As a result of contemporary ecological and sustainable movements, a number of constructions from wood, as the only renewable building material, is still increasing. In accordance with these trends, wood elements are often left untreated. The presented study is aimed to characterize and compare a surface degradation of untreated wood caused by weathering. Weathering characteristics of softwoods and hardwoods (spruce, pine, Douglas fir, larch, oak, black locust, maple, poplar and alder) during twelve months of exposure in the climatic conditions of Central Europe were determined. All the wood species were characterized by colour and gloss changes and increasing roughness. The lowest discoloration was observed for oak and the highest one for spruce wood, respectively. The lowest changes of roughness were observed for alder, the highest for spruce wood. The depth of colour changes was relatively similar among the softwoods. Regarding hardwoods, it varied more. The values of total colour changes had a significant correlation with the depth values of these colour changes. Maple, alder and poplar samples were characterized by the presence of mould and blue-stain fungi. Douglas fir wood was found to be the most liable for the formation of cracks.

A top hydrophobic layer can increase the durability of exterior coatings applied on wood. Two hydrophobic topcoats - synthetics and waterborne acrylate resin with wax additives, were tested as top layers on twenty-four different coating systems applied on oak wood in this experiment. Artificial accelerated weathering lasted for six weeks. Changes of color, gloss, surface wetting were evaluated, and microscopic analyses of coated surfaces were done during weathering. The results have shown that a top hydrophobic layer increases the durability of tested coating systems in most cases. However, the effectiveness of the two tested hydrophobic topcoats turned out to be different depending on the specific coating systems used.

Colour changes and associated wood degradation in exterior and interior applications influenced by ultraviolet (UV) and visible radiation (VIS) decreases the aesthetic value of the products and shortens the overall life of transparent coatings. The aim of the paper is to achieve colour stabilization of oak, larch, Douglas fir and spruce heartwood via surface treatment with UV stabilizers, hindered amine light stabilizers (HALS), nanoparticles TiO₂, ZnO, and mixtures thereof, during exposure to UV and VIS radiation. Colour changes were evaluated during accelerated artificial ageing testing in Xenotest. The distinctly individual character of colour changes in surface treatments due to the underlying wood species was confirmed. A synergistic effect was found when using a combination of active substances compared to substances used individually. The mixture of benzotriazoles with HALS (Tinuvin 5151) in combination with TiO₂ and ZnO nanoparticles was confirmed as one of the most effective treatments for colour stabilization of wood due to UV and VIS spectrums.

Determination of Correlation between Destructive and Nondestructive Test Methods Applied on Modified Wood Exposed to Natural Weathering

Reducing discoloration of wood due to photodegradation caused by ultraviolet (UV) and visible (VIS) radiation enhances its aesthetical value and prolongs the overall service life of protective coatings. In this study, the efficiency of pretreatments with different active ingredients to reduce degradation and stabilize the color of Siberian (Larix sibirica Ledeb.) and European larch (Larix decidua Mill) wood was investigated. UV absorbers (UVA), hindered amine light stabilizers (HALS) and zinc oxide nanoparticles were used in twenty different pretreatments. The ability to protect wood surface against radiation was evaluated via color and gloss change measurements during artificial ageing. The efficiency of tested color-stabilizing pretreatments differed for Siberian and European larch and not all of them reduced discoloration. The most effective pretreatments were based on a combination of UVA and HALS in a synergistic effect. Overall, the best efficiency from tested variants for larch wood generally was observed for combination of Eversorb 80 on benzotriazole basis + Eversorb 93 on a piperidinyl basis. The pretreatments did not significantly affect the gloss values. The results revealed convenient variants of stabilizers for Siberian and European larch wood and confirmed different compatibility between specific wood species and color stabilizers.

The efficiency of surface pretreatment with natural essential oils relative to the weathering performance of Norway spruce wood was examined. This study investigated the combination of this pretreatment increasing biological resistance and oil-based coating with protection against ultraviolet light and hydrophobic topcoat with silicon nanoparticles during natural and artificial weathering. The coating systems were exposed to 24 months of natural weathering in climatic conditions of Central Europe and 2,016 hours of artificial weathering. The synergistic effect of a coating system based on safflower with essential oils and commercial oil-based coating was the most efficient. The application of one layer of an oil-based coating in a wet state of surface pretreatment exhibited results comparable to the application of two layers in a dry state. For all coating systems, increasing changes of colour, roughness, and surface wettability were observed, which differed according to the weathering method. Weathering performance of transparent coating systems was evaluated during both weathering tests by exact measurements, laser scanning microscopy and visual evaluation as well. Total colour difference did not prove to be a sufficient evaluation criterion to indicate coating performance during weathering.