Nanocrystalline materials based on titanium dioxide possess unique properties, including photocatalytic and antibacterial activities. Despite many approaches have already been utilized to fabricate and characterize pure and doped TiO₂, a systematic description of its nanostructured samples depending on the synthesis method has not been presented yet. In this study, we shed new light on the process–structure relationships of nanocrystalline TiO₂-based powders fabricated by extraction–pyrolytic, hydrothermal, and sol–gel techniques. The comprehensive analysis of the fabricated nanocrystalline TiO₂-based powders with different anatase/rutile phase content is performed by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS). The hydrothermal and sol–gel methods are also used to grow TiO₂ particles doped with Cu and Er-Yb. The correlation between synthesis parameters (pyrolysis and annealing temperature) and properties of the produced materials is studied. Particular attention is paid to Raman spectroscopy and the detailed comparison of our obtained data with existing experimental and theoretical studies.

The recovery of radiation damage induced by 231-MeV xenon ions with varying fluence (from 5 × 10¹¹ to 2 × 10¹⁴ cm⁻²) in α-Al₂O₃ (corundum) single crystals has been studied by means of isochronal thermal annealing of radiation-induced optical absorption (RIOA). The integral of elementary Gaussians (product of RIOA spectrum decomposition) OK has been considered as a concentration measure of relevant oxygen-related Frenkel defects (neutral and charged interstitial-vacancy pairs, F-H, F⁺-H⁻). The annealing kinetics of these four ion-induced point lattice defects has been modelled in terms of diffusion-controlled bimolecular recombination reactions and compared with those carried out earlier for the case of corundum irradiation by fast neutrons. The changes in the parameters of interstitial (mobile component in the recombination process) annealing kinetics—activation energy E and pre-exponential factor X—in ion-irradiated crystals are considered.

Metal-coated mesoporous PSi (mesoPSi) opens up disruptive perspectives for biosensing, which is primarily enabled by surface-enhanced Raman scattering (SERS). Although the unique performance of SERS-active substrates based on metal-coated mesoPSi has already been praised, influence of defects in silicon wafer on its morphology has not been revealed. Defects lead to formation of spiral regions in mesoPSi with varying porosity, which affects SERS activity of the overlying metallic nanostructures. It limits the reliability of SERS analysis. Here, we investigate repeatability of morphology and SERS activity of silver particles on mesoPSi as a function of defects in parent silicon, which are induced by irregular dopant levels. We propose an original corrosion approach that has not yet been applied to control the morphology of silicon nanostructures in general and mesoPSi in particular. By replacing silicon nanocrystallites with sacrificial copper nanoparticles, we were able to eliminate the surface irreproducibility of mesoPSi. The copper-corrosion-modified porous silicon surface was shown to be a suitable substrate for reliable SERS-active substrates. In more detail, SERS-active substrate based on mesoPSi without a defective surface layer allowed for a more than 40% increase in the SERS-active surface area with a signal deviation of only 10 % compared to that with a defective layer.

The recovery of radiation damage induced by 231-MeV xenon ions with varying fluence (from 5´1011 and 2´1014 cm-2) in a-Al2O3 (corundum) single crystals has been studied by means of isochronal thermal annealing of radiation-induced optical absorption (RIOA). The integral of elementary Gaussians (product of RIOA spectrum decomposition) has been considered as concentration measure of relevant oxygen-related Frenkel defects (neutral and charged interstitial-vacancy pairs, F-H, F+-H-). The annealing kinetics of these four ion-induced point lattice defects has been modelled in terms of diffusion-controlled bimolecular recombination reactions and compared with those earlier done for the case of corundum irradiation by fast neutrons. The changes in the parameters of interstitial (mobile component in the recombination process) annealing kinetics - activation energy E and pre-exponential factor X - in ion-irradiated crystals are considered.