The increased CO₂ emissions determined by the cement industry led to continuous and intensive research on the discovery of sustainable raw materials with cementitious properties. One such raw material category is agricultural waste. This study involved research on the effects of corn cob ash and sunflower stalk ash, respectively, on compressive strength measured after 28 days and 3 months, the flexural and splitting tensile strengths, the resistance to repeated freeze–thaw cycles, and on the resistance to chemical attack of hydrochloric acid of the concrete. A 2.5% and 5% replacement of the cement volume with corn cob ash (CCA) of A and B quality was applied, and with sunflower stalk ash (SSA) at A and B quality, respectively. The obtained results revealed that CCA and SSA decreased the compressive and tensile strength, but led to higher resistance of the concrete on repeated freeze–thaw cycles and to hydrochloric acid. The mixes with 2.5% SSA at A quality obtained the best results regarding splitting the tensile strength and resistance to repeated freeze–thaw cycles, the mixes with 2.5% SSA at B quality led to the highest resistance to hydrochloric acid, and those with 2.5% CCA at A quality led to the best values of compressive strength and flexural tensile strength.

The carbon steel is used in many areas due to its good mechanical properties; however, its low corrosion resistance presents a very important problem, for example, when carbon steel carabiners are used in the petroleum industry or navy, the possibility of an accident is higher due to carabiner failure. This phenomenon could occur as a consequence of the corrosion process which negatively affects mechanical properties. This paper study the possibility to improve its corrosion resistance by depositing on its surface a phosphate layer and a paint layer, and also aims to analyze the immersion behavior in saltwater of carbon steel, phosphate carbon steel, and phosphate and painted carbon steel. According to this study, by coating the carbon steel with a phosphate or paint layer, a higher polarization resistance is obtained in saltwater. Moreover, by electrochemical impedance spectroscopy (EIS), it was observed that the corrosion rate decreases with the increase of the immersion time. Meanwhile scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) revealed that the main compounds which formed on the sample’s surface were iron oxides or hydroxy-oxides, after immersion for a longer period. The overall results show that all types of deposited layers increase the corrosion resistance of C45 steel.

The continuous development of urban areas around the world led to an increase in construction material use and demand, with concrete seeing significant market uptake. Although significant progress has been made to reduce the environmental impact of concrete, there is still a stringent need for improvement. One of the most widely used methods to reduce the environmental impact of the cement industry and the construction industry alike is the replacement of ordinary Portland cement (OPC) by supplementary cementitious materials (SCM). Aside from by-products of industry, SCMs could also come from natural sources. Taking into account the porous structure of zeolites and their contribution to the improvement of the mechanical and durability properties of cement-based materials, the analysis of pore structure in cement pastes incorporating micronized natural zeolite is deemed necessary. In this research, the OPC was replaced by zeolite in three different percentages: 10%, 20%, and 30% by mass. The evolution of pore structure was investigated by means of nuclear magnetic resonance relaxometry at the curing ages of 1, 7, and 28 days. The microstructure of cement pastes was assessed by scanning electron microscopy investigations at 1, 7, 14, 21, and 28 days. The obtained results show that smaller pore sizes are present in cement pastes containing zeolites during the first 7 days. However, at the age of 28 days, the reference mix exhibits a similar pore structure to the mix containing 10% micronized zeolite due to the presence of larger amounts of hydration products. Increasing the replacement percentage to 30% results in larger pores, as indicated by larger values of the relaxation time.

In this study, kaolinite-based clay (Ka-Clay) was used as an adsorbent for the efficient removal of Pb(II), Cd(II) and Hg(II) ions from aqueous media. The selection of Pb(II), Cd(II) and Hg(II) ions for experimental studies took into account their high toxicity, while the choice of Ka-Clay, the ease of preparation and high availability of this material were the most important arguments. Ka-Clay exhibits high adsorption performance, with removal percents over 98% for Pb(II) and 93% for Cd(II), even at high concentrations of metal ions (over 150 mg/L, pH = 6.5, 4 g adsorbent/L, 21 ± 1 °C). For Hg(II) ions, the adsorption percent does not exceed 55%, and this moderate value is mainly due to the significant change in pH. The adsorption behavior was in accordance with the Langmuir model (R² > 0.95) and the pseudo-second order kinetic model (R² > 0.99), indicating an adsorption process that occurs mainly through chemical interactions at the adsorbent surface between the metal ions and the functional groups. Adsorption processes are spontaneous (ΔG = −8.66 ÷ −15.76 kJ/mol) and endothermic (ΔH = 7.09 ÷ 21.81 kJ/mol), and the adsorption mechanism is the results of elementary processes of electrostatic attraction, ion exchange and superficial complexation. The insignificant effect of other ions (Ca(II), Mg(II), Na(I), K(I)) present in real wastewater samples as well as the desorption behavior of exhausted adsorbent highlight the practical utility of this adsorbent on a large scale. The experimental results included in this study suggest that Ka-Clay can be used as a promising adsorbent for the removal of high concentrations of toxic heavy metals with low cost and high efficiency, and this can contribute to the design of a sustainable wastewater treatment method.

A new possible method to produce a transdermal patch is proposed in this paper. The study refers to the pulsed laser deposition method (PLD) applied on turmeric target in order to obtain thin layers. Under high power laser irradiation of 532 nm wavelength, thin films containing curcuminoids were obtained on different substrates such as glass and quartz (laboratory investigation) and hemp fabric (practical application). Compared FTIR, SEM-EDS and LIF analyses proved that the obtained thin film chemical composition is mainly demethoxycurcumin and bisdemethoxycurcumin which is evidence that most of the curcumin from turmeric has been demethixylated during laser ablation. Silanol groups with known role into dermal reconstruction are evidenced in both turmeric target and curcuminoid thin films. UV–VIS reflection spectra show the same characteristics for all the curcuminoid thin films, indicating that the method is reproducible. The method proves to be successful for producing a composite material, namely curcuminoid transdermal patch with silanol groups, using directly turmeric as target in the thin film deposited by pulsed laser technique. Double layered patch curcuminoid—silver was produced under this study, proving compatibility between the two deposited layers. The silver layer added on curcuminoid-silanol layer aimed to increase antiseptic properties to the transdermal patch.

Ge-Sb-Te thin films were obtained by ns-, ps-, and fs-pulsed laser deposition (PLD) in various experimental conditions. The thickness of the samples was influenced by the Nd-YAG laser wavelength, fluence, target-to-substrate distance, and deposition time. The topography and chemical analysis results showed that the films deposited by ns-PLD revealed droplets on the surface together with a decreased Te concentration and Sb over-stoichiometry. Thin films with improved surface roughness and chemical compositions close to nominal values were deposited by ps- and fs-PLD. The X-ray diffraction and Raman spectroscopy results showed that the samples obtained with ns pulses were partially crystallized while the lower fluences used in ps- and fs-PLD led to amorphous depositions. The optical parameters of the ns-PLD samples were correlated to their structural properties.