This paper is devoted to the study of the structure and thermomechanical properties of PVDF-based ferroelectric polymer film. Transparent electrically conductive ITO coatings are applied to both sides of such a film. In this case, such material acquires additional functional properties due to piezoelectric and pyroelectric effects, forming, in fact, a full-fledged flexible transparent device, which, for example, will emit a sound when an acoustic signal is applied, and under various external influences can generate an electrical signal. The use of such structures is associated with the influence of various external influences on them: thermomechanical loads associated with mechanical deformations and temperature effects during operation, or when applying conductive layers to the film. The article presents structure investigation and its change during high-temperature annealing using IR spectroscopy and comparative results of testing a PVDF film before and after deposition of ITO layers for uniaxial stretching, its dynamic mechanical analysis, DSC, as well as measurements of the transparency and piezoelectric properties of such structure. It is shown that the temperature-time mode of deposition of ITO layers has little effect on the thermal and mechanical properties of PVDF films, taking into account their work in the elastic region, slightly reducing the piezoelectric properties. At the same time, the possibility of chemical interactions at the polymer–ITO interface is shown.

The work is aimed at studying the impact resistance of epoxy oligomer matrices (EO) modified with polysulfone (PSU) or polyethersulfone (PES) and glass fibers reinforced plastics (GFRP) based on them under low-velocity impact conditions. The concentration dependences of strength and fracture energy of modified matrices and GFRP were determined. It has been determined that the type of concentration curves of the fracture energy of GFRP depends on the concentration and type of the modifying polymer. It is shown that strength σ and fracture energy E_M of thermoplastic-modified epoxy matrices change little in the concentration range from 0 to 15 wt.%. However, even with the introduction of 20 wt.% PSU into EO, the strength increases from 164 MPa to 200 MPa, and the fracture energy from 32 kJ/m² to 39 kJ/m². The effect of increasing the strength and fracture energy of modified matrices is retained in GFRP. The maximum increase in shear strength (from 72 MPa to 87 MPa) is observed for GFRP based on the EO + 15 wt.% PSU matrix. For GFRP based on EO + 20 wt.% PES, the shear strength is reduced to 69 MPa. The opposite effect is observed for the EO + 20 wt.% PES matrix, where the strength value decreases from 164 MPa to 75 MPa, and the energy decreases from 32 kJ/m² to 10 kJ/m². The reference value for the fracture energy of GFRP 615 is 741 kJ/m². The maximum fracture energy for GFRP is based on EO + 20 wt.% PSU increases to 832 kJ/m² for GFRP based on EO + 20 wt.% PES—up to 950 kJ/m². The study of the morphology of the fracture surfaces of matrices and GFRP confirmed the dependence of impact characteristics on the microstructure of the modified matrices and the degree of involvement in the process of crack formation. The greatest effect is achieved for matrices with a phase structure “thermoplastic matrix-epoxy dispersion.” Correlations between the fracture energy and strength of EO + PES matrices and GFRP have been established.

The product of ozonolysis, glycero-(9,10-trioxolane)-trioleate (ozonide of oleic acid triglyceride, [OTOA]), was incorporated into polylactic acid/polycaprolactone (PLA/PCL) blend films in the amount of 1, 5, 10, 20, 30 and 40% w/w. The morphological, mechanical, thermal and antibacterial properties of the biodegradable PLA/PCL films after the OTOA addition were studied. According to DSC and XRD data, the degree of crystallinity of the PLA/PCL + OTOA films showed a general decreasing trend with an increase in OTOA content. Thus, a significant decrease from 34.0% for the reference PLA/PCL film to 15.7% for the PLA/PCL + 40% OTOA film was established using DSC. Observed results could be explained by the plasticizing effect of OTOA. On the other hand, the PLA/PCL film with 20% OTOA does not follow this trend, showing an increase in crystallinity both via DSC (20.3%) and XRD (34.6%). OTOA molecules, acting as a plasticizer, reduce the entropic barrier for nuclei formation, leading to large number of PLA spherulites in the plasticized PLA/PCL matrix. In addition, OTOA molecules could decrease the local melt viscosity at the vicinity of the growing lamellae, leading to faster crystal growth. Morphological analysis showed that the structure of the films with an OTOA concentration above 20% drastically changed. Specifically, an interface between the PLA/PCL matrix and OTOA was formed, thereby forming a capsule with the embedded antibacterial agent. The moisture permeability of the resulting PLA/PCL + OTOA films decreased due to the formation of uniformly distributed hydrophobic amorphous zones that prevented water penetration. This architecture affects the tensile characteristics of the films: strength decreases to 5.6 MPa, elastic modulus E by 40%. The behavior of film elasticity is associated with the redistribution of amorphous regions in the matrix. Additionally, PLA/PCL + OTOA films with 20, 30 and 40% of OTOA showed good antibacterial properties on Pseudomonas aeruginosa, Raoultella terrigena (Klebsiella terrigena) and Agrobacterium tumefaciens, making the developed films potentially promising materials for wound-dressing applications.

