The present study offers an alternative method for green synthesis of the formation of two types of nanoparticles (NPs). These NPs, titanium oxide and silver NPs (TiO₂ and Ag NPs, respectively), were obtained from the amalgamation of intracellular extract of a wild mushroom, Fomes fomentarius, with aqueous solutions of titanium isopropoxide and silver nitrate, respectively. F. fomentarius was identified phenotypically and by 18S ribosomal RNA gene sequencing (Gene accession no: MK635351). The biosynthesis of TiO₂ and Ag NPs was studied and characterized by X-ray diffraction (XRD), diffuse reflectance UV-Visible spectroscopy (DR-UV), fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM) and transmission electron microscope (TEM). Success was achieved in obtaining NPs of differing sizes and shapes. The antibacterial and anticancer activity of the NPs was significant with morphological damage being caused by both, although Ag NPs (10–20 nm) were found to have profound effects on bacterial and cancer cells in comparison to TiO₂ NPs (100–120 nm). These metal NPs, synthesized using wild mushrooms, hold a great potential in biomedicinedue to an effective enzyme combination, which permits them to modify different chemical compounds to less toxic forms, which is required for ecofriendly and safe biomaterials.

Nanoformulation involving biocompatible MOFs and magnetic nanocarriers is an emerging multifunctional platform for drug delivery and tumor imaging in targeted cancer therapeutics. In this study, a nanocomposite has been developed comprising Fe/SBA-16 and ZIF-8 (Fe/S-16/ZIF-8) through ultrasonication. The drug delivery of cisplatin was studied using an automated diffusion cell system equipped with a flow type Franz cell. The anticancer activity of Fe/S-16/ZIF-8 was studied in vitro in MCF-7, HeLa cells and Human Foreskin Fibroblast (HFF-1) cells. XRD and d-spacing measurements of Fe/S-16/ZIF-8 using TEM revealed the presence of cubic-structured Fe₃O₄, γ-Fe₂O₄ (magnetite), and α-FeOOH (goethite) over an SBA-16/ZIF-8 nanocomposite. The composite showed a surface area of 365 m² g⁻¹, a pore size of 8.3 nm and a pore volume of 0.33 cm³ g⁻¹. VSM analysis of Fe/S-16/ZIF-8 showed that it possessed paramagnetic behavior with a saturated magnetization value of 2.39 emu g⁻¹. The Fe²⁺/Fe³⁺ coordination environment was characterized using diffuse reflectance spectroscopy. The cisplatin drug delivery study clearly showed the synergistic effects present in Fe/S-16/ZIF-8 with over 75% of cisplatin release as compared to that of Fe/S-16 and ZIF-8, which showed 56% and 7.5%, respectively. The morphology analysis of CP/Fe/SBA-16/ZIF-8 using TEM showed an effective transit of nanoparticles into MCF-7 cells. The lethal concentration (LC₅₀) of Fe/SBA-16/ZIF-8 for MCF-7 and HeLa cells is 0.119 mg mL⁻¹ and 0.028 mg mL⁻¹ at 24 h, respectively. For HFF-1 cells, the LC₅₀ is 0.016 mg mL⁻¹. The antibiofilm activity of Fe/SBA-16/ZIF-8 was investigated against biofilm-forming strains of drug resistant P. aeruginosa and MRSA by a microtiter tissue culture plate assay. Overall, nanosized ZIF-8 with a bioactive alkaloid imidazole inside the 3D cage type of SBA-16 pores is found to exhibit both anticancer and antibacterial properties. A Fe/S-16/ZIF-8 composite could be effectively used as a drug and drug delivery system against cancer and promote antibacterial activity.

The combination of magnetic nanoparticles with a porous silica is a composite that has attracted significant attention for potential multifunctional theranostic applications. In this study, 30 wt % CuFe₂O₄ was impregnated into a matrix of monodispersed spherical hydrophilic silica (HYPS) nanoparticles through a simple dry impregnation technique. The chemotherapy drug cisplatin was loaded through electrostatic equilibrium adsorption over 24 h in normal saline solution. The presence of cubic spinel CuFe₂O₄ on HYPS was confirmed through powder X-ray diffraction (PXRD), Fourier transform infrared spectroscopy (FTIR) and diffuse reflectance UV–vis spectroscopy (DR UV–vis) analysis. The HYPS particles showed a surface area of 170 m²/g, pore size of 8.3 nm and pore volume of 0.35 cm³/g. The cisplatin/CuFe₂O₄/HYPS nanoformulation showed the accumulation of copper ferrite nanoparticles on the surface and in the pores of HYPS with a surface area of 45 m²/g, pore size of 16 nm and pore volume of 0.18 cm³/g. Transmission electron microscopy (TEM) and energy dispersive X-ray (EDX) mapping analysis showed the presence of homogeneous silica particles with nanoclusters of copper ferrite distributed on the HYPS support. Vibrating sample magnetometry (VSM) analysis of CuFe₂O₄/HYPS showed paramagnetic behavior with a saturated magnetization value of 7.65 emu/g. DRS UV–vis analysis revealed the functionalization of cisplatin in tetrahedral and octahedral coordination in the CuFe₂O₄/HYPS composite. Compared to other supports such as mesocellular foam and silicalite, the release of cisplatin using the dialysis membrane technique was found to be superior when CuFe₂O₄/HYPS was applied as the support. An in vitro experiment was conducted to determine the potential of CuFe₂O₄/HYPS as an anticancer agent against the human breast cancer cell line MCF-7. The results show that the nanoparticle formulation can effectively target cancerous cells and could be an effective tumor imaging guide and drug delivery system.

