The aim of the investigations was to compare the microstructure, mechanical, and wear properties of Cr₃C₂-NiCr+Ni and Cr₃C₂-NiCr coatings deposited by HVOF technique (the high-velocity oxygen fuel spray process) on ductile cast iron. The effect of nickel particles added to the chromium carbide coating on mechanical and wear behavior in the system of Cr ₃ C ₂ -NiCr+Ni/ductile cast iron was analyzed in order to improve the lifetime of coated materials. The structure with particular emphasis of characteristic of the interface in the system of composite coating (Cr ₃ C ₂ -NiCr+Ni)/ductile cast iron was studied using the optical, scanning, and transmission electron microscopes, as well as the analysis of chemical and phase composition in microareas. Experimental results show that HVOF-sprayed Cr₃C₂-NiCr+Ni composite coating exhibits low porosity, high hardness, dense structure with large, partially molten Ni particles and very fine Cr₃C₂ and Cr₇C₃ particles embedded in NiCr alloy matrix, coming to the size of nanocrystalline. The results were discussed in reference to examination of bending strength considering cracking and delamination in the system of composite coating (Cr ₃ C ₂ -NiCr+Ni)/ductile cast iron as well as hardness and wear resistance of the coating. The composite structure of the coating provides the relatively good plasticity of the coating, which in turn has a positive effect on the adhesion of coating to the substrate and cohesion of the composite coating (Cr₃C₂-NiCr+Ni) in wear conditions.

High-velocity oxy-fuel (HVOF) thermally sprayed Cr₃C₂-NiCr coatings have been shown to be effective in shielding important machinery and equipment components from wear in harsh, high-temperature conditions. In this investigation, the HVOF thermal spray coating technique was used to deposit Cr₃C₂-NiCr powder with 10% Co particles onto ductile cast iron. The effect of the Co particles on the mechanical, tribological, and microstructure characteristics of a Cr₃C₂-NiCr/ductile cast iron system was investigated. The microstructure analysis employed various techniques, including light microscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy-dispersive X-ray spectroscopy (EDS). Scratch tests were applied to analyze the coating quality and adhesion. The coatings created using the HVOF spray method with Cr₃C₂-NiCr powders mixed with Co particles exhibited a dense structure containing large Co particles, partially melted, and very fine Cr₃C₂ particles embedded into the NiCr alloy matrix. Additionally, they possessed high hardness and excellent adhesion to the substrate. The results of bending strength tests were also presented, together with information on the coating’s microhardness and fracture toughness. These included an analysis of the cracks and delamination in the Cr₃C₂-NiCr/ductile cast iron system. It was observed that the addition of Co particles significantly increased the resistance to cracking and wear behavior in the studied system.

Recent work indicates that the high-velocity oxy-fuel (HVOF) thermal spraying WC–Co coatings have been used to enhance the wear resistance of various engineering components in a variety of industrial environments. In the present work, WC–Co powder, containing Cr particles in an amount of 10%, was deposited on ductile cast iron with the HVOF thermal spray coating technique. An investigation was conducted to determine the role of Cr particles in the WC–Co coating produced with the HVOF technique on microstructure, mechanical, and wear properties in a system of type: WC-Co coating/ductile cast iron. The microstructure of the HVOF-sprayed WC–Co + Cr coating was characterised by light microscopy, X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and energy-dispersive X-ray spectroscopy (EDS). The analysis of the microstructure showed the formation of a coating with low porosity, compact structure, and good adhesion to the substrate with a typical lamellar structure composed of fine molten Cr particles and finely fragmented WC grains embedded in a Co matrix, reaching the size of nanocrystalline. The scratch test was applied for the analysis of the adhesion of coatings to the substrate. The erosion behaviour and mechanism of material removal was studied and discussed based on microstructural examinations. Moreover, the results were discussed in relation to the bending strength test, including cracks and delamination in the system of the WC–Co + Cr/ductile cast iron, as microhardness and erosion resistance of the coating. It was found that the addition of Cr particles to the WC–Co powder, which causes hardening of the binder phase is a key influence on increased mechanical and wear properties in the studied system. Additionally, due to the construction of nanostructured coatings, suitable proportion of hard and soft phases, the technique sprayed HVOF coatings have advantageous properties such as high density and good slurry erosion resistance.