The use of a biosorbent based on residual biomass from brewing industry (Saccharomyces pastorianus) immobilized in a natural biopolymer (sodium alginate) was investigated for Methylene Blue removal from aqueous medium. Saccharomyces pastorianus, immobilized by a simple entrapment technique and by microencapsulation in alginate was characterized using SEM, EDAX, pH_PZC and the biosorption behavior toward organic pollutant, such as cationic dye. The biosorption experiments were studied by assessing, in a first stage, the influence of the most important operational physical parameters on the efficiency of the biosorbent: the initial concentration of the dye, the contact time between phases, the temperature, the dye solution pH, the biosorbent granule size, and the amount of biosorbent. The highest sorption capacity was obtained for the biosorbent obtained by microencapsulation, at pH 9, at biosorbent dose of 5.28 g/L and a contact time of about 100 min. The biosorption equilibrium was then studied by modeling the data on the Langmuir, Freundlich and Dubinin- Radushkevich isotherms. The Langmuir model is best suited for experimental data on both particle sizes leading to a maximum biosorption capacity of 188.679 mg/g at room temperature. The values of the adsorption energy, E, obtained with the help of the Dubinin-Radushkevich model-suggest that the type of mechanism (physical or chemical) involved in the biosorption process depends on the particle size of the biosorbent. The results confirm that the residual microbial biomass of Saccharomyces pastorianus immobilized in a polymeric matrix such as sodium alginate, can be considered an efficient biosorbent in retaining cationic organic dyes present in aqueous solutions in moderate concentrations.

In recent years, biodegradable materials have included magnesium alloys with homogenous disintegration and a controllable degradation rate. Utilized in medical applications, biodegradable materials based on magnesium have been widely explored throughout the years. It is well-known that alloying Mg with biocompatible and non-toxic elements increases the biodegradability of surgical alloys. The purpose of this study was to examine the microstructure and the electrochemical response (corrosion resistance) of a new experimental Mg-based biodegradable alloy—Mg–0.5%Ca with additions of Zn as follows: 0.5, 1.5, and 3.0 wt.% in order to control the corrosion rate. Immersion tests were performed for different periods in a simulated body fluid electrolyte solution at 37 °C, and the mass loss was appreciated in order to calculate the corrosion rate (CR). The investigation led to the discovery of a dendritic Mg solid solution, a lamellar Mg₂Ca compound, and a MgZn₂ intermetallic phase. Scanning electron microscopy, optical microscopy, and energy dispersive spectroscopy were used for surface analysis after the immersion and electro-corrosion resistance tests. The metallic and ceramic compounds that detached themselves from the sample and passed into the solution were evaluated using the SEM-EDS system. All samples presented a generalized electro-corrosion with anodic and cathodic reactions of similar intensity. The corrosion rate was similar regardless of the percentage of zinc, with a smaller value for a higher than 3 wt.% Zn percentage based on the more protective zinc oxide that appeared on the surface.

A new possible method to produce a transdermal patch is proposed in this paper. The study refers to the pulsed laser deposition method (PLD) applied on turmeric target in order to obtain thin layers. Under high power laser irradiation of 532 nm wavelength, thin films containing curcuminoids were obtained on different substrates such as glass and quartz (laboratory investigation) and hemp fabric (practical application). Compared FTIR, SEM-EDS and LIF analyses proved that the obtained thin film chemical composition is mainly demethoxycurcumin and bisdemethoxycurcumin which is evidence that most of the curcumin from turmeric has been demethixylated during laser ablation. Silanol groups with known role into dermal reconstruction are evidenced in both turmeric target and curcuminoid thin films. UV–VIS reflection spectra show the same characteristics for all the curcuminoid thin films, indicating that the method is reproducible. The method proves to be successful for producing a composite material, namely curcuminoid transdermal patch with silanol groups, using directly turmeric as target in the thin film deposited by pulsed laser technique. Double layered patch curcuminoid—silver was produced under this study, proving compatibility between the two deposited layers. The silver layer added on curcuminoid-silanol layer aimed to increase antiseptic properties to the transdermal patch.

The surface condition of the materials involved in dentistry is significant for the subsequent operations that are applied in oral cavity. Samples of Co–Cr–W alloy, obtained through selective laser melting (SLM) 3D printing, with different surface states were analyzed. Surface analysis after the 3D printing process and sandblasting was realized from microstructural, chemical composition, profilometry, droplet adhesion, scratch test, and microhardness perspectives. The results presented a hardening process and a roughness modification following the sandblasting procedure, a better adhesion of the liquid droplets, the appearance of micro-cracks during the scratch test, and the oxidation of the sample after the 3D printing process and surface processing.

Special materials are required in many applications to fulfill specific medical or industrial necessities. Biodegradable metallic materials present many attractive properties, especially mechanical ones correlated with good biocompatibility with vivant bodies. A biodegradable iron-based material was realized through electric arc-melting and induction furnace homogenization. The new chemical composition obtained presented a special property named SME (shape memory effect) based on the martensite transformation. Preliminary results about this special biodegradable material with a new chemical composition were realized for the chemical composition and structural and thermal characterization. Corrosion resistance was evaluated in Ringer’s solution through immersion tests for 1, 3, and 7 days, the solution pH was measured in time for 3 days with values for each minute, and electro-corrosion was measured using a potentiostat and a three electrode cell. The mass loss of the samples during immersion and electro-corrosion was evaluated and the surface condition was studied by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). SME was highlighted with differential scanning calorimetry (DSC). The results confirm the possibility of a memory effect of the materials in the wrought case and a generalized corrosion (Tafel and cyclic potentiometry and EIS) with the formation of iron oxides and a corrosion rate favorable for applications that require a longer implantation period.

Nowadays, alongside metallic biomaterials, there is increasing interest in using degradable metals in an appreciable number of medical applications. There are new kinds of metallic biomaterials for medical applications and many new findings have been reported over the past few years. Iron-based materials are a solution for biodegradable applications based on their mechanical and chemical properties. In order to control the corrosion rate of the Fe10Mn6Si alloy, we proposed the use of two additional elements, Ca and Mg, as corrosion promoters. The new material was obtained in an air-controlled atmosphere furnace after five melting operations. The material was in vitro analyzed from a corrosion resistance point of view. The experiments were realized by immersion (7, 14, and 30 days) in simulated body fluid (SBF) solution at 37 °C and a constant pH, and by electrochemical tests (electrochemical impedance spectroscopy (EIS), linear polarization (LP), cyclic polarization (CP)). Material surfaces before and after corrosion tests were analyzed through scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and X-ray diffraction (XRD) techniques. A discussion on the degradation rate of the material was realized from a comparison of the results. The results presented good composition homogeneity after the re-melting stages, with low percentages of Ca and Mg in the material, but with an adequate spread in the alloy.