The purpose of the work was to emphasize the main differences and similarities in the degradation mechanisms in the case of polymeric coatings compared with the bulk ones. Combined with the current background, this work reviews the properties of commonly utilized degradable polymers in drug delivery, the factors affecting degradation mechanism, testing methods while offering a retrospective on the evolution of the controlled release of biodegradable polymeric coatings. A literature survey on stability and degradation of different polymeric coatings, which were thoroughly evaluated by different techniques, e.g., polymer mass loss measurements, surface, structural and chemical analysis, was completed. Moreover, we analyzed some shortcomings of the degradation behavior of biopolymers in form of coatings and briefly proposed some solving directions to the main existing problems (e.g., improving measuring techniques resolution, elucidation of complete mathematical analysis of the different degradation mechanisms). Deep studies are still necessary on the dynamic changes which occur to biodegradable polymeric coatings which can help to envisage the future performance of synthesized films designed to be used as medical devices with application in drug delivery.

Tantalum oxynitride thin films have been deposited by reactive magnetron sputtering, using a fixed proportion reactive gas mixture (85% N₂ + 15% O₂). To produce the films, the partial pressure of the mixture in the working atmosphere was varied. The characteristics of the produced films were analyzed from three main perspectives and correspondent correlations: the study of the bonding states in the films, the efficiency of photo-degradation, and the antibacterial/antibiofilm capacity of the coatings against Salmonella. X-ray Photoelectron Spectroscopy results suggest that nitride and oxynitride features agree with a constant behavior relative to the tantalum chemistry. The coatings deposited with a higher reactive gas mixture partial pressure exhibit a significantly better antibiofilm capacity. Favorable antibacterial resistance was correlated with the presence of dominant oxynitride contributions. The photocatalytic ability of the deposited films was assessed by measuring the level of degradation of an aqueous solution containing methyl orange, with or without the addition of H₂O₂, under UV or VIS irradiation. Degradation efficiencies as high as 82% have been obtained, suggesting that tantalum oxynitride films, obtained in certain configurations, are promising materials for the photodegradation of organic pollutants (dyes).

Our study focused on the long-term degradation under simulated conditions of coatings based on different compositions of polycaprolactone-polyethylene glycol blends (PCL-blend-PEG), fabricated for titanium implants by a dip-coating technique. The degradation behavior of polymeric coatings was evaluated by polymer mass loss measurements of the PCL-blend-PEG during immersion in SBF up to 16 weeks and correlated with those yielded from electrochemical experiments. The results are thoroughly supported by extensive compositional and surface analyses (FTIR, GIXRD, SEM, and wettability investigations). We found that the degradation behavior of PCL-blend-PEG coatings is governed by the properties of the main polymer constituents: the PEG solubilizes fast, immediately after the immersion, while the PCL degrades slowly over the whole period of time. Furthermore, the results evidence that the alteration of blend coatings is strongly enhanced by the increase in PEG content. The biological assessment unveiled the beneficial influence of PCL-blend-PEG coatings for the adhesion and spreading of both human-derived mesenchymal stem cells and endothelial cells.