In order to examine the geometric characteristics of BOF (blast oxygen furnace) slag coarse aggregate, the aggregate image measurement system (AIMS) was used to analyze the sphericity, gradient angularity and micro texture. Both volumetric and mechanical properties were studied to evaluate the influence of geometric characteristics of BOF slag coarse aggregate on asphalt concrete. The experimental results show that the BOF slag coarse aggregate has the characteristics of high sphericity, good angular performance and rough surface texture. The geometric characteristics of BOF slag has obvious influence on the volume performance of asphalt concrete. the higher sphericity of BOF slag causes an increase of the air voids of asphalt mixture. BOF slag coarse aggregate can effectively improve the road performances of asphalt concrete. BOF slag’s higher sphericity and angularity improve the moisture damage resistance and rutting resistance of asphalt concrete. Results indicate that better angularity can slightly enhance the moisture resistance property of asphalt concrete, but excessively high angularity of BOF slag coarse aggregates reduces the anti-rutting properties of asphalt mixture.

Using rejuvenator to improve the asphalt pavement service state has become an increasing concern in recent years. This study mainly focuses on the diffusion analysis between rejuvenator and aged asphalt, and further rheological influences by addition of rejuvenators. First, two rejuvenators, oil rejuvenator (OR) and penetrative rejuvenator (PR), were prepared in the laboratory. Afterward, the diffused performance of rejuvenators was investigated by viscosity, contact angle, and three self-designed feasible test indexes, which were sinking time test, softening rate test, and gravitational collapsing test. Beside the comparison in physical properties tests of aged and rejuvenated asphalt, their rheological performances were also evaluated by dynamic shear rheometer (DSR) and bending beam rheometer (BBR) respectively. The results indicated that three proposed indexes can comparatively analyze the diffusion rate of different rejuvenators on aged asphalt effectively. Furthermore, all adopted test indexes signaled that PR has a faster diffusion rate and better penetrative efficiency. Comparatively, exceeding rejuvenator dosage would increase the rutting possibility. Nevertheless, 2.5 wt% addition dosage for both OR and PR into aged asphalt can promote appropriate improvement in physical properties and crack resistance. The study would supply a significant reference for penetrative rejuvenator preparation and its diffusing evaluation.

Due to the difference of cooling and treatment processes (rolling method, hot braised method, layer pouring method), basic oxygen furnace (BOF) steel slag can be mainly classified as roller steel slag (RSS), hot braised steel slag (HBSS) and layer pouring steel slag (LPSS). Treatment difference directly results in the performance variations of different BOF steel slag and corresponding asphalt mixtures. The primary purpose of this research was to examine the effects of different cooling and treatment processes on the morphological discrepancy of different BOF steel slag. Also, the road performances of corresponding asphalt mixtures, and mechanism between steel slag performance and road performance were studied. The results show that LPSS owns the largest variability of angular index and texture index, and RSS has the most balanced morphological parameters. The structure of RSS asphalt mixture is advantageous for improving the ability of the asphalt mixture to resist the deformation and enhancing the stability of structure. Higher content of CaO and lower content of SiO₂ make the acid-base reaction of RSS asphalt mixture most intense, which contribute to the best road performance of it.

The fillers of ordinary and pyrolytic basic oxygen furnace (BOF) slag were selected to investigate the properties of their asphalt mastic. XRF (X-Ray Fluorescence) was used to analyze chemical composition of fillers. Meanwhile, SEM (Scanning Electron Microscope) and AIMS (Aggregate Image Measurement System) were utilized to explore meso-morphology, angularity and sphericity. Penetration, softening point and viscosity of asphalt mastic were discussed, while the rheological properties of asphalt mastic were studied by means of DSR (dynamic shear rheometer) and BBR (bending beam rheometer) tests. The experimental results show that chemical composition of different types of BOF slag is similar. The grinding energy consumption of pyrolytic BOF slag is higher than that of limestone and ordinary BOF slag. It is not recommended that pyrolytic BOF slag filler is produced by grinding process. The micro-texture structure of ordinary BOF slag filler is more abundant and their angularity index is about 15% higher than that of limestone filler. The stiffness modulus and rutting factor of asphalt mastic with ordinary BOF slag filler is higher than that of limestone filler. Meanwhile the incorporation of BOF slag filler will further reduce the low-temperature flow performance of asphalt mastic. The effect of pyrolytic BOF slag filler on the performance of asphalt mastic is less than that of ordinary BOF slag. Ordinary BOF slag filler can effectively improve high temperature anti-rutting stability of asphalt mixture. Ordinary BOF slag has a useful application prospect as filler in asphalt mixture.

As an industrial waste, basic oxygen furnace (BOF) slag is an ideal substitute for natural rubble and sand. However, its potential instability of volume restricts the application of the BOF slag in engineering. This study aims at investigating the volume stability and mechanical properties of BOF slag and its application as an aggregate in cement-stabilized macadam. As part of this research, the physicochemical properties, especially the volume stability, of two types of BOF slags and andesite were first studied. Then, mechanical properties, volume stability, and an environment analysis are used to evaluate the application of pyrolytic BOF slag in cement-stabilized macadam. The experimental results show that different types of BOF slags have similar thermal expansion coefficients, which are higher than andesite. The free CaO content of pyrolytic BOF slag is much lower than that of ordinary BOF slag and the volume expansion of pyrolytic BOF slag is less than 0.5%. The unconfined compressive strength (UCS) of cement-stabilized macadam using pyrolytic BOF slag is about 30% higher than that of andesite. Although the water loss rate is higher than a natural aggregate, dry shrinkage of pyrolytic BOF slag cement-stabilized macadam is about 30–50% less than that of a natural aggregate. Meanwhile, its shrinking speed is also slower than that of a natural aggregate. The micro-expansion properties of pyrolytic BOF slag could effectively partially offset the shrinkage characteristics of cement-stabilized macadam. Finally, the Toxicity Characteristic Leaching Procedure (TCLP) test results indicated that the metal leaching concentration meets the Chinese environmental standards. This study provides a direction for the large-scale and effective sustainable application of pyrolytic BOF slag.