The utilization of waste rubber tires is of great value for environment protection and resource recovery, which can also improve the properties of matrix asphalt. The adhesion characteristics were evaluated for crumb rubber modified asphalt and limestone aggregate using the surface free energy (SFE) approach. Four types of matrix asphalt and four rubber contents were used to prepare the crumb rubber modified asphalt. The contact angle of matrix and crumb rubber modified asphalt was obtained, and the SFE indicators (dispersion, polar component, and compatibility rate—CR) were calculated. Moreover, the water stability tests were conducted using one matrix and rubber modified asphalt in order to investigate the relationship between SFE and water stability indicators. Results showed that the total SFE, dispersion component, adhesion work, and CR increased with the addition of crumb rubber, while the polar component and spalling work decreased. The types of asphalt had different influences on SFE indicators. The results from analysis of variation (ANOVA) indicated asphalt type and rubber content had significant influence on the adhesion work, spalling work and CR, and the influence of asphalt type was greater than that of rubber content. Additionally, the retained Marshall Stability and tensile strength ratio had better correlation with adhesion work and CR, but less with spalling work. The presented results demonstrated that the type of matrix asphalt played an important role in the adhesion characteristics for the crumb rubber modified asphalt.

Unbound granular materials (UGM) in permeable pavement will experience large numbers of infiltration during their service-life. The frequently changed moisture not only affects the cooling effect of permeable pavement, but also influences the mechanical behaviors of UGM. However, evidence is lacking to state the influence of infiltration on the behaviors of UGM, which is commonly in fully permeable pavement. Considering the influence of infiltration, this study conducted experimental tests to investigate the effect on the water-retaining and bearing capacity of UGM. With the water-retaining tests, the water-retaining rate in the whole structure and at different depths was analyzed under different infiltration numbers and duration. The results showed that the water-retaining rate increased with the extension of the infiltration duration. The infiltration duration had a significant influence on the water-retaining capacity of UGM, while the infiltration number had little. The difference in the water-retaining rate between the top and bottom layers was up to 2.56%. The water-retaining capacity of the integrated structure was hardly affected due to the dissimilarity of the water-retaining rate at different depths. With infiltrations, the fine aggregate in the upside structure migrated downward to the lower structure, resulting in a reduction in water-retaining rate in the upper structure and an increase at the bottom. In addition, the mechanical behaviors were evaluated by the traditional California Bearing Ratio (CBR) and repeated CBR tests under five infiltrations. The first and second infiltration had a significant influence on the CBR of UGM. With two infiltrations, the plastic strain increased by 57.8% via the repeated CBR tests. The resilient strain had an increase by 36.52% and the equivalent modulus decreased by 28.7% with the first infiltration. The first infiltration presented a critical influence on the bearing capacity of UGM and the effect decreased with the increase in the infiltration number. These findings will enrich the behaviors investigation of UGM and promote its application in the fully permeable pavement.

C50 manufactured sand concrete requires good workability and strength, and economic efficiency and carbon emissions also need to be considered. This study incorporates sensitivity and significance analyses to recommend the optimal economic mix composition for C50 manufactured sand concrete. The relationship between cost, workability, and mechanical properties was analyzed by considering the water/binder ratio, sand ratio, fly ash content, and superplasticizer dosage. An optimal composition of C50 manufactured sand concrete was recommended. The cost and carbon emissions were quantified at the optimal composition. The results showed that the water/binder ratio had the most significant impact on the cost and carbon emission, while the sand ratio and superplasticizer dosage had the least. All factors significantly affected its cost and carbon emission. Compared to natural sand concrete, manufactured sand concrete achieved a lower cost but higher carbon emissions. Considering the workability, strength, and cost per cubic meter of concrete, the most economical mix proportion for C50 concrete was recommended with a water/binder ratio of 0.36, a fly ash content of 25%, a sand ratio of 0.42, and a superplasticizer dosage of 1.2%. This composition cost 356 yuan, and carbon emission was 352.6 kg CO₂ per cubic meter of concrete. Compared to a composition with a water/binder ratio of 0.34 and fly ash content of 15%, the unit cost can be reduced by 18.4 yuan, and carbon emission can be minimized by 56.6 kg CO₂ e/m³. The appropriate water/binder ratio and fly ash content can reduce cost and carbon emissions without compromising the workability, compressive strength, or elastic modulus of C50 concrete. This achieves triple benefits in terms of performance, economy, and the environment when applying C50 manufactured sand concrete.

