The growing demands for material longevity in marine environments necessitate the development of highly efficient, low-cost, and durable corrosion-protective coatings. Although magnesium alloys are widely used in the automotive and aerospace industries, severe corrosion issues still hinder their long-term service in naval architecture. In the present work, an epoxy composite coating containing sericite nanosheets is prepared on the AZ31B Mg alloy using a one-step electrophoretic deposition method to improve corrosion resistance. Due to the polyetherimide (PEI) modification, positively charged sericite nanosheets can be highly orientated in an epoxy coating under the influence of an electric field. The sericite-incorporated epoxy coating prepared in the emulsion with 4 wt.% sericite exhibits the highest corrosion resistance, with its corrosion current density being 6 orders of magnitude lower than that of the substrate. Electrochemical measurements and immersion tests showed that the highly orientated sericite nanosheets in the epoxy coating have an excellent barrier effect against corrosive media, thus significantly improving the long-term anti-corrosion performance of the epoxy coating. This work provides new insight into the design of lamellar filler/epoxy coatings with superior anticorrosion performance and shows promise in the corrosion protection of magnesium alloys.

Metal oxide semiconductor (MOS) hydrogen sensors offer advantages, such as high sensitivity and fast response, but their challenges remain in achieving low-cost fabrication and stable operation at room temperature. This study investigates Nb-doped TiO₂ (NTO) thin films prepared via a one-step micro-arc oxidation (MAO) with the addition of Nb₂O₅ nanoparticles into the electrolyte for room-temperature hydrogen sensing. The characterization results revealed that the incorporation of Nb₂O₅ altered the film’s morphology and phase composition, increasing the Nb content and forming a homogeneous composite thin film. Hydrogen sensing tests demonstrated that the NTO samples exhibited significantly improved sensitivity, selectivity, and stability compared to undoped TiO₂. Among the fabricated samples, NTO thin film prepared at Nb₂O₅ concentration of 6 g/L (NTO-6) showed the best performance, with a broad detection range, excellent sensitivity, rapid response, and good specificity to hydrogen. A strong linear relationship between response values and hydrogen concentration (10–1000 ppm) highlights its potential for precise hydrogen detection. The enhanced hydrogen sensing mechanism of NTO thin films primarily stems from the influence of Nb₂O₅; nanoparticles doping in the anatase-phase TiO₂ structure on the semiconductor surface depletion layer, as well as the improved charge transfer and additional adsorption sites provided by the Nb/Ti composite metal oxides, such as TiNb₂O₇ and Ti_0.95Nb_0.95O₄. This study demonstrates the potential of MAO-fabricated Nb-doped TiO₂ thin films as efficient and reliable hydrogen sensors operating at room temperature, offering a pathway for novel gas-sensing technologies to support clean energy applications.

This study investigates the tribological properties of Ti-6Al-4V alloy treated with single laser texturing, single thermal oxidation, and laser texturing combined with thermal oxidation in a PAO6 oil environment. The surface morphology, cross-sectional morphology, surface chemical composition, microhardness, wettability, and wear surface morphology were analyzed using a three-dimensional profiler, scanning electron microscope, electron spectrometer, X-ray diffractometer, micro-Vickers hardness tester, and optical contact angle measuring instrument. The results indicate that combining laser texturing with thermal oxidation treatment enhances groove edge hardness to approximately 1932 HV_0.2, due to the synergistic effects of laser-induced heat-affected zones and the formation of high-hardness rutile phase TiO₂. Simultaneously, the treatment effectively enhances the wettability of PAO6 oil on the surface. Furthermore, the composite-treated surface combines the oil reservoir and debris-trapping capabilities of a single laser-textured surface with the excellent load-bearing capacity of a single thermally oxidized surface. This enhancement improves the durability and reliability of the groove-type texture, leading to reduced material loss and a diminished wear rate, and significantly improving the surface wear resistance of Ti-6Al-4V alloy.

The growing demands of material longevity in marine environments necessitate the development of highly efficient, low-cost and durable corrosion protective coatings. Although magnesium alloys are widely used in the automotive and aerospace industries, severe corrosion issues still hinder their long-term service in naval architecture. In present work, an epoxy composite coating containing sericite nanosheets is prepared on the AZ31B Mg alloy by one-step electrophoretic deposition method to improve corrosion resistance. Due to the PEI modification, positively-charged sericite nanosheets can be highly orientated in an epoxy coating under the influence of an electric field. The sericite-incorporated epoxy coating prepared in the emulsion with 4 wt.% sericite exhibits the highest corrosion resistance in 3.5 wt.% NaCl solution, as manifested by electrochemical corrosion and long-term immersion tests. The highly-orientated sericite nanosheets in epoxy coating provide excellent barrier effect against corrosive media, thereby significantly improving the long-term anti-corrosion performance of the epoxy coating. This work provides new insight toward the design of lamellar filler/epoxy coatings with superior anticorrosion performance and shows promise in the corrosion protection of magnesium alloys.