As the lightest structural materials, Mg alloys show great effectiveness at energy saving and emission reduction when applied in the automotive and aerospace fields. In particular, Zr-bearing Mg alloys (non-Al containing) exhibit high strengths and elevated-temperature usage values. Zr is the most powerful grain refiner, and it provides fine grain sizes, uniformities in microstructural and mechanical properties and processing formability for Mg alloys. Due to the importance of Zr alloying, this review paper systematically summarizes the latest research progress in the grain refinement effects of Zr on Mg alloys. The main points are reviewed, including the alloying process of Zr, the grain refinement mechanism of Zr, factors affecting the grain refinement effects of Zr, and methods improving grain refinement efficiency of Zr. This paper provides a comprehensive understating of grain refinement effects of Zr on Mg alloys for the researchers and engineers.

In this paper, ZL205A (AlCu5Mn alloy) castings were prepared by squeeze casting. The effects of solution and ageing treatment on the microstructure and mechanical properties of ZL205A castings were studied by metallography, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and mechanical properties tests. The results showed that most of the θ(Al₂Cu) and T(Al₁₂CuMn₂) phases in squeeze-cast ZL205A dissolved into the α(Al) matrix after solution treatment for 15 h. The fine precipitates gradually increased with the ageing time. The ultimate tensile strength of the specimen aged for 6 h was the highest of 467 MPa and the elongation was up to 15.1%, showing good comprehensive mechanical properties.

It has long been recognized that grain refinement of Mg-Al alloys is difficult, although various methods have been tried. In the present paper, a novel grain refiner, Al-3.4V-1B master alloy, has been developed to refine the as-cast AZ91 alloy. A comparative study on grain refinement effects of Al-3.4V-1B, Al-5V, and Al-3Ti-1B master alloys was performed under the same solidification conditions. It is shown that Al-3.4V-1B master alloy not only has significant grain refinement ability, but also keeps stable anti-fading capacity with holding time up to 2 h. Based on the analysis of grain refinement, VB₂ particles introduced by Al-3.4V-1B master alloy are the heterogeneous nuclei for AZ91 alloy.