Using rejuvenator to improve the asphalt pavement service state has become an increasing concern in recent years. This study mainly focuses on the diffusion analysis between rejuvenator and aged asphalt, and further rheological influences by addition of rejuvenators. First, two rejuvenators, oil rejuvenator (OR) and penetrative rejuvenator (PR), were prepared in the laboratory. Afterward, the diffused performance of rejuvenators was investigated by viscosity, contact angle, and three self-designed feasible test indexes, which were sinking time test, softening rate test, and gravitational collapsing test. Beside the comparison in physical properties tests of aged and rejuvenated asphalt, their rheological performances were also evaluated by dynamic shear rheometer (DSR) and bending beam rheometer (BBR) respectively. The results indicated that three proposed indexes can comparatively analyze the diffusion rate of different rejuvenators on aged asphalt effectively. Furthermore, all adopted test indexes signaled that PR has a faster diffusion rate and better penetrative efficiency. Comparatively, exceeding rejuvenator dosage would increase the rutting possibility. Nevertheless, 2.5 wt% addition dosage for both OR and PR into aged asphalt can promote appropriate improvement in physical properties and crack resistance. The study would supply a significant reference for penetrative rejuvenator preparation and its diffusing evaluation.

In this research, the durability of skid resistance during the ice melting process with temperature increasing from −5 °C to 10 °C was characterized by means of a British Pendulum Skid Tester. Four types of pavement surfaces were prepared and tested. The difference between two antiskid layers prepared with bitumen emulsion was the aggregate. The detailed angularity and form 2D index of fine aggregates used for antiskid surfaces, characterized by means of the Aggregate Image Measure System (AIMS) with micro image analysis methods, were then correlated with British Pendulum Number (BPN) values. Results indicate that skid resistance has the lowest value during the ice-melting process. The investigated antiskid layers can increase the surface friction during icy seasons. In icy conditions, the skid resistance behavior first worsens until reaches the lowest value, and then increases gradually with increasing temperature. Results from ice-melting conditions on four investigated pavement surfaces give the same temperature range where there will be lowest skid resistance. That temperature range is from 3 °C to 5 °C. A thicker ice layer will result in a lower skid resistance property and smaller “lowest BPN”.