A laboratory method was designed and verified that allows for the testing of alkaline, magnesite-based reactive materials for permeable reactive barriers (PRBs) to remove heavy metals from contaminated groundwater. It was found that caustic calcined magnesia (CCM) with high reactivity and low solubility to remove Cu²⁺, Zn²⁺, Ni²⁺, and Mn²⁺ cations from mixed aqueous solutions can be prepared by calcination at a suitable temperature and residence time. Regarding the solubility of both the reactive material itself and the precipitates formed, the CCM should contain just a limited content of lime. One way is the calcination of a ferroan magnesite at temperatures above 1000 °C. However, the decrease in pH is accompanied by lower efficiency, attributed to the solid-phase reactions of free lime. A different way is the calcination of magnesite under the conditions when CaCO₃ is not thermally decomposed. The virtually complete removal of the heavy metals from the model solution was achieved using the CCM characterised by the fraction of carbonates decomposed of approximately 80% and with the highest specific surface area. CCM calcined at higher temperatures could also be used, but this would be associated with higher consumption of crude magnesite. Under the conditions considered in the present work, the product obtained by the calcination at 750 °C for 3 h appeared to be optimal. The full heavy metal removal was observed in this case using less magnesite, and, moreover, at a lower temperature (resulting, therefore, in a lower consumption of energy for the calcination and material handling).

This study addresses the development of advanced anode materials for lithium-ion batteries by investigating the high-entropy perovskite La(Co_0.2Mn_0.2Fe_0.2Ni_0.2Cu_0.2)O₃. The material was synthesized via spray drying of aqueous metal nitrate solutions, followed by calcination at various temperatures (800 °C/1 h, 1000 °C/1 h, 1000 °C/2 h, 1100 °C/1 h) to optimize structural properties. Structural analysis using X-ray diffraction confirmed the formation of a single-phase perovskite in the sample calcined at 1100 °C for 1 h, while SEM/EDS revealed homogeneous elemental distribution. Electrochemical testing of the powders as anode materials in coin-type lithium-ion cells revealed a trend of slightly increasing capacity over 150 cycles, with capacity ultimately reaching 617 mAh g⁻¹, indicating progressive electrochemical activation. Although the samples share the same composition, variations in calcination conditions resulted in differences in capacity and cycling behavior. These results demonstrate that synthesis parameters critically influence the electrochemical performance of high-entropy perovskites. The findings suggest that such materials have potential as stable anodes for next-generation lithium-ion batteries, contributing to improved durability and efficiency in energy-storage technologies.

A facile and cost-effective sol–gel method for the synthesis of uniformly porous alumina (Al₂O₃) was developed using stable CTAB/hexanol/water microemulsions as soft templates. The phase behavior of the ternary system was investigated to identify compositions that form kinetically stable microemulsions, with an optimal ratio of 7.5 wt.% CTAB, 5 wt.% hexanol, and 87.5 wt.% water exhibiting minimal droplet size variation over one week. Gelation was induced by partial neutralization to pH 4.2 with ammonium carbonate, promoting the formation of polynuclear Al species and enabling the uniform entrapment of hexanol droplets. Lyophilization preserved the porous network, and calcination at 500 °C yielded η-Al₂O₃ with a large specific surface area (~225 m²·g⁻¹) and a narrow mesopore size distribution centered around 100 nm, consistent with the original droplet size. Mercury porosimetry and SEM analyses confirmed a highly porous, low-density material (0.75 g·cm⁻³) with an interconnected pore morphology. This scalable synthesis method, supported by the high kinetic stability of the microemulsion, provides sufficient processing time and eliminates the need for post-synthesis purification. It shows strong potential for producing advanced alumina materials for use in energy storage, catalysis, and sensor applications.

The fusibility of ash from woodchip combustion is characterised in the present work. The impact of the increase in MgO, CaO, and Al₂O₃ content in the bio-ash on the classification of ash into categories according to slagging and fouling indices was evaluated. The ash was characterized based on the chemical composition using slagging and fouling indices. However, these ash composition changes did not assign the ash into categories of the indices F_U, S_R, R_S, and B/A (fouling, slagging, slag viscosity, basicity), with less ash inclination to slagging and fouling. The indices were primarily derived for ashes from coal combustion. The indices values characterizing the ash were compared with measured results of ash melting according to STN ISO 540. The measured ash fusibility values showed that the addition of magnesite, limestone, and alumina to dendro-ashes increases the DT (temperature of deformation), HT (temperature of hemisphere), and the AFI (ash fusibility index). There is no conformity between the values of the indices and the measurement of ash fusibility temperatures. In terms of temperatures in the combustion chamber, the measured sintering (T_sin) and DT are suitable for evaluating the tendency of ash to slagging and fouling as well as an accretion of ash particles sticking to the lining.