This study investigates the impact of annealing time, temperature, and layer height on the tensile strength and dimensional change of three 3D printing materials (PLA, PETG, and carbon fiber-reinforced PETG). Samples with varying layer heights (0.1 mm, 0.2 mm, and 0.3 mm) were annealed at temperatures ranging from 60–100 °C for 30, 60, and 90 min. Tensile tests were conducted, and regression models were developed to analyze the effects of these parameters on tensile strength. The models exhibited high accuracy, with a maximum deviation of only 5% from measured validation values. The models showed that layer height has a significantly bigger influence on tensile strength than annealing time and temperature. Optimal combinations of parameters were identified for each material, with PLA performing best at 0.1 mm/60 min/90 °C and PETG and PETGCF achieving optimal tensile strength at 0.1 mm/90 min/60 °C. PETGCF demonstrated smallest dimensional change after annealing and had the best modulus of elasticity of all the materials. The study employed experimental testing and regression models to assess the results across multiple materials under consistent conditions, contributing valuable insights to the ongoing discussion on the influence of annealing in 3D-printed parts.

Polyamide 12 (PA 22000) is a well-known material and one of the most biocompatible materials tested and used to manufacture customized medical implants by selective laser sintering technology. To optimize the implants, several research activities were considered, starting with the design and manufacture of test samples made of PA 2200 by selective laser sintering (SLS) technology, with different processing parameters and part orientations. The obtained samples were subjected to compression tests and later to SEM analyses of the fractured zones, in which we determined the microstructural properties of the analyzed samples. Finally, an evaluation of the surface roughness of the material and the possibility of improving the surface roughness of the realized parts using finite element analysis to determine the optimum contact pressure between the component made of PA 2200 by SLS and the component made of TiAl6V4 by SLM was performed.

Surging electricity demand, its limited supply, and the pandemic crisis are just some of the key factors that resulted in changes in electricity prices on the power exchanges. This topic brings about a notable economic influence on both producers and consumers. The main purpose of this paper is to explore power price volatility during the four-year period from 1 January 2018 to 31 December 2021, in 28 power exchanges in Europe, measured using daily velocity data. In addition, based on the fixed and chain base index numbers, as well as their relative merits, this paper was designed to measure the gap and convergence in trends. Considering that the price volatility varies depending on the observation period, this paper performs a comparative analysis of electricity price volatility on a daily, monthly, quarterly, and annual level for all examined countries. The obtained results indicate that electricity price volatility is higher on a daily basis. Related to this, convergent trends are demonstrated on all 28 observed markets, and there is a growing trend of hourly spot prices in the analyzed four-year period. The results of this paper also confirm a higher power price volatility during the pandemic period in 2020 and 2021 compared to the prepandemic period during 2018 and 2019.

Selective laser melting (SLM) is one of the most important technologies used when complex metallic parts need to be rapidly manufactured. There are some requirements related to the quality of the manufactured part or the accuracy of the process control, in order to turn SLM process into a production technique. This paper presents a case study undertaken at the Technical University of Cluj‐Napoca (TUCN) in cooperation with an industrial company from Romania, focusing on the accuracy issues. Finite element analysis (FEA) and Design Expert software were jointly used in order to determine the optimum process parameters required to improve the accuracy of the SLM metallic parts. Experimental results are also presented in the paper.

This paper presents the outcomes of investigations conducted on the development procedure of a personalized prosthetic device for an adult patient. The individualization is achieved through 3D scanning, followed by semi-automated design using the AutoMedPrint system, and low-cost fused deposition modelling (FDM) technology for 3D printing. The prosthesis is aimed for use during bicycle riding and other sport activities. During the conducted experiments outlined in this manuscript, the prosthesis is equipped with force and movement sensors. The purpose is to collect data on its functionality across different scenarios and dynamic activities, aiming to assess potential harm, refine the design, and serve as an initial step before activating the prosthesis end effector. This article describes the methodology in detail, including the process of designing, producing, and programming, as well as laboratory and field test results (including testing performed with and without a patient). Overall, the design and prototype are implemented successfully. A discussion about the need for particular improvements in both the mechanical and electrical areas is finally presented.

The article presents analysis of mechanical properties of specimens fabricated by fused deposition modeling (FDM). The four of considered materials are the well-known 3D printing filaments i.e., polylactide (PLA), Nylon 12 (PA12), acrylonitrile butadiene styrene (ABS), polyethylene terephthalate...