High crystallinity leads to low hydrophilicity of fabric made of (poly(ethylene terephthalate)) fibers (PET) causing problems in finishing, washing, and dyeing processes. To improve these properties, the surface of PET fibers is usually modified by hydrolysis. Alkaline hydrolysis is a conventional process usually performed at a temperature higher than 100 °C for more than 1 h. However, the use of strong alkali and high processing temperatures (>100 °C) can lead to fabric damage and a negative impact on the environment. Therefore, in this paper, the possibility of hydrolysis of the PET fibers in the fabric in a sustainable, energy-efficient process was researched. The influence of low temperature (60–100 °C) and an accelerator (a cationic surfactant HDTMAC) to PET alkaline hydrolysis was studied through weight loss, the loss in breaking force, and fiber morphology. The kinetics of PET dissolution in 1.5 mol cm⁻³ NaOH at low temperature with and without the addition of HDTMAC was determined and the activation energy was calculated according to the theoretical model. It has been confirmed that PET hydrolysis can be carried out in 1.5 mol cm⁻³ NaOH with the addition of HDTMAC as an accelerator at 80 °C for 10 min. This process is more economically and energetically acceptable than the conventional process, and is therefore more sustainable.

The use of synthesized natural starches for the sizing process in fabric production is primarily an environmental contribution. Synthesized corn starch is environmentally friendly and productive, showing good results in cotton yarn sizing. Acrylamide (AA) and 2-hydroxyethyl methacrylate (HEMA) were applied for the grafting process of corn starch, and the initiators azobisisobutyronitrile (AIBN), potassium persulfate (KPS), and benzoyl peroxide (BP) were chosen to form the grafted monomers more effectively. The application of synthesized corn starch has been confirmed, especially with the AIBIN initiator in the grafting process of HEMA onto starch. The FTIR analysis confirmed that new and efficient products for sizing cotton yarns based on natural raw material (corn) were developed. The research showed that the synthesized corn starch improved physical-mechanical yarn properties and abrasion resistance and reduced yarn surface hairiness. Ultrasonic desizing of yarn and the use of a lower size concentration led to better results than desizing by washing, and the Tegewa numbers confirmed that the desizing process was successful.

The objective of this research was to verify the feasibility of the use of newly synthesized biopolymer materials for sizing cotton yarns based on the basic principles of chemical modification. Research included acid hydrolysis of potato starch up to controlled molar masses together with graft-polymerization and methacrylic acid onto hydrolyzed starch to improve hydrophilicity and solubility, to increase the capability of film forming, to increase adhesive potential and to avoid retrogradation phenomena. Research objectives were primarily focused on finding an appropriate, environmentally-friendly and productive sizing agent for cotton yarns via the analysis and systematization of a large number of synthesis methods in conjunction with the characterization and properties of graft-copolymers. The research results showed that potassium persulfate initiator was most efficient in grafting of methacrylic acid onto hydrolyzed starch, while azobisisobutyronitrile (AIBIN) initiator was most efficient in grafting of acrylic acid (AC). FTIR analysis confirmed that new and efficient products for sizing cotton yarns from synthetized potato starch were obtained. Research on rheological properties of copolymers shows a higher viscosity of grafted products indicating the good stability of potential starches. Ecological improvements have been established through high desizing degree as well as improvements in physical-mechanical properties of yarn, abrasion resistance and decrease in yarn surface hairiness were noticed. The use of new derivatives of potato starch, especially of hydrolyzed starch grafted with methacrylic acid (MAA), potassium persulfate (KPS) as initiator, was confirmed. Anova statistical analysis determined the influence of the entire sizing process on individual yarn parameters.

In this paper, the synthesis, characterization and application of a copolymer as a sizing agent obtained by the grafting of methacrylic acid on hydrolyzed potato starch were investigated. Starch hydrolysis was performed in order to reduce the average molar mass (i.e. the size of the macromolecules). Grafting of methacrylic acid on hydrolyzed potato starch was performed to obtain a product that can be effective in textile processing, for example, for sizing yarn. The grafting of the monomer has been confirmed by Fourier transform infrared spectroscopy spectra of hydrolyzed and grafted potato starch. The distribution of molar masses was determined chromatographically. The results obtained by sizing of cotton yarn with the new starch agent confirmed its higher breaking strength, elongation, abrasion resistance, reduced hairiness, better evenness, etc. Grafted hydrolyzed potato starch (almost identical to the commercial medium) exhibits better performance as a potential agent for sizing cotton yarn than ungrafted hydrolyzed starch.

The objective of this work was to determine the influence of washing and sterilization under real hospital conditions on properties of microbial barrier offered by polyurethane coated fabrics used in surgery and for wrapping sterile items. Emphasis was put on the change of surface polyurethane coating by using FTIR analysis. The permeability and durability of the microbial barrier were determined after 0, 10, and 20 washing and sterilization procedures according to previously developed methods. Bacterial endospores of the apathogenic species of the genus Bacillus Geobacillus stearothermophilus and Bacillus atrophaeus were used. Mechanical damage to medical textiles in the washing and sterilization process was determined according to standard HRN EN ISO 13914-1:2008 and associated with changes in physical and mechanical properties. Chemical changes of PU coatings were determined using FTIR analysis. The results showed an exceptionally efficient microbial barrier and its durability in all samples after 0, 10 and 20 washing and sterilization procedures and for a period of one, two and three months.

An adsorption process using cheap adsorbents could be described as a simple, selective and low cost alternative for the treatment of colored waste water compared to conventional physical and chemical processes. In this study the use of a natural waste adsorbent - ash was investigated for the removal of a textile vat dye Ostanthren Blue GCD remaining after the dyeing of cotton textile. The ash obtained as a waste material during the burning of brown coal in the heating station of Leskovac (Serbia) was used for the treatment of waste waters from the textile industry, i.e., waste water after the dyeing process. The effect of ash quantity, initial dye concentration, pH and agitation time on adsorption was studied. The Langmuir model was used to describe the adsorption isotherm. Based on the analytical expression of the Langmuir model, the adsorption constants, such as adsorption capacity and adsorption energy, were found. Pseudo first and second order kinetic models were studied to evaluate the kinetic data.