For practical use of carbon nanotube (CNT) composites, especially in electronic applications, uniform dispersion of a high concentration of CNTs in a polymer matrix is a critical challenge. Three-roll milling is one of most reliable dispersion techniques. We investigate the effect of three-roll milling time on CNT length and the electrical properties of a CNT/polydimethylsiloxane composite film with 10 wt% CNTs. During the milling process, the CNT length is decreased from 10 to 1–4 μm by mechanical shear forces. The electrical conductivity increases after 1.5 min of milling owing to dispersion of the CNTs but decreases with increasing milling time owing to the decrease in the CNT length. Considering the changes in the electrical conductivity of the CNT composite and CNT length, we determined how to optimize the three-roll milling time to obtain a suitable dispersion state.

This paper reviews the major researchers of liquid, immersion, and two-phase cooling. Currently, liquids are used instead of air to cool the growing data centers. Immersion cooling shows a higher heat transfer coefficient than conventional cooling (<37 W/cm²). Because the use of liquids with high global warming potentials is prohibited, the number of liquids that can be used is limited. This paper discusses the existing, relevant literature from researchers who have studied the issue at least thrice. The authors were divided into those who focused on the surface and those who formed a structure on the surface. In summary, the authors suggested the following research directions: The experimental conditions of porous foam are not diverse, and there is a concern about the separation of foam and coating into the tub. The experimental conditions of the immersion tub should also be varied according to the heat and pressure over time. Structure-level research shows higher performance than surface-level research, but an economic feasibility study is required.

The structural stability of various structures (railroads, bridges, buildings, etc.) is lowered due to freezing because of the decreasing outside temperature in winter. To prevent damage from freezing, a technology for de-icing has been developed using an electric-heating composite. For this purpose, a highly electrically conductive composite film with multi-wall carbon nanotubes (MWCNTs) uniformly dispersed in a polydimethylsiloxane (PDMS) matrix through a three-roll process was fabricated by shearing the MWCNT/PDMS paste, through a two-roll process. The electrical conductivity and the activation energy of the composite were 326.5 S/m and 8.0 meV at 5.82 Vol% of MWCNTs, respectively. The dependence of the electric-heating performance (heating rate and temperature change) on the applied voltage and environmental temperature (from −20 °C to 20 °C) was evaluated. The heating rate and effective-heat-transfer characteristics were observed to decrease as the applied voltage increased, while they showed the opposite tendency when the environmental temperature was at sub-zero temperatures. Nevertheless, the overall heating performance (heating rate and temperature change) was maintained with little significant difference in the considered external-temperature range. The unique heating behaviors can result from the low activation energy and the negative-temperature (T) coefficient of resistance (R) (NTCR, dR/dT < 0) of the MWCNT/PDMS composite.

Our goal is to fabricate flexible magnetic polymer composites as antenna substrates for very high frequency (VHF)/low ultra high frequency (UHF) antennas for unmanned aerial vehicles (UAVs) and medical devices. Magnetodielectric materials, which have permeability (μ) similar to permittivity (ε), have attracted great attention, because they facilitate miniaturization of microwave devices while keeping or enhancing electromagnetic characteristics. Mechanically millled Ba_1.5Sr_1.5Co₂Fe₂₄O₄₁ (Ba_1.5Sr_1.5Z) hexaferrite particles were used to increase permeability in the interesting frequency band. The microwave properties of Ba_1.5Sr_1.5Z composites were predicted and measured. Hansen’s zero-order analysis of antenna bandwidth and electromagnetic field simulation showed that the hexaferrite-based flexible composite could enhance a bandwidth and achieve the miniaturization of antennas as well. The magnetic antenna substrates can be a good solution to integrate antennas into the UAVs whose dimensions are comparable to or larger than communication wavelength.

LPM-GDNL with a hydrophilic–superhydrophobic columnar interface enables separate water and gas transport. This structure improves current and power densities by up to 58% compared to commercial GDLs.