A piezoelectric nanogenerator (PNG) that is based on c-axis GaN nanowires is fabricated on flexible substrate. In this regard, c-axis GaN nanowires were grown on GaN substrate using the vapor-liquid-solid (VLS) technique by metal organic chemical vapor deposition. Further, Polydimethylsiloxane (PDMS) was coated on nanowire-arrays then PDMS matrix embedded with GaN nanowire-arrays was transferred on Si-rubber substrate. The piezoelectric performance of nanowire-based flexible PNG was measured, while the device was actuated using a cyclic stretching-releasing agitation mechanism that was driven by a linear motor. The piezoelectric output was measured as a function of actuation frequency ranging from 1 Hz to 10 Hz and a linear tendency was observed for piezoelectric output current, while the output voltages remained constant. A maximum of piezoelectric open circuit voltages and short circuit current were measured 15.4 V and 85.6 nA, respectively. In order to evaluate the feasibility of our flexible PNG for real application, a long term stability test was performed for 20,000 cycles and the device performance was degraded by less than 18%. The underlying reason for the high piezoelectric output was attributed to the reduced free carriers inside nanowires due to surface Fermi-level pinning and insulating metal-dielectric-semiconductor interface, respectively; the former reduced the free carrier screening radially while latter reduced longitudinally. The flexibility and the high aspect ratio of GaN nanowire were the responsible factors for higher stability. Such higher piezoelectric output and the novel design make our device more promising for the diverse range of real applications.

Understanding the thermal stability and degradation mechanism of β-Ga2O3 metal-oxide-semiconductor field-effect transistors (MOSFETs) is crucial for their high-power electronics applications. This work examines the high temperature performance of the junctionless lateral β-Ga2O3 FinFET grown on a native β-Ga2O3 substrate, fabricated by metal-assisted chemical etching with Al2O3 gate oxide and Ti/Au gate metal. The thermal exposure effect on threshold voltage (Vth), subthreshold swing (SS), hysteresis, and specific on-resistance (Ron,sp), as a function of temperature up to 298 °C, is measured and analyzed. SS and Ron,sp increased with increasing temperatures, similar to the planar MOSFETs, while a more severe negative shift of Vth was observed for the high aspect-ratio FinFETs here. Despite employing a much thicker epilayer (∼2 μm) for the channel, the high temperature performance of Ion/Ioff ratios and SS of the FinFET in this work remains comparable to that of the planar β-Ga2O3 MOSFETs reported using epilayers ∼10–30× thinner. This work paves the way for further investigation into the stability and promise of β-Ga2O3 FinFETs compared to their planar counterparts.

Human skin contains slowly adaptive (SA) and rapidly adaptive (RA) mechanoreceptors, which respond differently to external stimuli. Based on human tactile perception principles, the fabrication of a self-powered electronic skin (e-skin) that simultaneously mimics SA- and RA-mechanoreceptors is a prime need for robots and artificial prosthetics to interact with the surrounding environment. However, the complex process of merging multimode sensors to mimic SA- and RA-mechanoreceptors hinders their utilization in e-skins. We proposed SA- and RA-mechanoreceptors based on n-type and semi-insulating GaN nanowire arrays. The SA- and RA-mechanoreceptors demonstrated distinguished features such as grasping of objects and detection of their surface textures. Based on piezoelectric sensing principles, the proposed e-skin can simultaneously mimic static and dynamic pressure signals. Mechanoreceptors further detected several stimuli of various pressures with low and high frequencies. The response and reset times showed by SA-mechanoreceptors were 11 and 18 ms under 1-Hz frequency, which are rapid enough for practical e-skin applications.