature wood (Picea abies), Scots pine sapwood (Pinus sylvestris), and European beech wood (Fagus sylvatica) were tested in this work. The samples were treated using long-term dipping technology or coating (according to EN 152:2012) and then tested against selected wood-destroying brown rot fungi according to the standard EN 839:2015, wood-staining fungi according to EN 152:2012, and against mould growth according to EN 15457:2015. The penetration of caffeine solution into wood depth was also evaluated using liquid extraction chromatography, as well as the effect of the treatment used on selected physical and mechanical properties of wood. The test results showed that the type of wood used and the specific type of wood-degrading agent had a significant effect on the effectiveness of caffeine protection. The most resistant wood was the treated spruce, whereas the most susceptible to deterioration was the treated white pine and beech wood. The results of the work showed that caffeine treatment is effective against wood-destroying fungi at a concentration of 2%, and at 1% in some of the tested cases. It can be used as an ecologically acceptable short-term protection alternative against wood-staining fungi in lumber warehouses and is also partially effective against moulds. It also does not have negative effects on changes in the physical and mechanical properties of the tested wood species.