The paper presents the results of tests of rapid solidification (RS) aluminum alloys with the addition of silicon (5%, 11%, and 20%). Casting by melt-spinning on the surface of an intensively cooled copper cylinder allowed to obtain a metallic material in the form of flakes, which were then consolidated in the process of pressing and direct extrusion. The effect of refinement on structural components after rapid solidification was determined. Rapidly solidified AlSi materials are characterized by a comparable size of Si particles, regardless of the silicon content, and the shape of these particles is close to spheroidal. Not only Si particles are fragmented, but also the Al-Si-Fe phase, which also changed its shape from irregular with sharp edges to regular and spherical. The melt-spinning process resulted in a fine-grained structure compared to materials obtained by gravity-casting and extrusion. The influence of the high-temperature compression test on the mechanical properties of rapidly solidified materials was analyzed, and the results were compared with those of gravity-cast materials. An increase in strength properties was found in the case of the AlSi5 RS alloy by 20%, in the case of AlSi11RS by 25%, and in the case of the alloy containing 20% Si by as much as 86% (tensile test). On the basis of the homogeneity of the particle distribution determined by the SEM method, it was found that rapid solidification is an effective method of increasing the strength properties and improving the plastic properties of Al-Si alloys.

The paper presents the results of the joining tests of the EN AW-6082 T6 alloy. The materials were joined using the EBW high-energy (electron beam welding) and friction stir welding (FSW) methods. In the case of FSW welding, the following parameters were used: the linear speed was 355 mm/min, and the rotational speed of the welding tool was 710. In the case of EBW welding, the following parameters were used: accelerating voltage U = 120 kV, beam intensity I = 18.7 mA, welding speed v = 1600 mm/min and, in the case of a smoothing weld, U = 80 kV, beam intensity I = 17 mA, and welding speed v = 700 mm/min. Comprehensive microstructural tests of all welded joints (MO, SEM and TEM) and mechanical property tests (tensile and hardness tests) were carried out. The topographies of the fractures after the tensile test were also examined. Based on the results, it was found that the strength properties of the EBW joint were reduced by 23% and the FSW joint by 38% compared to the base material. A decrease in elongation was also noted, with an FSW elongation of 7.2% and an elongation of 2.7% for EBW. In the case of the EBW joint, magnesium evaporation was found in the weld during welding, while in the FSW joint, the dissolution of the Mg2Si particles responsible for strengthening the material during heat treatment to the T6 state was observed.

Civilization and technical progress are not possible without energy. Dynamic economic growth translates into a systematic increase in demand for electricity. Ensuring the continuity and reliability of electricity supplies is one of the most important aspects of energy security in highly developed countries. Growing energy consumption results not only in the need to build new power plants but also in the need to expand and increase transmission capacity. Therefore, large quantities of electric cables are produced all over the world, and after some time, they largely become waste. Recycling of electric cables focuses on the recovery of metals, mainly copper and aluminum, while polymer insulation is often considered waste and ends up in landfills. Currently, more and more stringent regulations are being introduced, mainly environmental ones, which require maximizing the reduction in waste. This article provides a literature review on cable recycling, presenting the advantages and disadvantages of various recycling methods, including mechanical and material recycling. It has been found that currently, there are very large possibilities for recycling cables, and intensive scientific work is being carried out on their development, which is consistent with global climate policy.

Recycling of raw materials and is crucial for the production of new products for the global economy. The aim here is, on the one hand, to reduce energy consumption, and, on the other hand, to obtain materials with similar functional properties. The study undertook research on the possibility of processing AlSi11 aluminum chips by compaction and co-extruding to obtain a product in the form of a flat bar with mechanical properties not lower than those of the cast materials. The performed tests and the developed technique allowed to obtain flat bars with more favorable mechanical properties (Yield Strength YS ≥ 155 MPa; Ultimate Tensile Strength UTS ≥ 212 MPa) than the castings (YS ≥ 70 MPa ≥ 150 MPa). The weldability evaluation tests revealed that the material is susceptible to porosity. The presence of pores, which reduces the cross-section (up to 60%), reduces the tensile strength (up to 20 MPa). The typical joint structure and plasticity is obtained, which indicate the possibility of tensile strength improvement.

Continuous pressure put on researchers all over the world these days to design materials of improved properties create opportunities to study new methods of production in conjunction with entirely new and innovative materials such as alloys or composites. The authors in the current research manufactured aluminium reinforced with glass fibre (GF) using metallurgical synthesis, which is an unconventional and not sufficiently studied method of production. The composites with 1, 2 and 5 wt.% of glass fibre were produced with additional material obtained using consolidation of aluminium powder in extrusion process as reference material with 5 wt.% of glass fibre. All the materials were subjected to series of tests in order to determine their microstructure, density, electrical properties, hardness and susceptibility to plastic working in the compression test. It was found that glass fibre during metallurgical synthesis of aluminium composite partially melted and thus did not reinforce the material as well as during extrusion, which has been observed not only in the scanning electron microscope (SEM) and energy-dispersive X-ray (EDX) analysis but also in the analysis of macroscopic physical and mechanical properties. Based on the analysed samples, it may be stated that electrical conductivity of the samples obtained via metallurgical synthesis is higher than might be estimated on the basis of the rule of mixtures and glass fibre content and concerning the sample with 5 wt.% of GF is higher (32.1 MS/m) than of the reference material obtained in extrusion process (30.6 MS/m). Similar situation has been observed in terms of hardness of the tested samples where a minor increase in hardness was noticeable as the amount of glass fibre increased in the composites obtained by metallurgical synthesis. It is believed to be related to the melting of glass fibre, which reduced the volume fraction of GF containing mainly silicon oxides and their diffusion into the aluminium matrix, thus causing solid solution strengthening.

The paper is devoted to highlighting the potential application of the quantitative imaging technique through results associated with work hardening, strain rate and heat generated during elastic and plastic deformation. The aim of the research presented in this article is to determine the relationship between deformation in the uniaxial tensile test of samples made of 1-mm-thick nickel-based superalloys and their change in temperature during deformation. The relationship between yield stress and the Taylor–Quinney coefficient and their change with the strain rate were determined. The research material was 1-mm-thick sheets of three grades of Inconel alloys: 625 HX and 718. The Aramis (GOM GmbH, a company of the ZEISS Group) measurement system and high-sensitivity infrared thermal imaging camera were used for the tests. The uniaxial tensile tests were carried out at three different strain rates. A clear tendency to increase the sample temperature with an increase in the strain rate was observed. This conclusion applies to all materials and directions of sample cutting investigated with respect to the sheet-rolling direction. An almost linear correlation was found between the percent strain and the value of the maximum surface temperature of the specimens. The method used is helpful in assessing the extent of homogeneity of the strain and the material effort during its deformation based on the measurement of the surface temperature.