Boron nitride nanotubes (BNNTs) have many fascinating properties and a wide range of applications. An improved ball milling method has been developed for high-yield BNNT synthesis, in which metal nitrate, such as Fe(NO3)3, and amorphous boron powder are milled together to prepare a more effective precursor. The heating of the precursor in nitrogen-containing gas produces a high density of BNNTs with controlled structures. The chemical bonding and structure of the synthesized BNNTs are precisely probed by near-edge X-ray absorption fine structure spectroscopy. The higher efficiency of the precursor containing milling-activated catalyst is revealed by thermogravimetric analyses. Detailed X-ray diffraction and X-ray photoelectron spectroscopy investigations disclose that during ball milling the Fe(NO3)3 decomposes to Fe which greatly accelerates the nitriding reaction and therefore increases the yield of BNNTs. This improved synthesis method brings the large-scale production and application of BNNTs one step closer.

Superwetting surfaces are widely used in many engineering fields for reducing energy and resistance loss. A facile and efficient method using laser etching has been used to fabricate and control superwettable drag reduction surfaces. Inspired by the self-cleaning theory of lotus leaves, we propose controllable patterned bionic superhydrophobic surfaces (BSSs) simulating the uneven micro/nanostructures of lotus leaves. The superhydrophobicity and drag reduction ratios at low velocities are highly improved using a laser ablation method on metal substrates. However, unstable air layers trapped on superhydrophobic surfaces are usually cut away by a high-velocity flow, which greatly reduces the drag reduction performance. The fabricated bionic superhydrophobic/hydrophilic surfaces (BSHSs) with alternated hydrophilic strips can build a large surface energy barrier to bind the three-phase contact line. It maintains the stable drag reduction by capturing the air bubbles attached to the hydrophilic strips at a high velocity. Three-dimensional simulation analysis and equipment to measure the weak friction of a self-assembled solid–liquid interface are used to explain the drag reduction mechanism and measure the drag reduction ratios at different flow speeds. BSSs achieve an improved drag reduction effect (maximum 52.76%) at a low velocity (maximum 1.5568 m/s). BSHSs maintain an improved and steady drag reduction effect at high speed. The drag reduction ratios can be maintained at about 30% at high speed, with a maximum value of 4.448 m/s. This research has broad application prospects in energy saving, liquid directional transportation, and shipping due to their robust superhydrophobic properties and stable drag reduction effect.

Our previous research work indicated that highly boron doped polysilicon nanofilms (≤100 nm in thickness) have higher gauge factor (the maximum is ~34 for 80 nm-thick films) and better temperature stability than common polysilicon films (≥ 200nm in thickness) at the same doping levels. Therefore, in order to further analyze the influence of deposition temperature on the film structure and piezoresistance performance, the piezoresistive sensitivity, piezoresistive linearity (PRL) and resistance time drift (RTD) of 80 nm-thick highly boron doped polysilicon nanofilms (PSNFs) with different deposition temperatures were studied here. The tunneling piezoresistive model was established to explain the relationship between the measured gauge factors (GFs) and deposition temperature. It was seen that the piezoresistance coefficient (PRC) of composite grain boundaries is higher than that of grains and the magnitude of GF is dependent on the resistivity of grain boundary (GB) barriers and the weight of the resistivity of composite GBs in the film resistivity. In the investigations on PRL and RTD, the interstitial-vacancy (IV) model was established to model GBs as the accumulation of IV pairs. And the recrystallization of metastable IV pairs caused by material deformation or current excitation is considered as the prime reason for piezoresistive nonlinearity (PRNL) and RTD. Finally, the optimal deposition temperature for the improvement of film performance and reliability is about 620 °C and the high temperature annealing is not very effective in improving the piezoresistive performance of PSNFs deposited at lower temperatures.

In this paper, we proposed a novel bonding technology to fabricate a microfluidic device based on Poly(methyl methacrylate) (PMMA). The method, which used chloroform and ethanol as miscible bonding solvent, can complete complex structures rapid assembly (10 min) at 40°C. A bonding strength of 267.5 N/cm² can be achieved, while the micro channel deformation was less than 7.26%. Then we utilized this method to produce a three layers micro mixer, which included a T-shaped inlet channel and six H-shaped mixing units. Numerical simulation indicated that, the well mixing length of the mixer was only about 6 mm when Re = 10. Finally, fluorescence microscopy was used to verify mixer performance. The method provided the potential for mass production of multilayer rigid polymer microfluidic devices.

Sigma-delta (ΣΔ) closed-loop operation is the best candidate for realizing the interface circuit of MEMS accelerometers. However, stability and reliability problems are still the main obstacles hindering its further development for high-end applications. In situ self-testing and calibration is an alternative way to solve these problems in the current process condition, and thus, has received a lot of attention in recent years. However, circuit methods for self-testing of ΣΔ closed-loop accelerometers are rarely reported. In this paper, we propose a fifth-order ΣΔ closed-loop interface for a capacitive MEMS accelerometer. The nonlinearity problem of the system is detailed discussed, the source of it is analyzed, and the solutions are given. Furthermore, a built-in self-test (BIST) unit is integrated on-chip for in situ self-testing of the loop distortion. In BIST mode, a digital electrostatic excitation is generated by an on-chip digital resonator, which is also ΣΔ modulated. By single-bit ΣΔ-modulation, the noise and linearity of excitation is effectively improved, and a higher detection level for distortion is easily achieved, as opposed to the physical excitation generated by the motion of laboratory equipment.

The wettability of boron nitride nanotube (BNNT) films was modified using a combination of pulsed and continuous wave (CW) mode plasma. The combined mode effectively modified the wettability of BNNT films and kept the nanostructures intact. The BNNT films changed from superhydrophobic to superhydrophilic after combined mode treatment at 600 W min. In contrast, the contact angle controllable decreased linearly in a controllable way with increasing energy input before eventually becoming superhydrophilic after 1000 W min of CW mode treatment. A high concentration of graft functional groups formed, along with point defects. More point defects formed when using combined modes and higher energy input. Mainly amine functional groups were grafted by combined mode plasma, while the CW mode plasma led to more formation of amide and imine on the BNNTs. Research into controllable wettability and selection of grafted functional groups should enable promising applications of BNNTs in composites and biology in the future.