The increasing demand for complex and wear-resistant forming tools made of difficult-to-machine materials requires efficient manufacturing processes. In terms of high-strength materials; highly suitable processes such as micromilling are limited in their potential due to the increased tool loads and the resulting tool wear. This promotes hybrid manufacturing processes that offer approaches to increase the performance. In this paper; conduction-based thermally assisted micromilling using a prototype device to homogeneously heat the entire workpiece is investigated. By varying the workpiece temperature by 20 °C < T_W < 500 °C; a highly durable high-speed steel (HSS) AISI M3:2 (63 HRC) and a hot-work steel (HWS) AISI H11 (53 HRC) were machined using PVD-TiAlN coated micro-end milling tools (d = 1 mm). The influence of the workpiece temperature on central process conditions; such as tool wear and achievable surface quality; are determined. As expected; the temporary thermal softening of the materials leads to a reduction in the cutting forces and; thus; in the resulting tool wear for specific configurations of the thermal assistance. While only minor effects are detected regarding the surface topography; a significant reduction in the burr height is achieved.

Hot work tool steels (HWS) are widely used for high performance components as dies and molds in hot forging processes, where extreme process-related mechanical and thermal loads limit tool life. With the functionalizing and modification of tool surfaces with tailored surfaces, a promising approach is given to provide material flow control resulting in the efficient die filling of cavities while reducing the process forces. In terms of fatigue properties, the influence of surface modifications on surface integrity is insufficiently studied. Therefore, the potential of the machining processes of high-feed milling, micromilling and grinding with regard to the implications on the fatigue strength of components made of HWS (AISI H11) hardened to 50 ± 1 HRC was investigated. For this purpose, the machined surfaces were characterized in terms of surface topography and residual stress state to determine the surface integrity. In order to analyze the resulting fatigue behavior as a result of the machining processes, a rotating bending test was performed. The fracture surfaces were investigated using fractographic analysis to define the initiation area and to identify the source of failure. The investigations showed a significant influence of the machining-induced surface integrity and, in particular, the induced residual stress state on the fatigue properties of components made of HWS.

New manufacturing technologies, such as Sheet-Bulk Metal Forming, are facing the challenges of highly stressed tool surfaces which are limiting their service life. For this reason, the load-adapted design of surfaces and the subsurface region as well as the application of wear-resistant coatings for forming dies and molds made of high-speed steel has been subject to many research activities. Existing approaches in the form of grinding and conventional milling processes do not achieve the surface quality desired for the forming operations and therefore often require manual polishing strategies afterward. This might lead to an unfavorable constitution for subsequent PVD coating processes causing delamination effects or poor adhesion of the wear-resistant coatings. To overcome these restrictions, meso- and micromilling are presented as promising approaches to polishing strategies with varying grain sizes. The processed topographies are correlated with the tribological properties determined in an adapted ring compression test using the deep drawing steel DC04. Additionally, the influence of the roughness profile as well as the induced residual stresses in the subsurface region are examined with respect to their influence on the adhesion of a wear-resistant CrAlN PVD coating. The results prove the benefits of micromilling in terms of a reduced friction factor in the load spectrum of Sheet-Bulk Metal Forming as well as an improved coating adhesion in comparison to metallographic finishing strategies, which can be correlated to the processed roughness profile and induced compressive residual stresses in the subsurface region.