A top hydrophobic layer can increase the durability of exterior coatings applied on wood. Two hydrophobic topcoats - synthetics and waterborne acrylate resin with wax additives, were tested as top layers on twenty-four different coating systems applied on oak wood in this experiment. Artificial accelerated weathering lasted for six weeks. Changes of color, gloss, surface wetting were evaluated, and microscopic analyses of coated surfaces were done during weathering. The results have shown that a top hydrophobic layer increases the durability of tested coating systems in most cases. However, the effectiveness of the two tested hydrophobic topcoats turned out to be different depending on the specific coating systems used.

The effect of the initial modification of beech and spruce wood using a solution of caffeine and of a commercial product FN-NANO^® FN-1 containing a water dispersion of TiO₂ nanoparticles for increasing the service life of a transparent oil and acrylate coatings during 6 weeks of artificial accelerated weathering was tested. Changes in colour, gloss, and the contact angle of water were monitored. Degradation of the coating film was also evaluated visually and microscopically. The resistance of the coatings to mould growth was also subsequently tested. Based on the results, it is possible to recommend the initial treatment of spruce and beech wood with a 2% caffeine solution or 15% solution of FN-NANO^® dispersion to increase the overall life of a transparent acrylic coating in exterior applications. No positive effect of the applied treatments was observed with the oil coating. In addition, lower concentrations of FN-NANO^® did not have a sufficient effect, and the synergistic effect of using FN-NANO^® in a mixture with a 1% caffeine solution was also not confirmed.

Plants and insects coevolved as an evolutionarily successful and enduring association. The molecular arms race led to evolutionary novelties regarding unique mechanisms of defence and detoxification in plants and insects. While insects adopt mechanisms to conquer host defence, trees develop well-orchestrated and species-specific defence strategies against insect herbivory. However, current knowledge on the molecular underpinnings of fine-tuned tree defence responses against different herbivore insects is still restricted. In the current study, using a multi-omics approach, we unveiled the defence response of Populus tremula against aphids (Chaitophorus populialbae) and spongy moths (Lymantria dispar) herbivory. Comparative differential gene expression (DGE) analyses revealed that around 272 and 1203 transcripts were differentially regulated in P. tremula after moth and aphid herbivory compared to uninfested controls. Interestingly, 5716 transcripts were differentially regulated in P. tremula between aphids and moth infestation. Further investigation showed that defence-related stress hormones and their lipid precursors, transcription factors, and signalling molecules were over-expressed, whereas the growth-related counterparts were suppressed in P. tremula after aphid and moth herbivory. Metabolomics analysis documented that around 37% of all significantly abundant metabolites were associated with biochemical pathways related to tree growth and defence. However, the metabolic profiles of aphid and moth-fed trees were quite distinct, indicating species-specific response optimization. After identifying the suitable reference genes in P. tremula, the omics data were further validated using RT-qPCR. Nevertheless, our findings documented species-specific fine-tuning of the defence response of P. tremula, showing conservation on resource allocation for defence overgrowth under aphid and moth herbivory. Such findings can be exploited to enhance our current understanding of molecular orchestration of tree responses against herbivory and aid in developing insect pest resistance P. tremula varieties.

The main biochemical traits were estimated in poplar leaves under biotic attack (aphids and spongy moth infestation). Changes in the abundance of bioactive compounds in genetically uniform individuals of European aspen (Populus tremula), such as proline, polyphenolic compounds, chlorophylls a and b, and volatile compounds, were determined between leaves damaged by sucking insects (aphid—Chaitophorus nassonowi) and chewing insects (spongy moth—Lymantria dispar) compared to uninfected leaves. Among the nine analyzed phenolic compounds, only catechin and procyanidin showed significant differences between the control leaves and leaves affected by spongy moths or aphids. GC-TOF-MS volatile metabolome analysis showed the clear separation of the control versus aphids-infested and moth-infested leaves. In total, the compounds that proved to have the highest explanatory power for aphid-infested leaves were 3-hexenal and 5-methyl-2-furanone, and for moth-infested leaves, trans-α-farnesene and 4-cyanocyclohexane. The aphid-infested leaves contained around half the amount of chlorophylls and twice the amount of proline compared to uninfected leaves, and these results evidenced that aphids influence plant physiology more than chewing insects.

Changes in surface material characteristics can significantly affect the adhesion and overall life of coatings on wood. In order to increase the durability of transparent exterior coatings, it is possible to use the surface modification of wood with UV-stabilizing substances. In this work, selected types of surface modifications using benzotriazoles, HALS, ZnO and TiO₂ nanoparticles, and their combinations were applied to oak wood (Quercus robur, L.). On such modified surfaces, the surface free energy, roughness, and contact wetting angle with three selected types of exterior transparent coatings were subsequently determined. An oil-based coating, waterborne acrylic thick layer coating, and thin-layer synthetic coating were tested and interaction with the aforementioned surface modifications was investigated after 6 weeks of accelerated artificial weathering. The results of changes in the initially measured surface characteristics of the modified oak wood were compared to the real results of degradation of coatings after artificial accelerated weathering. The positive effect of surface modification, in particular the mixture of benzotriazoles, HALS, and ZnO nanoparticles on all kinds of coatings was proven, and the best results were observed in thick-film waterborne acrylic coating. The changes in the measured surface characteristics corresponded to the observed durability of the coatings only when measured by wetting using drops of the tested coatings.

This study determined the impact of undertaking an initial treatment of oak wood by sealing its surface pores with epoxy resin, focusing on the durability of transparent coating systems when exposed outdoors. Throughout the exposure period, various parameters including color, gloss, surface wettability, and both macroscopic and microscopic surface evaluation were continuously monitored. The study involved two sets of samples: one set underwent the pretreatment, while the other did not. Subsequently, four coating systems were applied to the samples, comprising two solvent-based and two water-based coatings. The experiment was conducted over a period of two years, utilizing natural weathering methods within the premises of the Czech University of Life Sciences in Prague. The pretreatment with epoxy resin exhibited enhanced durability for all paint systems. The analysis showed a significant difference in gloss and color after 12 months of weathering exposure without any significant effect on surface wettability and sealing. However, after 24 months of the weathering exposure, no significant differences between the sealed and unsealed surface were observed. The most significant change in properties was noted for the water-based coatings used in coating systems number 3 and 4, and these coatings were rated as the best.