We studied the effect of CrC interlayers with different carbon contents on the adhesion of CrC/a-C:H coatings prepared by anode assisted reactive magnetron sputtering combined with DC-pulsed plasma enhanced chemical vapor deposition. The adhesion of the coating was measured by indentation and scratching. The coatings were characterized by Raman, XPS, SEM and Nanoindentation. The adhesion of the CrC/a-C:H coating is best when the carbon content in the interlayer of CrC is 44.5%, the scratch adhesion is 74 N, and the indentation adhesion is HF1. In this case, the elastic modulus of the interlayer CrC (284 GPa) is closest to that of the a-C:H layer (274 GPa). In conclusion, when there is no graphitization in the CrC interlayer, and the elastic modulus of the CrC interlayer is close to that of the a-C:H layer, the CrC/a-C:H coatings show the best adhesion.

We investigate the nanostructures and phase diagrams of ABC linear triblock copolymers confined in spherical cavities by using real-space self-consistent field theory. Various 3D morphologies, such as spherical concentric lamellae, dumbbell-like cylinder, and rotational structures, are identified in the phase diagrams, which are constructed on the basis of the diameters of spherical cavities and the interaction between the polymers and preferential surfaces. We designate specific monomer-monomer interactions and block compositions, with which the polymers spontaneously form a cylindrical morphology in bulk, and firstly study morphology transformation with a neutral surface when a confining radius progressively increases. We then focus on phase morphologies under the preferential surfaces and consolidate them into phase diagrams. The spherical radius and the degree of preferential interactions can obviously induce the formation of a cylindrical morphology. Theoretical results correspond to an amount of recent experimental observations to a high degree and contribute to synthesising functional materials.

In this work, the interactions between bottlebrush polymers and phospholipid membranes were investigated using dissipative particle dynamics simulations. The weak and strong adsorption phenomena between the polymers and membranes were examined by calculating the system parameters. A spring model was introduced to explain the variances in the shape factors and the radius of gyration of the bottlebrush polymers, as well as the order parameters of the phospholipid membrane in the pulling processes. This work provides further understanding for the application of bottlebrush polymers in biological processes.