Heavy reduction (HR) is an effective technique to control V segregation in continuous casting bloom, but the effect of segregation improvement is limited by the parameters such as reduction position and reduction amounts. In order to improve the macrosegregation of bloom, numerical simulation and plant experiments are adopted in this research. A heat transfer model and a reduction model with comprehensive thermo-physical parameters were established. The two models were verified by comparing the measured surface temperature and the theoretical strain at the solidification front. It is determined that the position of the HR of the bearing steel bloom is 20.82 m~24.97 m from the meniscus, and the solid fraction in the center of the bloom is 0.6~1. The total reduction of the HR is set to 30 mm, and the reduction of each roller in the reduction range is set to 4 mm, 5 mm, 9 mm, 7 mm, and 5 mm, respectively, to prevent the formation of internal cracks. Plant trials were conducted to verify the effect of the optimized HR. The results show that the carbon segregation degree on the V channel and non-channel of the bloom decreases from 1.2 to 1.16 and increases from 0.93 to 0.95, respectively, and the central carbon segregation degree decreases from 1.17 to 1.15. Meanwhile, the internal crack was not found in the bloom.

In this paper, a new mechanical vibration technology applied to continuous casting production is studied, which is used to break the dendrite at the solidification front, expand the equiaxed dendrite zone, and improve the center quality of the billet. The exciting force of this vibration technology is provided by a new type of vibration equipment (Vibration roll) independently developed and designed. Firstly, an investigation is conducted into the impacts of vibration acceleration, vibration frequency, and the contact area between the Vibration roll (VR) and the billet surface on the internal stress distribution within the billet shell, respectively. Secondly, the billet with and without vibration treatment was sampled and analyzed through industrial tests. The results show that the area ratio of equiaxed dendrites in transverse specimens treated with vibration technology was 11.96%, compared to 6.55% in untreated specimens. Similarly, for longitudinal samples, the linear ratio of equiaxed dendrites was observed to be 34.56% in treated samples and 22.95% in untreated samples. Compared to the specimens without mechanical vibration, the billet treated with mechanical vibration exhibits an increase in the area ratio and linear ratio of equiaxed dendrite ratio by 5.41% and 11.61%, respectively. Moreover, the probability of bridging at the end of solidification of the billet treated by vibration technology was significantly reduced, and the central porosity and shrinkage cavities of the billet were significantly improved. This study provides the first definitive evidence that the novel mechanical vibration technology can enhance the quality of the billet during the continuous casting process.