Low-density polyethylene composites containing different sizes of calcium oxide (CaO) nanoparticles were obtained by melt mixing. The CaO nanoparticles were synthesized by either the sol-gel or sonication methods, obtaining two different sizes: ca. 55 nm and 25 nm. These nanoparticles were used either as-synthesized or were modified organically on the surface with oleic acid (Mod-CaO), at concentrations of 3, 5, and 10 wt% in the polymer. The Mod-CaO nanoparticles of 25 nm can act as nucleating agents, increasing the polymer’s crystallinity. The Young’s Modulus increased with the Mod-CaO nanoparticles, rendering higher reinforcement effects with an increase as high as 36%. The reduction in Escherichia coli bacteria in the nanocomposites increased with the amount of CaO nanoparticles, the size reduction, and the surface modification. The highest antimicrobial behavior was found in the composites with a Mod-CaO of 25 nm, presenting a reduction of 99.99%. This strong antimicrobial effect can be associated with the release of the Ca²⁺ from the composites, as studied for the composite with 10 wt% nanoparticles. The ion release was dependent on the size of the nanoparticles and their surface modification. These findings show that CaO nanoparticles are an excellent alternative as an antimicrobial filler in polymer nanocomposites to be applied for food packaging or medical devices.

Polymer-based nanocomposites such as polycaprolactone/graphene oxide (PCL/GO) have emerged as alternatives for bone tissue engineering (BTE) applications. The objective of this research was to investigate the impact of a gelatin (Gt) coating on the degradability and different properties of PCL nanofibrous scaffolds fabricated by an electrospinning technique with 1 and 2 wt% GO. Uniform PCL/GO fibers were obtained with a beadless structure and rough surface. PCL/GO scaffolds exhibited an increase in their crystallization temperature (Tc), attributed to GO, which acted as a nucleation agent. Young’s modulus increased by 32 and 63% for the incorporation of 1 and 2 wt% GO, respectively, in comparison with neat PCL. A homogeneous Gt coating was further applied to these fibers, with incorporations as high as 24.7 wt%. The introduction of the Gt coating improved the hydrophilicity and degradability of the scaffolds. Bioactivity analysis revealed that the hydroxyapatite crystals were deposited on the Gt-coated scaffolds, which made them different from their uncoated counterparts. Our results showed the synergic effect of Gt and GO in enhancing the multifunctionality of the PCL, in particular the degradability rate, bioactivity, and cell adhesion and proliferation of hGMSC cells, making it an interesting biomaterial for BTE.

Hydrothermal carbonization (HTC) of rice husk was optimized in terms of the adsorption capacity at equilibrium (q_e) and hydrochar mass yield (MY). The studied variables were reaction temperature, residence time, and biomass-to-water ratio by means of response surface methodology. In both cases, reaction temperature resulted the most significant parameter promoting high q_e values at higher temperatures when treating methylene blue (MB) as the target pollutant. Nevertheless, MY was low (~40%) when focusing on a possible industrial application. Hence, maximizing q_e and MY simultaneously by optimization of multiple responses emerges as a promising solution to improve MY values (>60%) with no significant differences regarding the q_e response. Furthermore, additional activation was conducted on optimal hydrochars to further investigate the enhancement of q_e. As a result, no statistical differences between non-modified and activated hydrochars were observed for q_e; however, the pseudo-second-order constant (k₂) seemed to be increased after alkali activation, mainly due to a larger surface area. Non-modified and activated hydrochars were characterized via SEM, FTIR, XRD, and BET, resulting in two significant effects contributing to MB adsorption: increased surface area and functionalized hydrochar surface. Consequently, this work provides valuable insights on subsequent application of this HTC optimization scheme at an industrial scale.

This study reports the development and characterization of hierarchical electrospun scaffolds based on poly (L-lactic acid) (PLA) and polyacrylonitrile (PAN) reinforced with calcium oxide (CaO) nanoparticles (18.5 ± 4.7 nm) for skin regeneration. Six configurations, including two five-layer multilayer systems (PLA/PAN/CaO and PAN/PLA/CaO), were evaluated to determine how composition and deposition sequence influence physicochemical, mechanical, and biological performance. FT-IR, XRD and DSC confirmed the successful integration of CaO, while thermal analysis evidenced an effect of chain mobility and interfacial interactions within multilayer systems. Cross-sectional SEM revealed the presence of both fibers with continuous interfaces. Nitrogen adsorption showed that CaO significantly increased the specific surface area (e.g., from 4.6 m²/g in neat PLA to 21.65 m²/g in PLA/CaO), with type IV isotherms indicating mesoporosity. Wettability assays demonstrated reduced contact angle in PLA (from 126.3° to 91.8°) and sequence-dependent surface properties in multilayers. Tensile testing confirmed that the multilayer architecture bridged the mechanical gap between compliant PLA and high-strength PAN, yielding intermediate moduli (~10–11 MPa) and balanced toughness. Antibacterial assays against S. aureus and E. coli showed that CaO significantly reduced bacterial viability, with PLA/PAN/CaO achieving the highest inhibition (up to 37.1%). In vitro HaCaT assays and in vivo implantation in BALB/c mice confirmed high cytocompatibility and biocompatibility. These findings demonstrate that multilayer electrospinning of PLA/PAN/CaO enables the design of structurally integrated, bioactive, and mechanically balanced scaffolds for advanced wound healing and dermal repair.

This work describes an efficient and environmentally friendly method for the synthesis of silver-based nanostructures through a green route using Aloe vera extract as a reducing agent, silver nitrate (AgNO₃) as a precursor, and polyvinylpyrrolidone (PVP, 10 kDa molecular weight) as a stabilizing agent. The formation of these structures was supported by UV–Vis spectroscopy, where a surface plasmon resonance (SPR) band was observed between 425 and 460 nm. Scanning electron microscopy revealed predominantly spherical features in the 300–500 nm range; however, the distinction between primary nanoparticles and aggregates cannot be conclusively established from SEM alone. EDX analysis indicated a silver content of 59.96 wt%. Antibacterial assays performed in Z8 medium demonstrated a reduction in cyanobacterial growth with increasing dosage, with complete inhibition observed at ≥20 $\mu$L (nominal MIC = 1.77 mg mL⁻¹, based on precursor estimation). Total dissolved solids and absorbance measurements exhibited a decreasing trend with increasing concentration (effect size = 0.87, $p<0.001$), supporting an inhibitory effect under the tested conditions. These findings suggest potential antibacterial activity. However, this study should be considered exploratory, and further work is required to elucidate the underlying mechanisms.