This research investigated the effect of irradiation with an electron beam energy of 10 MeV in doses of 26–156 kGy on polytetrafluoroethylene (PTFE) with a 15% and 20% graphite additive. The research has shown that mechanical (compression strength, hardness, and Young’s modulus) and sclerometric (coefficient of wear micromechanism and coefficient of resistance to wear) properties improve and tribological wear decreases as graphite content increases. Electron beam irradiation increases the degree of crystallinity of both materials to a similar extent. However significant differences in the improvement of all examined properties have been demonstrated for PTFE with higher (20%) graphite content subjected to the electron beam irradiation. This polymer is characterized by higher hardness and Young’s modulus, reduced susceptibility to permanent deformation, higher elasticity, compression strength, and above all, a nearly 30% reduction in tribological wear compared to PTFE with a 15% graphite additive. The most advantageous properties can be obtained for both of the examined composites after absorbing a dose of 104 kGy. The obtained results hold promise for the improvement of the operational life of friction couples which do not require lubrication, used for example in air compressors and engines, and for the possibility of application of these modified polymers. In particular PTFE with 20% graphite content, in the nuclear and space industry.

Titanium and its alloys are among the most promising biomaterials for medical applications. In this work, the isothermal oxidation of Ti-6Al-7Nb biomedical alloy towards improving its mechanical properties, corrosion resistance, and bioactivity has been developed. The oxide layers were formed at 600, 700, and 800 °C for 72 h. Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), 3D profilometry, and microindentation test, were used to characterize microstructure, surface geometrical structure, and the hardness of the diphase (α + β) Ti-6Al-7Nb alloy after oxidation, respectively. In vitro corrosion resistance tests were carried out in a saline solution at 37 °C using the open-circuit potential method and potentiodynamic measurements. Electronic properties in the air were studied using the Scanning Kelvin Probe (SKP) technique. The bioactivity test was conducted by soaking the alkali- and heat-treated samples in simulated body fluid for 7 days. The presence of apatite was confirmed using SEM/EDS and Fourier Transform Infrared Spectroscopy (FTIR) studies. The thickness of oxide layers formed increased with the temperature growth from 0.25 to 5.48 µm. It was found that with increasing isothermal oxidation temperature, the surface roughness, hardness, corrosion resistance, and contact potential difference increased. The Ti-6Al-7Nb alloy after oxidation revealed the HAp-forming ability in a biological environment.

The paper investigates changes in the structure, microhardness, and sclerometrical and tribological properties of a Mg-Y-Nd alloy under the influence of deep cryogenic treatment (DCT) in combination with heat treatment. The solution treatment was carried out at 545 °C for 8 h, aging was carried out at 250 °C for 24 h, and the deep cryogenic treatment applied at different treatment stages was performed at −196 °C. Tests showed a significant increase in the number of β-phase precipitates identified as Mg_46.1Y_6.25RE_3.45 in the alloy subjected to DCT after solution treatment followed by aging. In addition, an approximately 20% reduction of the grain size was observed. Changes in the structure in the precipitation process strengthened the alloy and resulted in an increase of its hardness. At the same time, sclerometric tests allowed the micromechanism of wear and the coefficient of resistance to abrasive wear to be determined. Tribological tests showed a three-fold reduction in the volumetric wear and a considerable reduction of the friction coefficient, with the main mechanism observed during friction being abrasive wear. The most favorable properties of the alloy were obtained after precipitation hardening combined with DCT, resulting in a large increase in resistance to abrasive wear. Additionally, the formation of deep scratches in the examined material was reduced. The introduction of sub-zero treatment reduces the precipitation hardening time, and the results obtained indicate that the service life of the Mg-Y-Nd alloy can be extended.

The mechanical and tribological characteristics of the Ti-6Al-7Nb alloy were investigated within a wide range of temperature and time parameters of thermal oxidation. The hardness, H_IT, and indentation modulus, E_IT, of the alloy in question, with and without an anti-wear oxide layer, were determined. The tribological properties of sliding couples were studied under technically dry friction conditions, using a ball-on-disc tribometer. The test pieces were non-oxidized and oxidized Ti-6Al-7Nb alloy discs, and Al₂O₃, ZrO_2, and 100Cr6 balls were used as counter specimens. After thermal oxidation, the surface of the titanium alloy was characterized by a significantly higher hardness, H_IT (8–10 GPa), compared to the surface not covered with oxide layers (3.6 GPa). The study showed that the curvature of the loading segments increased with an increasing oxidation temperature, indicating a strong positive dependence of hardness on the thermal oxidation temperature. The value of the indentation modulus, E_IT, was also found to increase with the increasing oxidation temperature. The intensity of the tribological processes was strictly dependent on the oxidation parameters and the couple’s material (Al₂O₃, ZrO₂, 100Cr6). It has been shown that the thermal oxidation process makes it possible to control, within a wide range, the friction-wear characteristics of the Ti-6Al-7Nb alloy.

This study analyzed the effects of irradiation of polytetrafluoroethylene (PTFE) containing 40% of bronze using an electron beam with energy of 10 MeV. Dosages from 26 to156 kGy (2.6–15.6 Mrad) were used. The impact of a high-energy electron beam on the thermal, spectrophotometric, mechanical, and tribological properties was determined, and the results were compared with those obtained for pure PTFE. Thermal properties studies showed that such irradiation caused changes in melting temperature T_m and crystallization temperature T_c, an increase in crystallization heat ∆H_c, and a large increase in crystallinity χ_c proportional to the absorbed dose for both polymers. The addition of bronze decreased the degree of crystallinity of PTFE by twofold. Infrared spectroscopy (FTIR) studies confirmed that the main phenomenon associated with electron beam irradiation was the photodegradation of the polymer chains for both PTFE containing bronze and pure PTFE. This had a direct effect on the increase in the degree of crystallinity observed in DSC studies. The use of a bronze additive could lead to energy dissipation over the additive particles. An increase in hardness H and Young’s modulus E was also observed. The addition of bronze and the irradiation with an electron beam improved of the operational properties of PTFE.