The design of zirconia-based scaffolds using conventional techniques for bone-regeneration applications has been studied extensively. Similar to dental applications, the use of three-dimensional (3D) zirconia-based ceramics for bone tissue engineering (BTE) has recently attracted considerable attention because of their high mechanical strength and biocompatibility. However, techniques to fabricate zirconia-based scaffolds for bone regeneration are in a stage of infancy. Hence, the biological activities of zirconia-based ceramics for bone-regeneration applications have not been fully investigated, in contrast to the well-established calcium phosphate-based ceramics for bone-regeneration applications. This paper outlines recent research developments and challenges concerning numerous three-dimensional (3D) zirconia-based scaffolds and reviews the associated fundamental fabrication techniques, key 3D fabrication developments and practical encounters to identify the optimal 3D fabrication technique for obtaining 3D zirconia-based scaffolds suitable for real-world applications. This review mainly summarized the articles that focused on in vitro and in vivo studies along with the fundamental mechanical characterizations on the 3D zirconia-based scaffolds.

In this study, we have analysed the effects of a silane coupling agent on the volume fraction of zirconia for digital light processing (DLP)-based additive manufacturing processes. Zirconia suspension was prepared by the incorporation of silane-modified zirconia particles (experimental group) or untreated zirconia particles (control group). Furthermore, the control and experimental group were subdivided into three groups based on the volume fraction (52, 54, and 56 vol%) of zirconia particles. The disk-shaped zirconia samples were 3D (three-dimensional) printed using the DLP technique and their physical and mechanical properties were evaluated. The addition of a silane coupling agent to the zirconia samples was found to have influence of about 6% on the hardness and biaxial flexural strength. Moreover, the decrease in minute air gaps inside the zirconia layers significantly increased the material density (visualized from the microstructure analysis). Thus, from this study, it was established that the silane-modified zirconia particles had a positive effect on the physical properties of the zirconia parts.

Partially-stabilized zirconia is used in ceramic crowns due to its excellent mechanical properties and bio-inertness but does not match the natural color and translucency of tooth enamel. To reduce scattering of light and improve translucency, the grain size of zirconia ceramics should be less than the wavelength of visible light (0.4–0.7 μm), and porosity should be eliminated. The aim of the present work was to study the effect of two-step sintering of a commercial powder (Zpex Smile, Tosoh Corp., Tokyo, Japan) on the grain size and translucency of zirconia for use in ceramic crowns. Samples were sintered at a first step temperature (T₁) of 1300, 1375 and 1400 °C for 5 min, followed by a decrease to the second step temperature (T₂) and holding at T₂ for 5–20 h. Samples were also conventionally sintered at 1450 °C for 2 h for comparison. Two-step sintered samples with an almost equal density, smaller grain size and narrower grain size distribution compared to conventionally sintered samples could be sintered. However, the translucency of two-step sintered samples had lower values compared to conventionally sintered samples. This is due to the slightly higher porosity in the two-step sintered samples. Density and translucency of both conventionally and two-step sintered samples could be increased further by using a ball milled powder.

We evaluated the effect of electron beam (E-beam) sterilization (25 kGy, ISO 11137) on the degradation of β-tricalcium phosphate/polycaprolactone (β-TCP/PCL) composite filaments of various ratios (0:100, 20:80, 40:60, and 60:40 TCP:PCL by mass) in a rat subcutaneous model for 24 weeks. Volumes of the samples before implantation and after explantation were measured using micro-computed tomography (micro-CT). The filament volume changes before sacrifice were also measured using a live micro-CT. In our micro-CT analyses, there was no significant difference in volume change between the E-beam treated groups and non-E-beam treated groups of the same β-TCP to PCL ratios, except for the 0% β-TCP group. However, the average volume reduction differences between the E-beam and non-E-beam groups in the same-ratio samples were 0.76% (0% TCP), 3.30% (20% TCP), 4.65% (40% TCP), and 3.67% (60% TCP). The E-beam samples generally had more volume reduction in all experimental groups. Therefore, E-beam treatment may accelerate degradation. In our live micro-CT analyses, most volume reduction arose in the first four weeks after implantation and slowed between 4 and 20 weeks in all groups. E-beam groups showed greater volume reduction at every time point, which is consistent with the results by micro-CT analysis. Histology results suggest the biocompatibility of TCP/PCL composite filaments.

This study evaluated the effect of UV absorbers on the dimensional accuracy of zirconia specimens fabricated by additive manufacturing using a digital light process. Zirconia suspension for additive manufacturing was prepared by setting the volume fractions (0, 0.005, 0.05, and 0.1%) of various UV absorbers. The effect of UV absorber content was evaluated through curing thickness, geometric overgrowth model design, linear deviation, and microstructure evaluation before and after sintering. Statistical analysis was performed by Kruskal–Wallis H and post-tested by the Bonferroni correction method. There was no significant difference in the cure depth according to the presence or absence of the UV absorber, the difference in geometric overgrowth was from 2.1 to 12.5%, and the overgrowth significantly decreased as the amount of added UV absorber increased. This result may contribute to improved precision of 3D multilayer ceramic products.

Recently, a novel electrochemical regulation associated with a deposition/dissolution reaction on an electrode surface has been proven to show superiority in large-scale energy storage systems (ESSs). Hence, in the search for high-performance electrodes showcasing these novel regulations, we utilized a low-cost ZnO microsphere electrode to construct aqueous rechargeable batteries (ARBs) that supplied a harvestable and storable charge through electrochemical deposition/dissolution via a reversible manganese oxidation reaction (MOR)/manganese reduction reaction (MRR), respectively, induced by the inherent formation/dissolution of zinc basic sulfate in a mild aqueous electrolyte solution containing 2 M ZnSO₄ and 0.2 M MnSO₄.