Titanium and its alloys have superior electrochemical properties compared to other alloy systems due to the formation of a protective TiO₂ film on metal surfaces. The ability to generate the protective oxide layer will depend upon the type of alloy to be used. The aim of this work was to characterize the electrochemical corrosion behavior of titanium Ti-CP2 and alloys Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V, and Ti Beta-C. Samples were anodized in 1 M H₂SO₄ and H₃PO₄ solutions with a current density of 0.025 A/cm². Electrochemical tests on anodized alloys were carried out using a three-electrode cell and exposed in two electrolytes, i.e., 3.5 wt % NaCl and 3.5 wt % H₂SO₄ solutions at room temperature. Scanning electron microscopy (SEM) was used to observe the morphology of anodized surfaces. The electrochemical techniques used were cyclic potentiodynamic polarization (CPP) and electrochemical noise (EN), based on the ASTM-G61 and G199 standards. Regarding EN, two methods of data analysis were used: the frequency domain (power spectral density, PSD) and time-frequency domain (discrete wavelet transform). For non-anodized alloys, the results by CCP and EN indicate icorr values of ×10⁻⁶ A/cm². However, under anodizing conditions, the icorr values vary from ×10⁻⁷ to ×10⁻⁹ A/cm². The PSD Ψ⁰ values are higher for non-anodized alloys, while in anodized conditions, the values range from −138/−122 dBi (A²·Hz⁻¹)^1/2 to −131/−180 dBi (A²·Hz⁻¹)^1/2. Furthermore, the results indicated that the alloys anodized in the H₃PO₄ bath showed an electrochemical behavior that can be associated with a more homogeneous passive layer when exposed to the 3.5 wt % NaCl electrolyte. Alloys containing more beta-phase stabilizers formed a less homogeneous anodized layer. These alloys are widely used in aeronautical applications; thus, it is essential that these alloys have excellent corrosion performance in chloride and acid rain environments.

Biopolymers are promising materials as electrolytes with high flexibility, good performance, cost effectiveness, high compatibility with solvents, and film-forming ability. Chitosan (CS) and carboxymethylcellulose (CMC) can form an intermolecular complex, giving rise to hydrogels capable of absorbing ionic solutions. Citric acid (CA) is an effective biological chemical crosslinker that assists the formation of amide and ester bonds between CMC and CS, resulting in a structure with high ionic conductivity and good structural integrity. In this study, a chemical crosslinking strategy is used to synthesize electrolyte hydrogels for zinc–air batteries. The effects of crosslinking are studied on the structural and electrochemical performance of the membranes. The results show an improvement in the ionic conductivity with respect to the homologous electrolyte hydrogel systems reported, with a maximum of 0.19 S∙cm⁻¹ at 30 °C. In addition, the cyclic voltammetry studies showed a current intensity increase at higher CA content, reaching values of 360 mA∙cm⁻². Structural characterization suggests a higher thermal stability and a decrease in the degree of crystallinity caused by the polymers’ crosslinking. Finally, these membranes were tested in Zn–air batteries, obtaining power densities of 85 mW∙cm⁻². The proposed hydrogels show to be appropriate for energy zinc–air battery applications and present an alternative to support the sustainable energy transition.

Custom 450 stainless steel and AM 350 stainless steel are both precipitation hardening stainless steels, which are widely used in a variety of aerospace applications. The former steel exhibits very good corrosion resistance with moderate strength, whereas the latter is used for applications requiring high strength along with corrosion resistance. In this study, the corrosion behavior of CUSTOM 450 and AM 350 stainless steels passivated in (a) citric acid and (b) nitric acid solutions for 50 and 75 min at 49 and 70 °C, and subsequently exposed in 5 wt. % NaCl and 1 wt. % H₂SO₄ solutions are investigated. Two electrochemical techniques were used: electrochemical noise (EN) and electrochemical impedance spectroscopy (EIS) according to ASTM G199-09 and ASTM G106-13, respectively. The results indicated that passivation in nitric acid made the surface prone to localized corrosion. Statistical and PSD values showed a tendency toward pitting corrosion. On the whole, passivated CUSTOM 450 stainless steel showed the best corrosion behavior in both, NaCl and H₂SO₄ test solutions.

This study evaluated the corrosion inhibitory effects of Ruta graveolens leaf extract for 304 stainless steel in 1 M HCl. The analysis of the leaf extract using HPLC indicated that the primary compounds present in the leaf extract were rutin, caffeic acid, p-coumaric acid, and apigenin. The inhibition efficiency (IE%) of the extract was studied using weight loss, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and computational simulation (density functional theory, DFT). The effects of the inhibitor concentration and solution temperature were investigated. The results indicated that the IE% increased for increasing concentrations of the extract, while the reverse was true with increasing temperatures. At 25 °C and a 600 ppm extract concentration, the results indicated a maximum inhibition efficiency of 95%, 98%, and 96% by weight loss, potentiodynamic polarization, and EIS techniques, respectively. SEM observations showed a significant change in the surface morphology of the 304 SS with and without the addition of the inhibitor compound. At all temperatures, the adsorption of the inhibitor components onto the 304 SS surface was found to follow the Langmuir isotherm model, and the inhibition process was governed by physical adsorption. Furthermore, chemical interactions between the inhibitor and the 304 SS steel surface were elucidated via density functional theory (DFT) calculations.

Meeting the ever-increasing global energy demands through sustainable and environmentally friendly means is a paramount challenge. In response to this imperative, this study is dedicated to the development of biopolymer electrolytes, which hold promise for improving the efficiency, safety, and biodegradability of energy systems. The present study aims to evaluate hydrogels synthesized from chitosan biopolymer and starch from avocado seed residues in different ratios, and dried using freeze-thawing and freeze-drying techniques. Epichlorohydrin was used as a chemical crosslinker to create a suitable degree of swelling using an ionic solution. Physical freezing crosslinking strategies such as freezing–thawing and freezing–drying were performed to generate a denser porous structure in the polymer matrix. Subsequently, synthesized electrolytes were immersed in 12 M KOH solution to improve their electrochemical properties. The effect of the different ratios of starch in the hydrogels on the structural properties of the materials was evaluated using characterization techniques such as FTIR and XRD, which allowed to confirm the crosslinking between chitosan and starch. The electrochemical performance of the hydrogels is assessed using electrochemical impedance spectroscopy. A maximum conductivity value of 0.61 S·cm⁻¹ was achieved at room temperature. The designed materials were tested in prototype zinc–air batteries; their specific capacity value was 1618 mA h·g⁻¹, and their obtained power density was 90 mW·cm⁻². These substantial findings unequivocally underscore the potential of the synthesized hydrogels as highly promising electrolytes for the application in zinc–air battery systems.

The aim of this work was to evaluate the corrosion behavior of the AA6061 and AlSi10Mg alloys produced by extruded and additive manufacturing (selective laser melting, SLM). Alloys were immersed in two electrolytes in H₂O and 3.5 wt. % NaCl solutions at room temperature and their corrosion behavior was studied by electrochemical noise technique (EN). Three different methods filtered EN signals, and the statistical analysis was employed to obtain Rn, the localization index (LI), Kurtosis, skew, and the potential spectral density analysis (PSD). The Energy Dispersion Plots (EDP) of wavelets method was employed to determine the type of corrosion and the Hilbert–Huang Transform (HHT), analyzing the Hilbert Spectra. The result indicated that the amplitude of the transients in the time series in potential and current is greater in the AlSi10Mg alloy manufactured by additive manufacturing. The amplitude of the transients decreases in both alloys (AA6061 and AlSi10Mg) as time increases.