In recent years, with the development of hydrogen energy economy, there is an increasing demand for hydrogen in the market, and hydrogen production through biomass will provide an important way to supply clean, environmentally friendly and highly efficient hydrogen. In this study, cow dung was selected as the biomass source, and the efficiency of the biomass to hydrogen reaction was explored by coupling high temperature pyrolysis and water vapor gasification. The experimental conditions of gasification temperature, water mass fraction, heating rate and feed temperature were systematically studied and optimized to determine the optimal conditions for in situ hydrogen production by gasification of cow dung. The relationship of each factor to the yield of hydrogen production by gasification of cow dung semi-coke was investigated in order to elucidate the mechanism of the hydrogen production. The experiment determined the optimal operating parameters of in situ gasification: gasification temperature 1173 K, water mass fraction 80%, heating rate 10 K/min and feed temperature 673 K. The semi-coke treatment separated high temperature pyrolysis and water vapor gasification, and reduced the influence on gasification of volatile substances such as tar extracted from pyrolysis. The increase of semi-coke preparation temperature increases the content of coke, reduces the volatile matter and improves the yield of hydrogen; the small size of semi-coke particles and large specific surface area are beneficial to the gasification reaction.

In this paper, the effect of rare earth Ce content on the morphology, composition, type and size distribution of inclusions in W350 non-oriented silicon steel was investigated by means of ICP-MS (inductively coupled plasma mass spectrometry), SEM/EDS (scanning electron microscope-energy Dispersive Spectrometer), and ASPEX (automated SEM/EDS inclusion analysis). The results showed that with the increase of Ce content in the steel, the modification sequence of inclusions was CeAlO₃→Ce₂O₂S→Ce_xS_y. The type and size distribution of inclusions in the steel obviously changed with the difference in added Ce content. When the added Ce content in the steel was 10 ppm, 14 ppm, 20 ppm and 30 ppm respectively, the rare earth inclusions were mainly CeAlO₃-Ce₂O₂S. Furthermore, when the added Ce content increased to 60 ppm, the rare earth inclusions were mainly Ce₂O₂S with a small amount of CeAlO₃ contained in part inclusions. When the added Ce content increased continually to 95 ppm, the rare earth inclusions were mainly Ce_xS_y-Ce₂O₂S. The critical Ce content for the conversion between CeAlO₃ and Ce₂O₂S was 41 ppm. To ensure that inclusions transform from CeAlO₃ to Ce₂O₂S, the Ce content in the steel should be greater than 41 ppm. Under the current experimental conditions, it was found that when the Ce content was 20 ppm, the number density and proportion of inclusions in the steel were lower, and their average size was larger. When the added Ce content increased to 95 ppm, the number density of inclusions in the steel significantly increased, which deteriorated the steel cleanliness.