In this work, the fracture mechanism of winding carbon-fiber-reinforced plastics (CFRPs) based on epoxy matrices reinforced by polysulfone film was investigated. Two types of polymer matrices were used: epoxy oligomer (EO) cured by iso-methyltetrahydrophthalic anhydride (iso-MTHPA), and EO-modified polysulfone (PSU) with active diluent furfuryl glycidyl ether (FGE) cured by iso-MTHPA. At the winding stage, the reinforcing film was placed in the middle layer of the CFRP. The fracture toughness G_IR of the obtained CFRP was determined by the double-cantilever beam delamination method. Additionally, the effect of cyclic loading on the fracture toughness of CFRP reinforced with polysulfone film was investigated. It was shown that heterogeneous structures arising from the dissolution of the polysulfone film in the epoxy binder during the curing process increase the fracture toughness of CFRP from 0.5 kJ/m² to 1.2 kJ/m². Application of cyclic loads had little effect on the fracture toughness value. As a result of this study, it was revealed that the macrocrack propagates near the reinforcement layer along the diffusion zone, which has a phase organization of the type PSU matrix–EO dispersion.

The repair efficiency of various self-healing materials often depends on the ability of the prepolymer and curing agent to form mixtures. This paper presents a synthesis and study of the properties of modified self-healing polyurethanes using the Diels–Alder reaction (DA reaction), obtained from a maleimide-terminated preform and a series of furan–urethane curing agents. The most commonly used isocyanates (4,4′-methylene diphenyl diisocyanate (MDI), 2,4-tolylene diisocyanate (TDI), and hexamethylene diisocyanate (HDI)) and furan derivatives (furfurylamine, difurfurylamine, and furfuryl alcohol) were used as initial reagents for the synthesis of curing agents. For comparative analysis, polyurethanes were also obtained using the well-known “traditional” approach—from furan-terminated prepolymers based on mono- and difurfurylamine, as well as furfuryl alcohol and the often-used bismaleimide curing agent 1,10-(methylenedi-1,4-phenylene)bismaleimide (BMI). The structure and composition of all polymers were studied using spectroscopic methods. Molecular mass was determined using gel permeation chromatography (GPC). Thermal properties were studied using TGA, DSC, and TMA methods. The mechanical and self-healing properties of the materials were investigated via a uniaxial tensile test. Visual assessment of the completeness of damage restoration after the self-healing cycle was carried out using a scanning electron microscope. It was shown that the proposed modified approach helps obtain more durable polyurethanes with a high degree of self-healing of mechanical properties after damage.

Glycerol-(9,10-trioxolane) trioleate (OTOA) is a promising material that combines good plasticizing properties for PLA with profound antimicrobial activity, which makes it suitable for application in state-of-the-art biomedical and packaging materials with added functionality. On the other hand, application of OTOA in PLA-based antibacterial materials is hindered by a lack of knowledge on kinetics of the OTOA release. In this work, the release of glycero-(9,10-trioxolane) trioleate (OTOA) from PLA films with 50% OTOA content was studied during incubation in normal saline solution, and for the first time, the kinetics of OTOA release from PLA film was evaluated. Morphological, thermal, structural and mechanical properties of the PLA + 50% OTOA films were studied during incubation in normal saline and corresponding OTOA release using differential scanning calorimetry (DSC), X-ray diffraction (XRD), Fourier-transform infrared (FTIR) spectroscopy and mechanical tests. It was confirmed by DSC and XRD that incubation in the saline solution and corresponding OTOA release from PLA film does not lead to significant changes in the structure of the polymer matrix. Thus, the formation of more disturbed α’ crystalline phase of PLA due to partial hydrolysis of amorphous zones and/or most unstable crystallites in the PLA/OTOA semi-crystalline structure was observed. The degree of crystallinity of PLA + OTOA film was also slightly increased at the prolonged stages of OTOA release. PLA + 50% OTOA film retained its strength properties after incubation in normal saline, with a slight increase in the elastic modulus and tensile strength, accompanied by a significant decrease in relative elongation at break. The obtained results showed that PLA + 50% OTOA film could be characterized by sustained OTOA release with the amount of released OTOA exceeding 50% of the initial content in the PLA film. The OTOA release profile was close to zero-order kinetics, which is beneficial in order to provide stable drug release pattern. Developed PLA + 50% OTOA films showed a strong and stable antibacterial effect against Raoultella terrigena and Escherichia coli, bacterial strains with multidrug resistance behavior. The resulting PLA + OTOA films could be used in a variety of biomedical and packaging applications, including wound dressings and antibacterial food packaging.