In the present study, pulsed laser post-processing was applied to improve the properties of the thermally sprayed NiCrCoFeCBSi/40 wt.% WC coatings. The powder mix was deposited onto a mild steel substrate by flame spray method and then the as-sprayed coatings were processed by Nd:YAG laser. The peak power density applied was between 4.00 × 10⁶ and 5.71 × 10⁶ W/cm², and the laser operating speed ranged between 100 and 400 mm/min, providing processing in a melting mode. Scanning electron microscopy, energy dispersive spectroscopy, Knop hardness measurements, and “ball-on-disc” dry friction tests were applied to study the effect of the processing parameters on the geometry of laser pass and microstructure, hardness, and tribology of the processed layers. The results obtained revealed that pulsed laser processing provides a monolithic remelted coating layer with the microstructure of ultrafine, W-rich dendrites in Ni-based matrix, where size and distribution of W-rich dendrites periodically vary across remelted layer depth. The composition of W-rich dendrites can be attributed to a carbide of type (W, Cr, Ni, Fe)C. The cracks sensitivity of coatings was visibly reduced with the reduction of power density applied. The hardness of coatings was between ~1070 and ~1140 HK0.2 and correlated with microstructure size, being dependent on the processing parameters. The friction coefficient and wear rate of coatings during dry sliding were reduced by up to ~30% and up to ~2.4 times, respectively, after laser processing.

Recently, metal selective laser sintering (SLS) techniques have attracted lively interest as a promising technology, which offers a number of unique applications in manufacturing of metal parts with complex internal structure and geometry. However, unsatisfactory surface properties of as-manufactured SLS parts cause high cost of finish processing and restrict wider application of SLS products. The paper presents results of the study, which was taken to evaluate capability of laser processing to improve surface quality of SLS parts manufactured from powder maraging steel 1.2709 (X3NiCoMoTi 18-9-5). The properties of processed surfaces were assessed, and the main dependencies of the roughness, hardness, wear resistance, and phase composition on the main parameters of laser processing—scanning speed, laser power, and number of processing times—were determined. The roughness of surfaces was diminished up to ∼41%, the hardness was increased up to ∼88%, and the wear resistance was improved up to almost 4 times, as compared with surface of as-manufactured SLS part. The preliminary study has demonstrated that laser processing has considerable potential for improvement of surface conditions of steel additive manufactured parts.

In the present work, the experimental study on laser processing of additively manufactured (AM) maraging steel part surface was conducted. Nanosecond pulsed laser at ablation mode was used for surface modification in oxidizing atmosphere. The morphology, roughness, elemental and phase composition, microhardness and tribological properties of the processed surfaces were investigated. The obtained results revealed that pulsed laser processing under the ablation mode in air allows obtaining modified surface with uniform micro-texture and insignificant residual undulation, providing 3 times lower roughness as compared with the as-manufactured AM part. The intensive oxidation of surface during laser processing results in formation of the significant oxides amount, which can be controlled by scanning speed. Due to the presence of the oxide phase (such as Fe₂CoO₄ and Ti_0.11Co_0.89O_0.99), the hardness and wear resistance of the surface were significantly improved, up to 40% and 17 times, respectively. The strong correlation between the roughness parameter R_a and mass loss during the tribological test testifies the significant role of the obtained morphology for the wear resistance of the surface.

The problem of insufficient wear resistance of maraging steels (MSt) has so far been solved mainly by the use of the thermochemical nitriding process, which has a number of limitations and disadvantages. In the present work, for MSt parts manufactured by laser powder bed fusion (LPBF), a more flexible laser alloying process was suggested as an alternative surface hardening process. The purpose of the present work is to give a better understanding on the possible hardening effect obtainable when amorphous boron is used as an alloying additive in relation with microstructural evolution and specific process parameters and to promote further development of this technology. For the alloying, a one kilowatt CO₂ laser was applied at 0.5–4.0 mm laser spot and 250–1500 mm/min laser operating speed, providing 50,955–796 W∙cm⁻² power density and 24.0–4.0 J∙mm⁻¹ heat input. Before laser processing, surfaces were covered with amorphous boron. The appropriate melt pool geometry was obtained at 0.5 mm laser spot, for which XPS analysis revealed an increase in boron concentration from ~3.1 to ~5.7 wt.% with a laser speed increase from 500 to 1500 mm/min. XRD analysis revealed domination of Fe₃B type borides along with the presence of FeB, Fe₂B, Ni₄B₃ borides, austenitic and martensitic phases. The microstructure of modified layers exhibited evolution from hypoeutectic microstructure, having ~630–780 HK0.5 hardness, to superfine lamellar nanoeutectic (~1000–1030 HK0.2) and further to submicron-sized dendritic boride structure (~1770 HK0.2). Aging of laser-boronized layers resulted in the change of phase composition and microstructure, which is mainly expressed in a plenty precipitation of Mo₂B₅ borides and leads to a reduction in hardness—more significant (by ~200–300 HK0.2) for hypoeutectic and hypereutectic layers and insignificant (by ~50 HK0.2) for near-eutectic. With the application of the laser boronizing technique, the hardness of MSt parts surface was increased up to ~three times before aging and up to ~2.3 times after aging, as compared with the hardness of aged MST part.

The authors of this article analyze the existing methods and models of technological preparation of machine-building industries. The structure of a three-level simulation model with network-centric control, the structures of individual elements of the simulation model, and the process of simulation modeling are described. The criteria for choosing a rational option for the processing technological route have been determined. During this research, a simulation program was implemented in C++. It allows you to select the optimal scenario for the operation of a production site based on two criteria: time and cost. The volume of implementation is about 2 × 10³ lines of code. A diagram of the modeling algorithm for the implemented program and a description of the classes and their interactions are given in the article. The developed simulation model was tested at a machine-building enterprise using the example of the “Pusher” part, manufactured under single-unit production conditions. The technological equipment used for the manufacture of this part was formed in the form of input data of the simulation model. The results of simulation modeling for the selected part are described. For each variant of the technological processing route, the values of variable costs and the duration of the production cycle were determined.