A novel class of graphene-based materials incorporated into natural lignocellulosic fiber (NLF) polymer composites is surging since 2011. The present overview is the first attempt to compile achievements regarding this novel class of composites both in terms of technical and scientific researches as well as development of innovative products. A brief description of the graphene nature and its recent isolation from graphite is initially presented together with the processing of its main derivatives. In particular, graphene-based materials, such as nanographene (NG), exfoliated graphene/graphite nanoplatelet (GNP), graphene oxide (GO) and reduced graphene oxide (rGO), as well as other carbon-based nanomaterials, such as carbon nanotube (CNT), are effectively being incorporated into NLF composites. Their disclosed superior mechanical, thermal, electrical, and ballistic properties are discussed in specific publications. Interfacial shear strength of 575 MPa and tensile strength of 379 MPa were attained in 1 wt % GO-jute fiber and 0.75 wt % jute fiber, respectively, epoxy composites. Moreover, a Young’s modulus of 44.4 GPa was reported for 0.75 wt % GO-jute fiber composite. An important point of interest concerning this incorporation is the fact that the amphiphilic character of graphene allows a better way to enhance the interfacial adhesion between hydrophilic NLF and hydrophobic polymer matrix. As indicated in this overview, two basic incorporation strategies have so far been adopted. In the first, NG, GNP, GO, rGO and CNT are used as hybrid filler together with NLF to reinforce polymer composites. The second one starts with GO or rGO as a coating to functionalize molecular bonding with NLF, which is then added into a polymeric matrix. Both strategies are contributing to develop innovative products for energy storage, drug release, biosensor, functional electronic clothes, medical implants, and armor for ballistic protection. As such, this first overview intends to provide a critical assessment of a surging class of composite materials and unveil successful development associated with graphene incorporated NLF polymer composites.

The use of plant fibers in cementitious composites has been gaining prominence with the need for more sustainable construction materials. It occurs due to the advantages natural fibers provide to these composites, such as the reduction of density, fragmentation, and propagation of cracks in concrete. The consumption of coconut, a fruit grown in tropical countries, generates shells that are improperly disposed of in the environment. The objective of this paper is to provide a comprehensive review of the use of coconut fibers and coconut fiber textile mesh in cement-based materials. For this purpose, discussions were conducted on plant fibers, the production and characteristics of coconut fibers, cementitious composites reinforced with coconut fibers, cementitious composites reinforced with textile mesh as an innovative material to absorb coconut fibers, and treatments of coconut fiber for improved product performance and durability. Finally, future perspectives on this field of study have also been highlighted. Thus, this paper aims to understand the behavior of cementitious matrices reinforced with plant fibers and demonstrate that coconut fiber has a high capacity to be used in cementitious composites instead of synthetic fibers.

Composites with sustainable natural fibers are currently experiencing remarkably diversified applications, including in engineering industries, owing to their lower cost and density as well as ease in processing. Among the natural fibers, the fiber extracted from the leaves of the Amazonian curaua plant (Ananas erectifolius) is a promising strong candidate to replace synthetic fibers, such as aramid (Kevlar™), in multilayered armor system (MAS) intended for ballistic protection against level III high velocity ammunition. Another remarkable material, the graphene oxide is attracting considerable attention for its properties, especially as coating to improve the interfacial adhesion in polymer composites. Thus, the present work investigates the performance of graphene oxide coated curaua fiber (GOCF) reinforced epoxy composite, as a front ceramic MAS second layer in ballistic test against level III 7.62 mm ammunition. Not only GOCF composite with 30 vol% fibers attended the standard ballistic requirement with 27.4 ± 0.3 mm of indentation comparable performance to Kevlar™ 24 ± 7 mm with same thickness, but also remained intact, which was not the case of non-coated curaua fiber similar composite. Mechanisms of ceramic fragments capture, curaua fibrils separation, curaua fiber pullout, composite delamination, curaua fiber braking, and epoxy matrix rupture were for the first time discussed as a favorable combination in a MAS second layer to effectively dissipate the projectile impact energy.

Natural-fiber-reinforced polymer composites have recently drawn attention as new materials for ballistic armor due to sustainability benefits and lower cost as compared to conventional synthetic fibers, such as aramid and ultra-high-molecular-weight polyethylene (UHMWPE). In the present work, a comparison was carried out between the ballistic performance of UHMWPE composite, commercially known as Dyneema, and epoxy composite reinforced with 30 vol % natural fibers extracted from pineapple leaves (PALF) in a hard armor system. This hard armor system aims to provide additional protection to conventional level IIIA ballistic armor vests, made with Kevlar, by introducing the PALF composite plate, effectively changing the ballistic armor into level III. This level of protection allows the ballistic armor to be safely subjected to higher impact projectiles, such as 7.62 mm caliber rifle ammunition. The results indicate that a hard armor with a ceramic front followed by the PALF/epoxy composite meets the National Institute of Justice (NIJ) international standard for level III protection and performs comparably to that of the Dyneema plate, commonly used in armor vests.

Composites reinforced with natural lignocellulosic fibers (NLFs) are gaining relevance as the worldwide demand for renewable and sustainable materials increases. To develop novel natural composites with satisfactory properties, less common NLFs should also be investigated. Among these, the Cyperus malaccensis (CM), a type of sedge fiber, is already used in simple items like ropes, furniture, and paper, but has not yet been investigated as composite reinforcement for possible engineering applications. Therefore, the present work evaluated for the first time the properties of novel epoxy composites incorporated with 10, 20, and 30 vol.% of CM sedge fibers. Tensile, Izod-impact, and ballistic impact tests were performed, as well as Fourier transform infrared (FT-IR) spectroscopy and thermal analysis of the composites. Results disclosed a decrease (−55%) in tensile strengths as compared to the neat epoxy. However, the elastic modulus of the 30 vol.% sedge fiber composite increased (+127%). The total strain and absorbed ballistic energy did not show significant variation. The Izod impact energy of the 30 vol.% composite was found to be 181% higher than the values obtained for the neat epoxy as a control sample. An increase in both stiffness and toughness characterized a reinforcement effect of the sedge fiber. The thermal analysis revealed a slight decrease (−15%) in the degradation temperature of the CM sedge fiber composites compared to the neat epoxy. The glass-transition temperatures were determined to be in the range of 67 to 81 °C.