The high quality demand for machined functional surfaces of forming tools, entail extensive investigations for the adjustment of the manufacturing process. Since the surface quality depends on a multitude of influencing factors in face micromilling, a complex optimization problem arises. Through analytical and simulative approaches, the scope of the experimental investigation to meet the requirements for surface roughness can be significantly reduced. In this contribution, both analytical and simulation-based approaches are presented in the context of predicting the roughness of a machined surface. The consideration of actual tool geometry and shape deviations are used in a simulation system to achieve the agreement with experimental results.

The increasing demand for complex and wear-resistant forming tools made of difficult-to-machine materials requires efficient manufacturing processes. In terms of high-strength materials; highly suitable processes such as micromilling are limited in their potential due to the increased tool loads and the resulting tool wear. This promotes hybrid manufacturing processes that offer approaches to increase the performance. In this paper; conduction-based thermally assisted micromilling using a prototype device to homogeneously heat the entire workpiece is investigated. By varying the workpiece temperature by 20 °C < T_W < 500 °C; a highly durable high-speed steel (HSS) AISI M3:2 (63 HRC) and a hot-work steel (HWS) AISI H11 (53 HRC) were machined using PVD-TiAlN coated micro-end milling tools (d = 1 mm). The influence of the workpiece temperature on central process conditions; such as tool wear and achievable surface quality; are determined. As expected; the temporary thermal softening of the materials leads to a reduction in the cutting forces and; thus; in the resulting tool wear for specific configurations of the thermal assistance. While only minor effects are detected regarding the surface topography; a significant reduction in the burr height is achieved.

New manufacturing technologies, such as Sheet-Bulk Metal Forming, are facing the challenges of highly stressed tool surfaces which are limiting their service life. For this reason, the load-adapted design of surfaces and the subsurface region as well as the application of wear-resistant coatings for forming dies and molds made of high-speed steel has been subject to many research activities. Existing approaches in the form of grinding and conventional milling processes do not achieve the surface quality desired for the forming operations and therefore often require manual polishing strategies afterward. This might lead to an unfavorable constitution for subsequent PVD coating processes causing delamination effects or poor adhesion of the wear-resistant coatings. To overcome these restrictions, meso- and micromilling are presented as promising approaches to polishing strategies with varying grain sizes. The processed topographies are correlated with the tribological properties determined in an adapted ring compression test using the deep drawing steel DC04. Additionally, the influence of the roughness profile as well as the induced residual stresses in the subsurface region are examined with respect to their influence on the adhesion of a wear-resistant CrAlN PVD coating. The results prove the benefits of micromilling in terms of a reduced friction factor in the load spectrum of Sheet-Bulk Metal Forming as well as an improved coating adhesion in comparison to metallographic finishing strategies, which can be correlated to the processed roughness profile and induced compressive residual stresses in the subsurface region.

One of the major advantages of micromachining is the high achievable surface quality at highly flexible capabilities in terms of the machining of workpieces with complex geometric properties. Unfortunately, finishing operations often result in extensive process times due to the dependency of the resulting surface topography on the cutting parameter, e.g., the feed per tooth, f_z. To overcome this dependency, special tool shapes, called wipers, have proven themselves in the field of turning. This paper presents the transfer of such tool shapes to solid carbide milling tools for micromachining. In this context, a material removal simulation (MRS) was used to investigate promising wiper geometries for micro end mills (d = 1 mm). Through experimental validation of the results, the surface topography, the resulting process forces, and tendencies in the residual stress state were investigated, machining the hot work tool steel (AISI H11). The surface-related results show a high agreement and thus the potential of MRS for tool development. Deviations from the experimental data for large wipers could be attributed to the non-modeled tool deflections, friction, and plastic deformations. Furthermore, a slight geometry-dependent increase in cutting forces and compressive stresses were observed, while a significant reduction in roughness up to 84% and favorable topography conditions were achieved by adjusting wipers and cutting parameters.

Producing complex sheet metal components in fewer process steps motivated the development of the innovative forming process called sheet-bulk metal forming (SBMF). In this process, sheet metal forming and bulk-metal forming are combined to create a unique forming process in which a component with external and internal gearing is produced in three production steps. However, the high degrees of deformation that occur using high-strength steels and the number of different process steps result in high process forces, strongly limiting the service life of tools. To reduce the forming force during SBMF processes, tool and process modifications were investigated. Therefore, plane-strain compression tests were conducted to examine the influence of a CrAlN PVD coating and tailored surfaces produced by high-feed milling (HF) of tool-active elements on the material flow of the specimens. In addition to the tool-sided modifications, the influence of an oscillation overlay during the forming process was investigated. Based on the results of the compression tests, the surfaces of the active tool elements of the SBMF process were modified in order to transfer the basic experimental results to the production of a functional component. The friction is thus adapted locally in the SBMF process.