Electrospinning is an emerging technique for the preparation of electrospun fiber membranes (ENMs), and a very promising one on the basis of the high-yield and the scalability of the process according to a process intensification strategy. Most of the research reported in the literature has been focused on the preparation of poly (vinylidene fluoride) (PVDF) ENMs by using N,N- dimethylformamide (DMF) as a solvent, which is considered a mutagenic and cancerogenic substance. Hence, the possibility of using alternative solvents represents an interesting approach to investigate. In this work, we explored the use of dimethyl sulfoxide (DMSO) as a low toxicity solvent in a mixture with acetone for the preparation of PVDF-ENMs. As a first step, a solubility study of the polymer, PVDF 6012 Solef^®, in several DMSO/acetone mixtures was carried out, and then, different operating conditions (e.g., applied voltage and needle to collector plate distance) for the successful electrospinning of the ENMs were evaluated. The study provided evidence of the crucial role of solution conductivity in the electrospinning phase and the thermal post-treatment. The prepared ENMs were characterized by evaluating the morphology (by SEM), pore-size, porosity, surface properties, and performance in terms of water permeability. The obtained results showed the possibility of producing ENMs in a more sustainable way, with a pore size in the range of 0.2–0.8 µm, high porosity (above 80%), and water flux in the range of 11.000–38.000 L/m²·h·bar.

The development of a volumetric apparatus (also known as a Sieverts’ apparatus) for accurate and reliable hydrogen adsorption measurement is shown. The instrument minimizes the sources of systematic errors which are mainly due to inner volume calibration, stability and uniformity of the temperatures, precise evaluation of the skeletal volume of the measured samples, and thermodynamical properties of the gas species. A series of hardware and software solutions were designed and introduced in the apparatus, which we will indicate as f-PcT, in order to deal with these aspects. The results are represented in terms of an accurate evaluation of the equilibrium and dynamical characteristics of the molecular hydrogen adsorption on two well-known porous media. The contribution of each experimental solution to the error propagation of the adsorbed moles is assessed. The developed volumetric apparatus for gas storage capacity measurements allows an accurate evaluation over a 4 order-of-magnitude pressure range (from 1 kPa to 8 MPa) and in temperatures ranging between 77 K and 470 K. The acquired results are in good agreement with the values reported in the literature.

Pinecones, a common biomass waste, has an interesting composition in terms of cellulose and lignine content that makes them excellent precursors in various activated carbon production processes. The synthesized, nanostructured, activated carbon materials show textural properties, a high specific surface area, and a large volume of micropores, which are all features that make them suitable for various applications ranging from the purification of water to energy storage. Amongst them, a very interesting application is hydrogen storage. For this purpose, activated carbon from pinecones were prepared using chemical activation with different KOH/precursor ratios, and their hydrogen adsorption capacity was evaluated at liquid nitrogen temperatures (77 K) at pressures of up to 80 bar using a Sievert’s type volumetric apparatus. Regarding the comprehensive characterization of the samples’ textural properties, the measurement of the surface area was carried out using the Brunauer–Emmett–Teller method, the chemical composition was investigated using wavelength-dispersive spectrometry, and the topography and long-range order was estimated using scanning electron microscopy and X-ray diffraction, respectively. The hydrogen adsorption properties of the activated carbon samples were measured and then fitted using the Langmuir/ Töth isotherm model to estimate the adsorption capacity at higher pressures. The results showed that chemical activation induced the formation of an optimal pore size distribution for hydrogen adsorption centered at about 0.5 nm and the proportion of micropore volume was higher than 50%, which resulted in an adsorption capacity of 5.5 wt% at 77 K and 80 bar; this was an increase of as much as 150% relative to the one predicted by the Chahine rule.

Membrane distillation (MD) has recently gained considerable attention as a valid process for the production of fresh-water due to its ability to exploit low grade waste heat for operation and to ensure a nearly feed concentration-independent production of high-purity distillate. Limitations have been related to polarization phenomena negatively affecting the thermal efficiency of the process and, as a consequence, its productivity. Several theoretical models have been developed to predict the impact of the operating conditions of the process on the thermal polarization, but there is a lack of experimental validation. In this study, electrospun nanofiber membranes (ENMs) made of Poly(vinylidene fluoride) (PVDF) and doped with (1, 10-phenanthroline) ruthenium (II) Ru(phen)₃ were tested at different operating conditions (i.e., temperature and velocity of the feed) in direct contact membrane distillation (DCMD). The temperature sensitive luminophore, Ru(phen)₃, allowed the on-line and non-invasive mapping of the temperature at the membrane surface during the process and the experimental evaluation of the effect of the temperature and velocity of the feed on the thermal polarization.

To investigate and compare the surface roughness and morphology of posterior stromal lenticules created with a femtosecond laser using various pulse energies to that obtained with a mechanical microkeratome. A 150 kHz femtosecond laser platform (IntraLase iFS; Abbott Medical Optics) was programmed to create an 8.5-mm-diameter posterior stromal lenticule in 12 human corneal tissues. Specimens were dissected using different pulse energies (1.00, 0.75, 0.65, and 0.50) and fixed 2 μm spot separations. Three additional posterior corneal lenticules were prepared using a mechanical microkeratome (Moria Evolution 3; Moria). After the procedure, each corneal tissue was examined by atomic force microscopy (Autoprobe CP; Veeco). Femtosecond laser-treated tissues revealed similar morphological features, however, with significant differences in surface roughness in relation to the energy pulse used for lamellar dissection (P0.05). Atomic force microscopy submicron analysis of femtosecond-dissected donor tissues provided quantitative demonstration of the relation between pulse energy and stromal surface roughness. Surface quality of posterior corneal lenticules, comparable with that provided by mechanical microkeratome, is significantly improved when setting pulse energy for lamellar dissection of 0.50-μJ and 2-μm spot separations.