This paper presents a comparative study on chitosan degradation in organic acid solutions according to their different dissociation characteristics. More precisely, the aim of the study was to determine the kinetics of the degradation process depending on the different acid dissociation constants (pKa values). The scientists involved in chitosan to date have focused mainly on acetic acid solutions. Solutions of lactic, acetic, malic, and formic acids in concentrations of 3% wt. were used in this research. The progress of degradation was determined based on the intrinsic viscosity measurement, GPC/SEC chromatographic analysis, and their correlation. Changes in the viscosity parameters were performed at a temperature of 20 °C ± 1 °C and a timeframe of up to 168 h (7 days). The chemical structure and DDA of the initial chitosan were analyzed using 1H-NMR spectroscopy analysis. The results of this study can be considered of high importance for the purpose of electrospinning, production of micro- and nano-capsules for drug delivery, and other types of processing. Understanding the influence of the dissociation constant of the solvent on the kinetics of chitosan degradation will allow the selection of an appropriate medium, ensuring an effective and stable spinning process, in which the occurrence of polymer degradation is unfavorable.

Chitosan is an environmentally friendly agent that is used to achieve the antimicrobial properties of textiles. Nowadays, the binding of chitosan to the textiles has been thoroughly researched due to the increasing demands on the stability of achieved properties during the textile care processes. Most crosslinking agents for chitosan are not safe for humans or environment, such as glutaric aldehyde (GA) and formaldehyde derivatives. Eco-friendly polycarboxyilic acids (PCAs) are usually used in after-treatment. In this work, chitosan powder was dissolved in citric acid with sodium hydrophosphite (SHP) as a catalyst. Standard cotton (CO) and polyester/cotton (PES/CO) fabrics were pretreated in 20% NaOH, similar to mercerization, in order to open the structure of the cotton fibers and hydrolyze polyester fibers, continued by finishing in the gelatin chitosan bath. Afterwards, the hot rinsing process, followed by drying and curing, closed the achieved structure. The main objective was to achieve durable antimicrobial properties to multiple maintenance cycles CO and PES/CO fabric in order to apply it in a hospital environment. The characterization of fabrics was performed after treatment, first and fifth washing cycles according ISO 6330:2012 by field emission scanning electron microscopy (FE-SEM), Fourier transform infrared spectroscopy (FTIR-ATR), electrokinetic analysis (EKA), by the determination of tensile properties and mechanical damage (wear), and the antimicrobial activity. The application of 20% NaOH led to the swelling and mercerization of cotton cellulose, and hydrolysis of polyester, resulting in better mechanical properties. It has been confirmed that the chitosan particles were well implemented into the cotton fiber and onto to the polyester component of PES/CO blend. The presence of chitosan was confirmed after five washing cycles, but in lower quantity. However, achieved antimicrobial activity is persistent.

Chitosan acquires bacteriostatic properties via protonation of its amino groups. However, much of the literature assumes that chitosan itself inhibits the growth of bacteria. This article presents a comparative study of chitosan nonwovens modified with various acids, including acetic, propionic, butyric, and valeric organic acids, as well as hydrochloric acid. The aim was to determine which acid salts influence the antibacterial and antifungal activity of chitosan-based materials. Two methods were used to modify (formation of ammonium salts) the chitosan nonwovens: First, acid vapors (gassing process) were used to find which salt of chitosan had the best antibacterial properties. Based on the results, the most effective acid was prepared in a solution in ethanol. The influence of the acid concentration in ethanol, the time of treatment of chitosan materials with acid solution, and the rinsing process of modified nonwovens on the antimicrobial activity of the modified materials was investigated. The modified materials were subjected to microbiological tests. Each of the modified materials was placed in bacterial inoculum. The cultures were tested on agar to observe their microbial activity. Toxicity to human red blood cells was also investigated. A reduction in the number of bacterial cells was observed for the S. aureus strain with chitosan salt modified with 10% acetic acid in ethanol. The antibacterial activity of the chitosan salts increased with the percentage of acid salts formed on the surface of the solid material (decreasing numbers of bacterial colonies or no growth). No reduction in growth was observed for the E. coli strain. The chitosan samples were either inactive or completely eliminated the bacterial cells. Antimicrobial activity was observed for chitosan salts with hydrochloric acid and acetic acid. Finally, ¹H-NMR spectroscopy and FTIR spectroscopy were used to confirm the incorporation of the acid groups to the amino groups of chitosan.

Active dressings based on natural polymers are becoming increasingly popular on the market. One of such polymers is alginate, which is characterized by biodegradability, resorbability, has no carcinogenic properties, does not have allergenic or hemostatic properties, and has a confirmed lack of toxicity. However, this polymer does not show biocidal and biostatic properties, therefore the purpose of this research was to select the appropriate conditions for the production of calcium alginate fibers modified with nano titanium dioxide and nano zinc oxide. It was assumed that the presence of nano metal oxide fillers will give antibacterial properties to formed fibers, which were used to form nonwovens. The following article presents a comparative analysis of nonwovens made of alginate fibers, without nano additives, with nonwovens made of alginate fibers containing in their structure 7% titanium dioxide and nonwovens made of alginate fibers containing 2% ZnO. The selection of the nano additive content was determined by the spinning ability of the developed polymer solutions. Based on the results contained in the article, it was found that the introduction of modifiers in the structure of fibers increases the diameter of the fiber pores, which improves the sorption and retention properties of the obtained fibers, and also gives differentiated antibacterial properties to the obtained nonwovens depending on the type of nano additive used. Greater activity against Escherichia coli, Staphylococcus aureus strains and Aspergillus Niger molds was shown in nonwovens made of 2% ZnO modified fibers compared to nonwovens made from TiO₂ modified fibers.