Porosity in plasma-sprayed coatings is vital for most engineering applications. Porosity has its merits and demerits depending on the functionality of the coating and the immediate working environment. Consequently, the formation mechanisms and development of porosity have been extensively explored to find out modes of controlling porosity in plasma-sprayed coatings. In this work, a comprehensive review of porosity on plasma-sprayed coatings is established. The formation and development of porosity on plasma-sprayed coatings are governed by set spraying parameters. Optimized set spraying parameters have been used to achieve the most favorable coatings with minimum defects. Even with the optimized set spraying parameters, defects like porosity still occur. Here, we discuss other ways that can be used to control porosity in plasma-sprayed coating with emphasis to atmospheric plasma-sprayed chromium oxide coatings. Techniques like multilayer coatings, nanostructured coatings, doping with rare earth elements, laser surface re-melting and a combination of the above methods have been suggested in adjusting porosity. The influences of porosity on microstructure, properties of plasma-sprayed coatings and the measurement methods of porosity have also been reviewed.

Thermal barrier coatings (TBCs) play a vitally important role in protecting the hot parts of a gas turbine from high temperature and corrosion effectively. More and more attention has been paid to the performance modification of ZrO₂-based ceramics and seeking for new ceramic materials to meet requirements of gas turbine TBCs. The working principle, merits, and demerits of main technologies for coating preparation are elaborated in this paper, and the properties of new ceramic materials are reviewed. It is found that the thermal conductivity, thermal stability, mechanical properties, and other performances of traditional ZrO₂-based ceramics could be improved effectively by doping modification. The emphases for new ceramic materials research were put on pyrochlores, magnetoplumbites, rare-earth tantalates, etc. Rare-earth tantalates with great potentials as new top ceramic materials were described in detail. In the end, the development directions of advanced top ceramic coatings, combining doping modification with preparation technology to regulate and control structure property of high-performance ceramic material, were put forward.

The extended immersion of ships in seawater frequently results in biofouling, a condition characterized by the accumulation of marine organisms such as barnacles and algae. To combat this issue, the application of anti-fouling coatings to the hull surfaces of vessels has emerged as one of the most effective strategies. In response to the increasing global emphasis on environmental sustainability, there is a growing demand for anti-fouling coatings that not only demonstrate superior anti-fouling efficacy but also adhere to stringent environmental standards. The traditional use of organotin-based self-polishing anti-fouling coatings, known for their high toxicity, has been prohibited due to environmental concerns. Consequently, there is a progressive shift toward the development and application of environmentally friendly anti-fouling coatings. This paper reviews the toxicity and application limitations associated with conventional anti-fouling coatings. It provides a comprehensive overview of recent advancements in the field, including the development of novel self-polishing anti-fouling coatings, low surface energy coatings, biomimetic coatings, and nanostructured coatings, each leveraging distinct anti-fouling mechanisms. The paper evaluates the composition and performance of these emerging coatings and identifies key technical challenges that remain unresolved. It also proposes a multi-faceted approach to addressing these challenges, suggesting potential solutions for enhancing the effectiveness and environmental compatibility of anti-fouling technologies. The paper forecasts future research directions and development trajectories for marine anti-fouling coatings, emphasizing the need for continued innovation to achieve both environmental sustainability and superior anti-fouling performance.

Heat dissipation problem is the primary factor restricting the service life of an electronic component. The thermal conductivity of materials has become a bottleneck that hinders the development of the electronic information industry (such as light-emitting diodes, 5G mobile phones). Therefore, the research on improving the thermal conductivity of materials has a very important theoretical value and a practical application value. Whether the thermally conductive filler in polymer composites can form a highly thermal conductive pathway is a key issue at this stage. The carbon fiber/carbon felt (CF/C felt) prepared in the study has a three-dimensional continuous network structure. The nickel-coated carbon fiber/carbon felt (CF/C/Ni felt) was fabricated by an electroplating deposition method. Three-dimensional CF/C/Ni/epoxy composites were manufactured by vacuum-assisted liquid-phase impregnation. By forming connection points between the adjacent carbon fibers, the thermal conduction path inside the felt can be improved so as to improve the thermal conductivity of the CF/C/Ni/epoxy composite. The thermal conductivity of the CF/C/Ni/epoxy composite (in-plane K_∥) is up to 2.13 W/(m K) with 14.0 wt % CF/C and 3.70 wt % Ni particles (60 min electroplating deposition). This paper provides a theoretical basis for the development of high thermal conductivity and high-performance composite materials urgently needed in industrial production and high-tech fields.

Polydimethylsiloxane containing methacryloyloxy and methoxy silane groups (MAPDMS)-microcapsule-SiO₂ (MPMS) functional materials were prepared by constructing micro-nano hierarchical structures on the surface of MAPDMS matrix. Herein, MAPDMS@1,1-stilbene-modified hydrolyzed polyglycidyl methacrylate/graphene oxide/dimethyloctadecyl[3-(trimethoxysilyl) propyl]ammonium chloride (MAPDMS@PGMA_m/GO/QC18) self-healing microcapsules with compact multi-shell structure were synthesized and combined with nano-SiO₂ to construct the hierarchical structures. Furthermore, ultraviolet (UV)/moisture dual curing mode was introduced into deep curing reaction and efficient self-healing reaction of the MPMS. The results show that the introduction of UV/moisture dual curing mode and micro-nano hierarchical structure gives MPMS functional materials excellent mechanical properties, antifouling properties, self-healing properties, and antibacterial properties. The shear strength and tensile strength of MPMS increase from 3.32 and 4.26 MPa of MAPDMS to 3.81 and 5.06 MPa, respectively. Its static contact angle increases from 115.9° of MAPDMS to 156.5°, and its slide angle decreases from 68.5° of MAPDMS to 7.8°, respectively. The antifouling performance of MPMS against seawater, soy sauce, juice, coffee, protein, and other contaminants is effectively improved compared with MAPDMS matrix. At the same time, the tensile strength and elongation at break of MPMS after healing reach 98.22% and 96.57% of those in original state, respectively. In addition, the antibacterial rates of MPMS against Escherichia coli and Staphylococcus aureus reach 99.85% and 100%, respectively. The MPMS prepared in this paper is expected to be widely used in marine antifouling, pipeline network, anti-icing, microfluidics, wearable devices, medical devices, electrochemical biosensors, and other fields.

As electronic devices tend to be integrated and high-powered, thermal conductivity is regarded as the crucial parameter of electronic components, which has become the main factor that limits the operating speed and service lifetime of electronic devices. However, constructing continuous thermal conductive paths for low content particle fillers and reducing interface thermal resistance between fillers and matrix are still two challenging issues for the preparation of thermally conductive composites. In this study, 3D-oriented carbon fiber (CF) thermal network structures filled with boron nitride flakes (BN) as thermal conductive bridges were successfully constructed. The epoxy composite was fabricated by thermal conductive material with a 3D oriented structure by the vacuum liquid impregnation method. This special 3D-oriented structure modified by BN (BN/CF) could efficiently broaden the heat conduction pathway and connected adjacent fibers, which leads to the reduction of thermal resistance. The thermal conductivity of the boron nitride/carbon fiber/epoxy resin composite (BN/CF/EP) with 5 vol% 10 mm CF and 40 vol% BN reaches up to 3.1 W m⁻¹ K⁻¹, and its conductivity is only 2.5 × 10⁻⁴ S cm⁻¹. This facile and high-efficient method could provide some useful advice for the thermal management material in the microelectronic field and aerospace industry.