In saline soil and alpine regions of northwest China, fiber-reinforced recycled aggregate concrete (FR-RAC) beams are subjected to coupled degradation from a chloride–sulfate composite salt attack and freeze–thaw cycling. Existing studies predominantly focus on natural aggregate concrete in freshwater environments or single-salt solutions, with limited documentation on the shear performance of FR-RAC beams after freeze–thaw exposure in chloride–sulfate composite salt solutions. To investigate the durability degradation patterns of FR-RAC beams in Xinjiang’s saline soil regions, two exposure environments (pure water and 5% NaCl + 2.0% Na₂SO₄ composite salt solution) were established. Shear performance tests were conducted on nine groups of FR-RAC beams after 0–175 freeze–thaw cycles, with measurements focusing on failure modes, cracking loads, and ultimate shear capacities. The results revealed that under composite salt freeze–thaw conditions: after 100 cycles, the cracking load and shear capacity of tested beams decreased by 39.8% and 22.2%, respectively, compared to unfrozen specimens representing reductions 29.6% and 82.0% greater than those in freshwater environments; at 175 cycles, cumulative damage intensified, with total reductions reaching 56.8% (cracking load) and 36.1% (shear capacity). A shear capacity degradation prediction model for FR-RAC beams under composite salt freeze–thaw coupling was developed, accounting for concrete strength attenuation and interfacial bond degradation. Model validation demonstrated excellent agreement between predicted and experimental values, confirming its robust applicability.

Unbound granular materials (UGMs) have advantages in their water storage and drainage capabilities in permeable pavement, which is a benefit for urban sustainable development. The plastic strain of UGM is a crucial mechanical property that affects its design and construction. During its service life, repeated load only, repeated load after infiltration, and simultaneous action with load and infiltration are the three inevitable working conditions that will impact plastic strain, especially dynamic water infiltration. How these working conditions influence plastic strain needs to be focused on and solved. This study conducted laboratory tests to investigate plastic strain considering factors such as loading strength and repetitions, as well as infiltration number and duration. The results showed that the plastic strain and plastic strain rate exhibited similar variations during the repeated load only test and repeated load after infiltration test. The plastic strain changed significantly with different infiltration numbers but had relatively small variations in terms of the plastic strain rate. Longer infiltration duration led to greater plastic strain. With the simultaneous action, the plastic strain presented different variation to the other two conditions. The first and second infiltrations had a more obvious influence on the plastic strain when infiltration was applied. Calculation models were established to predict the effects of loading strength and repetitions as well as infiltration number and duration on plastic strains. For the repeated load only test, an error of 4.6% was observed. In terms of the infiltration number and duration, the errors were found to be 18.5% and 8.5%, respectively. The power function and Sigmoidal Logistic model were used to establish calculation models under the simultaneous action test with a maximum error of 11.5% ranging from 100 to 60,000 repetitions. The proposed calculation models can characterize plastic strain under the three working conditions very well, which can help in the design and construction of fully permeable pavement.

In order to investigate the change in the axial compression performance of circular recycled concrete-filled steel tubular short columns under chloride ion corrosion, 24 circular recycled concrete-filled steel tubular (RCFST) short columns and 12 circular natural concrete-filled steel tubular (NCFST) short columns for axial compression tests after being subjected to different corrosion degrees were designed. The experimental parameters include the corrosion degree (0, 2, 4, 6, 8, 10, 12, 14%) and the recycled concrete replacement rate (0, 100%). The experimental results show that the damage mode of the specimen after corrosion is localized buckling deformation of the steel tube. Due to the good confinement effect of the steel tube, the internal concrete was crushed only at the localized buckling part of the steel tube. The stiffness and ductility decreased significantly with increasing corrosion degree. As the corrosion degree increased from 0 to 14%, the stiffness of the circular RCFST short columns decreased by approximately 36.3%, and the ductility dropped by around 23.3%. And the corrosion resistance of the circular RCFST short column was worse than that of the circular NCFST short column. Based on the experimental results, the ultimate load capacity calculation model of the circular concrete-filled steel tubular short column is proposed.