The purpose of this work was to characterize an influence of the electric bias field on the elastic stiffness constants of important and unusual piezoelectric material Lead Zinc Niobate-Lead Titanate (PZN-PT). The longitudinal and transverse mode of sound propagation in single crystals containing 4.5% PT were studied. The influence of electric field, which poles the sample, is investigated by the pulse-echo sound propagation technique. From these measurements, the values of complex elastic stiffness constants are evaluated at different poling conditions with different frequencies for longitudinal and sheer excitations. Crystal cuts [001], [110] and [111] served for measurements of the elastic stiffness constants under application of the electric field. Aspects of field-induced phase transitions in PZN-4.5%PT single crystals at room temperature are discussed. Hysteretic behavior has an influence on attenuation and velocity of ultrasound.

Forgings produced in industry are an irreplaceable basis for subsequent elaborating on machine tools. The quality of the semi-finished product produced by forging is a necessary prerequisite for ensuring the final quality of the final product because the forging can produce some defects. The presented paper is aimed at investigation of selected characteristics of forging steel specimens for various levels of their relative reduction. Ultrasound testing belongs to methods for investigation of structure changes, including defects. Experimental investigation, using both the attenuation and velocity measurements, verify that the reduction of specimens’ material can have an effect on the propagation of ultrasound waves passing through the specimen body. The procedure of steel samples forging corresponds accordingly to the process of their hardening. The increase of toughness after relative reduction of forging in the range of 10–50% is with highest probability caused by the strength matrices development due to the relatively important deformation hardening. It is evident that the deformation hardening is almost the same after every 10% addition of relative reduction. Experiments are supplemented by Barkhausen noise detection and metallographic characteristics of the samples. While differences between the Barkhausen noise values are in principle relatively small and significant differences are only in the values of the position of the envelope, there is maximum coincidence with ultrasonic investigation.

The effect of Mn-doped zinc ferrite nanoparticles at a low volume concentration (1 × 10⁻⁴) on structural changes in the nematic liquid crystals 6CHBT and 5CB, induced by weak magnetic fields, was investigated using surface acoustic wave (SAW) and light transmission (LT) techniques. Structural changes caused by the applied magnetic field, in both increasing and decreasing modes, as well as after pulsed changes, were examined by measuring the responses of SAW attenuation and LT using a linearly polarized laser beam. The influence of nanoparticle shape (rods, needles, and clusters) and temperature on the structural changes was investigated. A shift in the threshold field and the transition temperature was observed. In addition, the magnetic properties of the individual samples in powder form were examined using M–H curves, M–T curves, and XRD patterns. The results obtained from all measurements are compared, and the effectiveness of each technique, considering the influence of nanoparticle shape and suspension stability, was evaluated.