Multifunctional nanomaterials can be used for dual applications: drug delivery as well as in bioimaging. In current study, we investigated potential use of silica based supports; 3D cage type SiSBA-16 (S-16), monodispersed hydrophilic spherical silica (HYPS) and mesocellular foam (MSU-F) for cisplatin (Cp) delivery. To obtain magnetic resonance characteristics, 10 wt% iron oxide was loaded through enforced adsorption technique. For pH stimuli responsive release of Cp, 10 wt%SPIONs/S-16 was functionalized with 3-(Aminopropyl)triethoxysilane (A) and poly acrylic acid (PAA) termed as 10 wt%SPIONs/S-16-A-Cp and 10 wt%SPIONs/S-16-APAA-Cp. By TEM analysis, the average diameter of the SPIONs was found to range between 10–60 nm. VSM analysis showed saturation magnetization over S-16, HYPS and MSU-F were in the following order: 10 wt%SPIONs/HYPS (4.08 emug⁻¹) > 10 wt%SPIONs /S-16 (2.39 emug⁻¹) > 10 wt%SPIONs/MSU-F (0.23 emug⁻¹). Cp release study using dialysis membrane in PBS solution over 10 wt%SPIONs/S-16 nanoformulations showed highest cumulative release (65%) than 10 wt%SPIONs/MSU-F-A-Cp (63%), 10 wt%SPIONs/HYPS-A-Cp (58%), and Cp-F127/S-16 (53%), respectively. 10 wt%SPIONs/S-16-A-Cp and 10 wt%SPIONs/S-16-APAA-Cp were evaluated for in vitro target anticancer efficiency in human cancer cell lines (colon cancer (HCT 116), cervical cancer (HeLa)) and normal cells (Human embryonic kidney cells (HEK293) using MTT and DAPI staining. 10 wt%SPIONs/S-16-A-Cp treated Hela and HCT116 cancerous cell lines showed significant control of cell growth, apoptotic activity and less cytotoxic effect as compared to Cp and 10 wt%SPIONs/S-16. Target specific Cp release in the cells shows that 10 wt%SPIONs/S-16-A-Cp can be easily upgraded for magnetic resonance imaging capability.

The engineering of multifunctional therapeutics in an integrated single platform is demonstrated using three-dimensional SBA-16 (S-16). 10 wt% iron oxide nanoparticles (Fe) were loaded into the cage type of cubic pores through enforced adsorption technique. Fe/S-16 is then functionalized with amine-based silane (A), polyacrylic acid (P) and cisplatin (Cp). The physicochemical textural analysis showed the formation of nano metal oxide distributions at pore walls of S-16 with magnetization of 2.39 emu/g. S-16 based nanoformulations showed high percentage of Cp adsorption (90%) and percentage cumulative release (60%). in vitro study of Fe/S-16-A-Cp showed high toxicity against breast cancer cell line MCF-7 and normal cell line Human foreskin fibroblast (HFF-1) compared to Fe/S-16 indicating cisplatin profusion inside the cells than free cisplatin. While skin fibroblast seems to be resistant to Fe/S-16-AP-Cp with very high LC₅₀ in compare to MCF-7. This indicates the unrelease of cisplatin in skin fibroblast after Fe/S-16-AP-Cp treatment due to effective encapsulation inside the cubic pores and core blockage due to pH-sensitive polyacrylic acid. Also, these treatments resulted in morphological changes in the cells such as DNA condensation and nuclear fragmentation.

Background: Platinum-based drugs are widely used in cancer therapy, but are known for toxic side effects and resistance. Combinational drug delivery represents an effective chemotherapeutic strategy, but often leads to an increased toxicity. Aim of this study is to test the co-delivery of cisplatin with natural antioxidants on hierarchial porous large surface area hexagonal nanocarriers for synergistic action.Results: A series of structured mesoporous materials were impregnated with magnetic spinel ferrite (30% CuFe₂O₄) and then coated with curcumin (25% wt/wt). Mesosilicalite and MCM-41 with high curcumin release abilities were functionalized with cisplatin (5% wt/wt) for synergistic effect of combinational drugs. The cytotoxic efficiency of our nanocomposites was tested on cell viability of MCF7 (human breast cancer), human cervical cancer (HeLa), colorectal cancer (HCT116), and HFF (human foreskin fibroblasts) cell lines using the MTT cell viability assay. At a concentration of 0.1 mg/ml, CuFe₂O₄/mesosilicalite/curcumin/cisplatin resulted in 89.53% reduction in viability in MCF7, 94.03% in HeLa, 64% in HCT116 and 87% in HFF; whereas, CuFe₂O₄/MCM-41/curcumin/cisplatin resulted in 76% reduction in viability in MCF7, 64.46% in HeLa, 64% in HCT116 and 24% in HFF. The EC₅₀for CuFe₂O₄/mesosilicalite/curcumin/cisplatin was 81.23 µg/ml in MCF7, 47.55 µg/ml in HeLa, 48.96 µg/ml in HCT116 and 76.83 µg/ml in HFF. The EC₅₀for CuFe₂O₄/MCM-41/curcumin/cisplatin was 72.51 µg/ml in MCF7, 58.6 µg/ml in HeLa, 62.58 µg/ml in HCT116 and 154.2 µg/ml in HFF. Furthermore, cells treated with both nanocomposites had a high number of cleaved Caspase 3-positive cells suggesting that the reduction in cell viability was triggered by activating the apoptotic signaling pathway.Conclusion: Our results show that CuFe₂O₄/MCM-41/curcumin/cisplatin is a better candidate for combinational drug therapy due to its lowest EC₅₀value and the wider difference in EC₅₀(a fold change) between cancerous and non-cancerous cell line.