The durability of transparent coatings applied to an oak wood exterior is relatively low due to its anatomic structure and chemical composition. Enhancement of the protection of oak wood against weathering using transparent hydrophobic coatings is presented in this study. Oak wood surfaces were modified using UV-stabilizers, hindered amine light stabilizer (HALS), and ZnO and TiO₂ nanoparticles before the application of a commercial hydrophobic topcoat. A transparent oil-based coating was used as a control coating system. The artificial weathering test lasted 6 weeks and colour, gloss, and contact angle changes were regularly evaluated during this period. The changes in the microscopic structure were studied with confocal laser scanning microscopy. The results proved limited durability against weathering of both tested hydrophobic coatings. The formation of micro-cracks causing the leaching of degraded wood compounds and discolouration of oak wood were observed after 1 or 3 weeks of the weathering test. Until then, an oil-based coating film had protected the wood sufficiently, but after 6 weeks the wood was fully defoliated to its non-homogenous thickness, which was caused by the presence of large oak vessels, and by the effects of specific oak tannins. Using transparent hydrophobic coatings can prolong the service life of the exteriors of wood products by decreasing their moisture content. Without proper construction protection against rainwater, the hydrophobic coating itself cannot guarantee the preservation of the natural appearance of wood exteriors.

This paper deals with the impact of heat treatment on the elastic and strength properties of two diffuse porous hardwoods, namely Fagus sylvatica and Betula pendula. Two degrees of the heat treatment were used at temperatures of 165 °C and 210 °C. The dynamic and static elasticity modulus, bending strength, impact toughness, hardness, and density were tested. It is already known that an increase in treatment temperature decreases the mechanical properties and, on the other hand, leads to a better shape and dimensional stability. Higher temperatures of the heat treatment correlated with lower elastic and strength properties. In the case of higher temperature treatments, the decline of tested properties was noticeable as a result of serious changes in the chemical composition of wood. It was confirmed that at higher temperature stages of treatment, there was a more pronounced decrease in beech properties compared to those of the birch, which was the most evident in their bending strength and hardness. Our research confirmed that there is no reason to consider birch wood to be of a lesser quality, although it is regarded by foresters as an inferior tree species. After the heat treatment, the wood properties are almost the same as in the case of beech wood.

A top hydrophobic layer can increase the durability of exterior coatings applied on wood. Two hydrophobic topcoats - synthetics and waterborne acrylate resin with wax additives, were tested as top layers on twenty-four different coating systems applied on oak wood in this experiment. Artificial accelerated weathering lasted for six weeks. Changes of color, gloss, surface wetting were evaluated, and microscopic analyses of coated surfaces were done during weathering. The results have shown that a top hydrophobic layer increases the durability of tested coating systems in most cases. However, the effectiveness of the two tested hydrophobic topcoats turned out to be different depending on the specific coating systems used.

This work deals with the quality of birch (Betula pendula) wood from different sites and the impact of heat treatment on it. Two degrees of heat treatment were used, 170 °C and 190 °C. The resulting property values were compared with reference to untreated wood samples. These values were wood density, compressive strength, modulus of elasticity (MOE), bending strength (MOR), impact bending strength (toughness), hardness, swelling, limit of hygroscopicity, moisture content and color change. It was supposed that an increase in heat-treatment temperature could reduce strength properties and, adversely, lead to better shape and dimensional stability, which was confirmed by experiments. It was also shown that the properties of the wood before treatment affected their condition after heat treatment, and that the characteristic values and variability of birch properties from 4 sites, 8 stems totally, were reflected in the properties of the heat-treated wood. Values of static MOR were the exception, where the quality of the input wood was less significant at a higher temperature, and this was even more significant in impact bending strength, where it manifested at a lower temperature degree. Impact bending strength also proved to be significantly negatively affected by heat treatment, about 48% at 170 °C, and up to 67% at 190 °C. On the contrary, the most positive results were the MOE and hardness increases at 170 °C by about 30% and about 21%, respectively, with a decrease in swelling at 190 °C by about 31%. On the basis of color change and other ascertained properties, there is a possibility that, after suitable heat treatment, birch could replace other woods (e.g., beech) for certain specific purposes, particularly in the furniture industry.

This study compares the quality of wood from two distinct sites in the Czech Republic—from former afforested agricultural land and forest land. We compared the properties of Norway spruce wood (Picea abies Karst.) and Scots pine wood (Pinus sylvestris L.), the most important domestic tree species, to Douglas fir (Pseudotsuga menziesii (Mirbel) Franco), a North American tree species and a potential substitute for the domestic spruce. Wood density, modulus of elasticity (MOE), modulus of rupture (MOR) and impact bending strength were the properties tested that were used for comparing tree species. Without taking into consideration the site, the highest density values from the tested tree species were obtained for Douglas fir (0.568 g·cm⁻³), followed by the pine (0.508 g·cm⁻³) and the spruce (0.463 g·cm⁻³). The Douglas fir also dominated in the remaining assessed properties, whilst the influence of site was not confirmed, with the exception of MOE and MOR, and only for the Douglas fir wood, wherein higher values were obtained for forest land. In terms assessed Douglas fir properties, it exceeds the domestic softwoods and represents a possible suitable replacement for them. The site only plays a role in terms of the Douglas fir, and only for certain properties.

At present, many historical artefacts and furniture are only reconstructed and not restored. They are preserved in terms of material reparation, but their historical value decreases significantly. This work is focused on the comparison of the resistance of high-gloss polyurethane varnish with traditional shellac varnish. The varnishes were applied to oak wood and exposed to interior artificial accelerated ageing in Xenotest. Before and after ageing, cold liquid-resistance tests were performed on the tested specimens and gloss, colour, and adhesion were also evaluated. The structures of the surfaces were also analysed using a confocal laser scanning microscope. As expected, polyurethane varnish was much more durable than shellac varnish. Interestingly, shellac varnish was fairly resistant to water at the beginning, but this resistance was greatly reduced after artificial accelerated ageing. This illustrates the importance of sheltering the shellac treated artefacts in stable temperature-humidity conditions with the least possible effect of solar radiation.