The deposition of a thin (several tens of microns) protective coating in atmospheric conditions is a challenging task for surface engineering. The structural features and tribological properties of a particle-reinforced metal matrix composite coating synthesized on middle-carbon steel by air pulse-plasma treatments were studied in the present work. The 24–31 µm thick coating of “24 vol.% (TiC + WC)/Hardened steel matrix” was produced by 10 plasma pulses generated by an electro-thermal axial plasma accelerator equipped with a consumable cathode of novel design (low-carbon steel tube filled with “TiC/WC + Epoxy resin” mixture). The study included optical microscopy (OM), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD, microhardness measurements, and dry “Ball-on-Plate” testing. The carbides were directly plasma-transferred to the substrate (steel of AISI 4145H grade) from the cathode without substantial melting. The hard (500–1044 HV) coating matrix consisted of 57 vol.% austenite (1.43 wt.% C) and 43 vol.% plate martensite was formed via carbon enrichment of steel from plasma flow. Additionally, a minor amount of oxide phases (TiO₂, WO₂, WO₃) were dispersed in the matrix. As compared to substrate, the coating had a lower coefficient of friction; its volumetric wear was decreased by 4.4 times when sliding against hardened steel ball and by 16 times when sliding against SiC ball.

In the present work, we have used unconventional short-term secondary recrystallization heat treatment employing extraordinary high heating rate to develop coarse-grained microstructure with enhanced intensity of rotating cube texture {100} in semi-finish vacuum degassed non-oriented electrical steels. The soft magnetic properties were improved through the increase of grains size with favourable cube crystallographic orientation. The appropriate final textural state of the treated experimental steels was achieved by strain-induced grain boundary migration mechanism, activated by gradient of accumulated stored deformation energy between neighbouring grains after the application of soft cold work, combined with steep temperature gradient during subsequent heat treatment under dynamic heating conditions. The materials in our experimentally prepared material states were mounted on the stator and rotor segments of electrical motors and examined for their efficiency in real operational conditions. Moreover, conventionally long-term heat treated materials, prepared in industrial conditions, were also tested for reference. The results show that the electrical motor containing the segments treated by our innovative approach, exhibits more than 1.2% higher efficiency, compared to the motor containing conventionally heat treated materials. The obtained efficiency enhancement can be directly related to the improved microstructural and textural characteristics of our unconventionally heat treated materials, specifically the homogenous coarse grained microstructure and the high intensity of cube and Goss crystallographic texture.

The paper presents research results on the quality of hardfacing layers made during the renovation of unheated mold surfaces designed for injection of aluminum alloys using the plasma transferred arc (PTA) technology. As mold material, the medium alloy steel X38CrMoV5-1 (H11) was used. For the formation of functional layers, three types of additives in the form of powder were applied: two types on an iron basis with the designation HSS 23 and HSS 30 and one type on a nickel basis with the designation DEW Nibasit 625-P. The hardfacing layers were made on a 120 × 350 × 50 mm plate in two layers on the plasma hardfacing machine PPC 250 R6. The quality of the layers was evaluated by means of nondestructive and destructive tests. The surface integrity of the layers was assessed using visual and capillary tests. The samples passed these tests. The impact of the parameters used and the mixing of the hardfacing metal with base material, as well as the structure analysis, were assessed by means of light and electron microscopy (SEM). The chemical composition of the elements was determined by energy-dispersive X-ray spectroscopy (EDX) analysis using a SEM microscope. The hardness of the individual layers was evaluated. Since, during operation, molds are subjected to significant wear due to friction, the friction coefficients for selected temperatures were determined by the equipment for the evaluation of tribology properties. Based on the experiments conducted, all three types of additives can be used for renovation. However, from a tribology perspective, the additive DEW Nibasit 625-P on a nickel alloy basis is recommended for renovation.

A high-carbon, high-silicon steel (1.21 wt% C, 2.56 wt% Mn, 1.59 wt% Si) was subjected to quenching from 900 and 1000 °C, resulting in microstructures containing 60 and 94% of retained austenite, respectively. Subsequent abrasive wear tests of quenched samples were performed using two-body abrasion and three-body abrasion testing machines. Investigations on worn surface and subsurface were carried out using SEM, XRD, and microhardness measurement. It was found that the highest microhardness of worn surface (about 1400 HV0.05) was achieved on samples quenched from 900 °C after three-body abrasion. Microhardness of samples after two-body abrasion was noticeably smaller. with a maximum of about 1200 HV0.05. This difference correlates with microstructure investigations along with XRD results. Three-body abrasion has produced a significantly deeper deformed layer; corresponding diffractograms show bigger values of the full width at half maximum parameter (FWHM) for both α and γ alone standing peaks. The obtained results are discussed in the light of possible differences in abrasive wear conditions and differing stability of retained austenite after quenching from different temperatures. It is shown that a structure of metastable austenite may be used as a detector for wear conditions, as the sensitivity of such austenite to phase transformation strongly depends on wear conditions, and even small changes in the latter lead to significant differences in the properties of the worn surface.

The present paper shows the impact of different laser scribing conditions on possible reduction of magnetic losses in grain oriented electrical steel sheets. The experimental Fe-3%Si steel was taken from industrial line after final box annealing. The surface of investigated steel was subjected to fiber laser processing using both pulse and continuous scribing regimes in order to generate residual thermal stresses inducing the magnetic domains structure refinement. The magnetic losses of experimental samples before and after individual laser scribing regimes were tested in AC magnetic field with 50Hz frequency and induction of 1.5T. The most significant magnetic losses reduction of 38% was obtained at optimized conditions of continuous laser scribing regime. A semi quantitative relationship has been found between the domain patterns and the used fiber laser processing.

TRIP-assisted C-Si-Mn steels are usually subjected to austempering with a preliminary intercritical annealing that is targeted at the multi-phase structure with 40–60 vol.% of proeutectoid ferrite. The kinetics and the mechanism of phase-structural transformations can be impacted due to the additional alloying of TRIP-assisted steel by the strong carbide forming elements, thus necessitating an alternative approach for the selection of intercritical annealing parameters. This issue is analyzed in the present work, which investigates the effect of the temperature of intercritical annealing on the “Structure/Properties” correlations in 0.2 wt.% C-Si-Mn-Nb steel additionally alloyed by 0.55 wt.% Cr, 0.20% Mo, and 0.11 wt.% V. The annealing temperature ranged from 770 °C to 950 °C, and austempering was performed at 350 °C for 20 min. It was observed that the addition of the (Cr, Mo, and V) complex significantly improved the steel hardenability. However, the annealing of steel at 770 °C (to gain 50 vol.% of proeutectoid ferrite) resulted in the precipitation of coarse cementite lamellas during bainite transformation, thus lowering the amount of retained austenite (RA) and decreasing the strength and ductility of the steel. At higher annealing temperatures, carbide-free bainite was formed, which presented a 2.5–3.5 times increase in the RA volume fraction and a 1.5 times increase in the RA carbon content. The optimal combination of the mechanical properties (UTS of 1040 MPa, TEL of 23%, V-notch impact toughness of 95 J/cm², PSE of 23.9 GPa·%) referred to annealing at a temperature close to the Ac₃ point, resulting in a structure with 5 vol.% ferrite and 9 vol.% RA (the residue was carbide-free bainite). This structure presented an extended manifestation of the TRIP effect with an enhanced strain hardening rate due to strain-induced martensite transformation. The impact of the alloying elements on the carbon activity in austenite served as the basis for the analysis of structure formation.