The development of transparent electronics has advanced metal–oxide–semiconductor Thin-Film transistor (TFT) technology. In the field of flat-panel displays, as basic units, TFTs play an important role in achieving high speed, brightness, and screen contrast ratio to display information by controlling liquid crystal pixel dots. Oxide TFTs have gradually replaced silicon-based TFTs owing to their field-effect mobility, stability, and responsiveness. In the market, n-type oxide TFTs have been widely used, and their preparation methods have been gradually refined; however, p-Type oxide TFTs with the same properties are difficult to obtain. Fabricating p-Type oxide TFTs with the same performance as n-type oxide TFTs can ensure more energy-efficient complementary electronics and better transparent display applications. This paper summarizes the basic understanding of the structure and performance of the p-Type oxide TFTs, expounding the research progress and challenges of oxide transistors. The microstructures of the three types of p-Type oxides and significant efforts to improve the performance of oxide TFTs are highlighted. Finally, the latest progress and prospects of oxide TFTs based on p-Type oxide semiconductors and other p-Type semiconductor electronic devices are discussed.

High Power Impulse Magnetron Sputtering (HiPIMS) has generated a great deal of interest by offering significant advantages such as high target ionization rate, high plasma density, and the smooth surface of the sputtered films. This study discusses the deposition of copper nitride thin films via HiPIMS at different deposition pressures and then examines the impact of the deposition pressure on the structural and electrical properties of Cu₃N films. At low deposition pressure, Cu-rich Cu₃N films were obtained, which results in the n-type semiconductor behavior of the films. When the deposition pressure is increased to above 15 mtorr, Cu₃N phase forms, leading to a change in the conductivity type of the film from n-type to p-type. According to our analysis, the Cu₃N film deposited at 15 mtorr shows p-type conduction with the lowest resistivity of 0.024 Ω·cm and the highest carrier concentration of 1.43 × 10²⁰ cm⁻³. Furthermore, compared to the properties of Cu₃N films deposited via conventional direct current magnetron sputtering (DCMS), the films deposited via HiPIMS show better conductivity due to the higher ionization rate of HiPIMS. These results enhance the potential of Cu₃N films’ use in smart futuristic devices such as photodetection, photovoltaic absorbers, lithium-ion batteries, etc.

Nitrogen-doped indium tin zinc oxide (ITZO:N) thin film transistors (TFTs) were deposited on SiO ₂ (200 nm)/p-Si〈1 0 0〉 substrates by RF magnetron sputtering at room temperature. The structural, chemical compositions, surface morphology, optical and electrical properties as a function of the active layer thickness were investigated. As the active layer thickness increases, Zn content decreases and In content increases gradually. Meanwhile, Sn content is almost unchanged. When the thickness of the active layer is more than 45 nm, the ITZO:N films become crystallized and present a crystal orientation along InN(0 0 2) plan. No matter what the thickness is, ITZO:N films always display a high transmittance above 80% in the visible region. Their optical band gaps fluctuate between 3.4 eV and 3.62 eV. Due to the dominance of low interface trap density and high carrier concentration, ITZO:N TFT shows enhanced electrical properties as the active layer thickness is 35 nm. Its field-effect mobility, on/off radio and sub-threshold swing are 17.53 cm ² V ⁻¹ · s ⁻¹ , 10 ⁶ and 0.36 V/dec, respectively. These results indicate that the suitable thickness of the active layer can enhance the quality of ITZO:N films and decrease the defects density of ITZO:N TFT. Thus, the properties of ITZO:N TFT can be optimized by adjusting the thickness of the active layer.