Our goal is to fabricate flexible magnetic polymer composites as antenna substrates for very high frequency (VHF)/low ultra high frequency (UHF) antennas for unmanned aerial vehicles (UAVs) and medical devices. Magnetodielectric materials, which have permeability (μ) similar to permittivity (ε), have attracted great attention, because they facilitate miniaturization of microwave devices while keeping or enhancing electromagnetic characteristics. Mechanically millled Ba_1.5Sr_1.5Co₂Fe₂₄O₄₁ (Ba_1.5Sr_1.5Z) hexaferrite particles were used to increase permeability in the interesting frequency band. The microwave properties of Ba_1.5Sr_1.5Z composites were predicted and measured. Hansen’s zero-order analysis of antenna bandwidth and electromagnetic field simulation showed that the hexaferrite-based flexible composite could enhance a bandwidth and achieve the miniaturization of antennas as well. The magnetic antenna substrates can be a good solution to integrate antennas into the UAVs whose dimensions are comparable to or larger than communication wavelength.

MWCNTs (multiwalled carbon nanotubes) were applied to fiber-reinforced composite materials with phenolic resin having flame retardance for the composite heating panels of railroad vehicles. Instead of dispersing MWCNTs in the matrix, the surface of a pristine plain-weave glass fiber fabric was coated with MWCNTs through a series of dip-coating and drying processes, followed by the resin infusion of the phenolic resin to make the composite heating panel. Before and after the resin infusion process, low percolation thresholds of 0.00216 wt%_MWCNT (weight percent of MWCNTs) and 0.001 wt%_MWCNT, respectively, were achieved, as were very high electrical conductivities of 47.5 S/m at 0.210 wt%_MWCNT and 26.7 S/m at 0.116 wt%, respectively. The low threshold and high conductivity can be attributed to the formation of electrical pathways directly onto the glass fabrics. It was confirmed that mechanical properties such as modulus, strength, and maximum strain were at the same level as those of the pristine glass fabric composite. The heating performance with temperature uniformity, as well as the electrical and mechanical properties, indicates that the resin-infused glass fabric composite having MWCNTs directly coated onto the fabric surface can be a solution for lightweight structural composite heating panels for railway vehicles.