The force chain network within asphalt mixtures serves as the primary load-bearing structure to resist external forces. The objective of this study is to quantitatively characterize the contact force distribution and force chain topology structure. The discrete element method (DEM) was employed to construct simulation models for two stone matrix asphalt (SMA) and two open-graded friction course (OGFC) mixtures. Load distribution characteristics, including average contact force, load bearing contribution and contact force angle, and force chain topological network parameters, clustering coefficient, edge betweenness and average path length, were analyzed to elucidate the load transfer mechanisms. The findings of the present study demonstrate that the average contact force between aggregate–aggregate contact types in specific particle sizes significantly exceeds the average contact force of the same particle size aggregates. For SMA16 and OGFC16 asphalt mixtures, the load-bearing contribution of aggregates initially increases and then decreases with decreasing particle size, peaking at 13.2 mm. SMA13 and OGFC13 mixtures demonstrate a consistent decline in load bearing contribution with decreasing aggregate size. The analysis of the force chain network topology of the asphalt mixture reveals that SMA mixtures exhibited higher average clustering coefficients in force chain topological features in comparison to OGFC mixtures. It indicates that SMA gradations have superior skeletal load-bearing structures. While the maximum nominal aggregate size minimally influences the average path length with a relative change rate of 3%, the gradation type exerts a more substantial impact, exhibiting a relative change rate of 7% to 9%. These findings confirm that SMA mixtures have more stable load-bearing structures than OGFC mixtures. The proposed topological parameters effectively capture structural distinctions in force chain networks, offering insights for optimizing gradation design and enhancing mechanical performance.

This paper aims to explore the influences of the content and gradation of mineral powder on the rheological properties of styrene-butadiene-styrene (SBS) modified asphalt mastic at different aging stages and temperatures. In the experiment, SBS modified asphalt mastic samples with different powder-to-binder ratios (0.6, 0.8, and 1.0) and different mineral powder gradations (500 mesh passing rates of 76.89% and 100%) were prepared. Following aging periods of 5, 25, and 45 h in the pressure aging vessel (PAV), the asphalt underwent comprehensive rheological characterization using a dynamic shear rheometer (DSR). The research shows that mineral powder can boost mastic’s deformation resistance and elastic effect. When aged by PAV for 45 h, the powder-to-binder ratio increased from 0.6 to 1.0, and its complex modulus increased by nearly 2.5 times at 58 °C. For SBS modified asphalt mastic of PAV 0 h, the powder-to-binder ratio increased from 0.6 to 1.0 and its phase angle was reduced from 59.6 to 53.2, which indicated that the elasticity of mastic was improved. However, this accelerated the degradation rate of SBS, making the aging process more complex. Fine-grained mineral powder is more effective in enhancing mastic’s deformation resistance than coarse-grained mineral powder. The fine-graded mastic had better rutting resistance after 45 h of aging than after 25 h of aging because the mineral powder compensated for the SBS loss-induced elasticity reduction. Smaller mineral powder particles lead to better a mastic anti-aging effect. After 45 h of aging, fine-grained mineral powder offered a better elastic effect. But the ways in which mineral powder and SBS boost mastic elasticity differ greatly. The results of this study provide a reference for optimizing the design of asphalt mixtures.