In the selective laser melting process (SLM), the region irradiated by the laser beam is melted and quickly solidified, forming solidification lines (laser scan tracks) with symmetrical shapes. Because of the unique (rapid) crystallization conditions, the subgrain structures, typically observed inside these solidification lines, could also have variable geometric symmetrical patterns, e.g., cellular, pentagonal, or hexagonal cellular. The existence of such distinctive microstructures in SLM-made alloys has a significant impact on their superior mechanical and corrosion properties. Thus, any modification of this symmetrical microstructure (due to post-processing) can degrade or improve the properties of SLM-fabricated alloys. This study presents the experimental results on the effects of heat treatment and ECAP on microstructure modification and corrosion behavior of SLM-fabricated AlSi10Mg alloy. Light microscopy, scanning electron microscopy (SEM), electron backscattered diffraction (EBSD), and X-ray diffraction (XRD) were used for microstructural analysis. The corrosion properties of the given samples were determined using open-circuit potential (OCP), potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) techniques. EBSD observations showed that the imposed strain resulted in an obvious reduction in grain size to ~1.42 µm and ~0.24 µm after the first and second ECAP passes, respectively. Electrochemical tests revealed that the corrosion resistance of the ECAP-processed AlSi10Mg alloy improved significantly, which was confirmed by a nobler E_corr and lower I_corr values, and higher polarization resistance. The final results indicated that the strain-induced crystalline defects provided more nucleation sites for the formation of a denser and thicker oxide film, thus enhancing the corrosion resistance of the AlSi10Mg alloy.

In this study, a dual rolls equal channel extrusion (DRECE) process has been applied for improving the mechanical properties of the 5754 alloy. Supplementary experiments involving metallography, electron backscattered diffraction (EBSD), and XRD tests were carried out to evaluate the effect of the DRECE process. XRD analysis showed that the maximum dislocation density was achieved after six DRECE passes, which were accompanied by the formation that is typical for low-strain structures. The increasing dislocation density, as well as grain refinement throughout DRECE deformation, resulted in an increase in the mechanical properties. Annealing of the as-deformed sample resulted in grain growth and strength reduction.

Hot extruded (EX) AZ61 magnesium alloy was processed by the twist channel angular pressing (TCAP) method, which combines equal channel angular pressing (ECAP) and twist extrusion (TE) processes and significantly improves the efficiency of the grain refinement process. Both the initial hot extruded AZ61 alloy and the alloy after completion of TCAP processing were examined by using optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron backscatter diffraction (EBSD) and their corresponding micro-tensile testing (M-TT) and hardness testing at room temperature. The results showed that the microstructure of hot extruded alloy was refined well by TCAP due to dynamic recrystallization (DRX) caused by TCAP. The tensile properties, investigated by micro-tensile testing (M-TT), of the AZ61 alloy were significantly improved due to refined microstructure. The highest tensile properties including YS of 240.8 MPa, UTS of 343.6 MPa and elongation of 21.4% of the fine-grained alloy with average grain size below 1.5 µm was obtained after the third TCAP pass at 200 °C using the processing route B_c.

The DRECE method belongs to the severe plastic deformation (SPD) processes used for the refinement of sheet metal elements. A forming device used in this method is currently being installed in the workplace in the Centre of Advanced Innovation Technologies, VSB Technical University of Ostrava. In the present work the structural characteristics and fracture morphology of Ck55 carbon steel after the application of the DRECE method with a forming tool angle of 118? are presented. The microstructure results are linked to selected mechanical properties. The tensile, hardness, and fatigue tests are performed. The methodology of non-destructive residual stresses measurement in the carbon steel after the extrusion and application of tensile tests on small samples are important for their use in technical practice. The paper presents the original results of selected properties after the application of the DRECE method on Ck55 steel, which will be used in the future to assess the application of the DRECE method and to determine other directions of the processing of ferrous alloys and steels.

This article presents a study on the influence of temperature and time of multi-variant heat treatment on the structure and properties of materials produced in direct metal laser sintering (DMLS) and casting technology. The materials were manufactured in the form of cuboidal elements with a cross-section of 1.5 mm × 15 mm and a length of 60 mm. The samples prepared in this way had a similar volume, but due to the production technology the metal crystallization took place at different rates and directions. In the cast, the direction of heat transfer was toward the mold, and the DMLS was directed locally layer by layer. The small thickness of the cast material allowed reaching conditions similar to the DMLS cooling process. Both DMLS and cast samples show similar mechanical properties (hardness) achieved after long ageing time, i.e., 16 h at 170 °C. The maximum hardness was observed for 8 h. In the DMLS samples, in contrast to cast samples, no lamellar precipitates of silicon were observed, which indicates their better resistance to cracking