This study compares the characteristics and low-temperature curing properties of pastes prepared from silver (Ag) powders synthesized by either wet powder (WP) or dry powder (DP) processing. The WP synthesis of electrode particles has the advantage of controlling the average particle size and particle size distribution but the disadvantage of producing low-purity, crystalline particles because they are synthesized through chemical reduction at less than 100 °C. Conversely, the DP synthesis of electrode particles has the advantage of producing pure, highly crystalline particles (due to synthesis at high temperatures) but the disadvantage of a high processing cost. WP and DP were used to manufacture pastes for low-temperature curing, and the physical properties of the pastes and the electrode characteristics after low-temperature curing were compared between powder types. Shear stress as a function of the shear rate shows that the WP paste is a plastic fluid, whereas the DP paste is a pseudoplastic fluid, closer to a Newtonian fluid. Screen printing the Ag pastes and curing for 30 min at 130 °C produces a nonconductive WP paste, whereas it produces a DP paste with a conductivity of 61 mΩ/sq, indicating that the highly crystalline DP paste is advantageous for low-temperature curing.

This study presents the development of a highly robust, pressureless, and void-free silver sinter-bonding technology for power semiconductor packaging. A bimodal silver paste containing silver nanoparticles and sub-micron particles was used, with polymethyl methacrylate (PMMA) as an additive to provide additional thermal energy during sintering. This enabled rapid sintering and the formation of a dense, void-free bonding joint. The effects of sintering temperature and PMMA content on shear strength and microstructure were systematically investigated. The results showed that the shear strength increased with rising sintering temperatures, achieving a maximum of 41 MPa at 300 °C, with minimal void formation due to enhanced particle necking facilitated by PMMA combustion. However, at 350 °C, the shear strength decreased to 35 MPa due to cracks and voids at the copper substrate–copper oxide interface caused by thermal expansion mismatch. The optimal PMMA content was found to be 5 wt.%, balancing sufficient thermal energy and void reduction. This pressureless sintering technology demonstrates significant potential for high-reliability applications in power semiconductor modules operating under high-temperature and high-stress conditions.

This study presents the development of a modified polyimide (MPI) with low dielectric properties and low-temperature curing capability for high-frequency flexible printed circuit boards (FPCBs). MPI was cured using dicumyl peroxide (DCP) at 80–140 °C through a radical process optimized via DSC analysis, while Fourier-transform infrared (FT-IR) confirmed the elimination of C=C bonds and the formation of imide structures. The MPI film exhibited low dielectric constants (D_k) of 1.759 at 20 GHz and 1.734 at 28 GHz, with ultra-low dissipation factors (D_f) of 0.00165 and 0.00157. High-frequency S-parameter evaluations showed an excellent performance, with S11 of −32.92 dB and S21 of approximately −1 dB. Mechanical reliability tests demonstrated a strong peel strength of 0.8–1.2 kgf/mm (IPC TM-650 2.4.8 standard) and stable electrical resistance during bending to ~6 mm radius, with full recovery after severe deformation. These results highlight MPI’s potential as a high-performance dielectric material for next-generation FPCBs, combining superior electrical performance, mechanical flexibility, and compatibility with low-temperature processing.