Raman spectroscopy of natural bones and hydroxyapatites is described. In addition, how Raman spectroscopy has proved crucial in providing baseline data for the modification of synthetic apatite powders that are routinely used now as bone replacement materials is explained. It is important to understand the chemical structural properties of natural bone. Bone consists of two primary components: an inorganic or mineral phase, which is mainly a carbonated form of a nanoscale crystalline calcium phosphate, closely resembling hydroxyapatite, and an organic phase, which is composed largely of type I collagen fibers. Other constituents of bone tissue include water and organic molecules such as glycosaminoglycans, glycoproteins, lipids, and peptides. Ions such as sodium, magnesium, fluoride, and citrate are also present, as well as hydrogenophosphate. Hence, the mineral phase in bone may be characterized essentially as nonstoichiometric substituted apatite. Such a distinction is important in the development of synthetic calcium phosphates for application as skeletal implants. An understanding of bone function and its interfacial relationship to an implant clearly depends on the associated structure and composition. Therefore, it is essential to fully understand the chemical composition of bone, and Raman spectroscopy is an excellent technique for such an analysis.

Photoactive NiO electrodes for cathodic dye-sensitised solar cells (p-DSCs) have been prepared with thicknesses ranging between 0.4 and 3.0 μm by spray-depositing pre-formed NiO nanoparticles on fluorine-doped tin oxide (FTO) coated glass substrates. The larger thicknesses were obtained in sequential sintering steps using a conventional furnace (CS) and a newly developed rapid discharge sintering (RDS) method. The latter procedure is employed for the first time for the preparation of p-DSCs. In particular, RDS represents a scalable procedure that is based on microwave-assisted plasma formation that allows the production in series of mesoporous NiO electrodes with large surface areas for p-type cell photocathodes. RDS possesses the unique feature of transmitting heat from the bulk of the system towards its outer interfaces with controlled confinement of the heating zone. The use of RDS results in a drastic reduction of processing times with respect to other deposition methods that involve heating/calcination steps with associated reduced costs in terms of energy. P1-dye sensitized NiO electrodes obtained via the RDS procedure have been tested in DSC devices and their performances have been analysed and compared with those of cathodic DSCs derived from CS-deposited samples. The largest conversion efficiencies (0.12%) and incident photon-to-current conversion efficiencies, IPCEs (50%), were obtained with sintered NiO electrodes having thicknesses of ∼1.5–2.0 μm. In all the devices, the photogenerated holes in NiO live significantly longer (τ_h ∼ 1 s) than have previously been reported for P1-sensitized NiO photocathodes. In addition, P1-sensitised sintered electrodes give rise to relatively high photovoltages (up to 135 mV) when the triiodide–iodide redox couple is used.

In this study, wind data of eleven years (2002–2012) has been used to determine wind characteristics of Saudi Arabian city Jeddah. These characteristics include the daily, monthly and annual wind speed, wind probability density distribution, shape ( k) and scale ( c) parameters at 10 m height. The analysis revealed that yearly values of k ranged from 1.398 to 1.763 with a mean value of 1.590 and values of scale parameter c varied from 3.146 to 4.329 with mean value of 3.95. Furthermore, the results showed that maximum and minimum wind power potential was observed in the month of March and February, respectively. The wind was found to be blowing predominantly from south east direction. It was found that wind potential of the region can be used for small scale off-grid wind applications.